Synthesis of Ni-Co Hydroxide/Graphene Hydrogel Composites with Three-dimensional Network Structure and Their Electrochemical Performance
LIU Tingting1,2,*, TIAN Guoxing3, ZHAO Xin3, YU Xinyong3, MAO Chao3, YU Xuehan3, CHEN Ling3,4,*
1 Northeast Petroleum University at Qinhuangdao, Qinhuangdao 066004, Hebei, China 2 Provincial Key Laboratory of Polyolefin New Materials, College of Chemistry & Chemical Engineering, Northeast Petroleum University, Daqing 163318, Heilongjiang, China 3 Hebei Key Laboratory of Applied Chemistry, College of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao 066004, Hebei, China 4 Hebei Key Laboratory of Heavy Metal Deep-remediation in Water and Resource Reuse, College of Environmental and Chemical Engineering, Yanshan University, Qinhuangdao 066004, Hebei, China
Abstract: In this work, graphene oxide (GO) was prereduced by chemical reduction method, and then mixed with Ni(NO3)2·6H2O and Co(NO3)2·6H2O for hydrothermal reaction to obtain the composites of nickel-cobalt hydroxide/graphene hydrogel with three-dimensional network structure. By adjusting the amount of GO, nickel-cobalt hydroxide/graphene hydrogel (NiCo-OH/GH100) with the best electrochemical performance was acquired, and nickel-cobalt hydroxide nanosheets were distributed on the surface of graphene uniformly. The specific capacitance of NiCo-OH/GH100 was 590 F/g at a current density of 0.5 A/g, and the retention rate was 76.1% when the current density increased to 10 A/g, showing high specific capacitance and good rate performance. The asymmetric supercapacitor (ASC) of NiCo-OH/GH100∥nitrogen-doped graphene hydrogel compounded with carbon nanotube (NCGH) was assembled, and the specific capacitance retention was 92.9% after 10 000 charge-discharge cycles at 20 A/g. The energy density reached 23.9 Wh/kg at the power density of 375 W/kg.
作者简介: 刘亭亭,东北石油大学秦皇岛校区教授、硕士研究生导师。2003年东北师范大学生态学专业本科毕业后到东北石油大学工作至今,2015年燕山大学应用化学专业博士毕业。目前主要从事超级电容器方面的研究工作。发表论文20余篇,包括Materials Letters、Journal of Solid State Chemistry、RSC Advances等。
引用本文:
刘亭亭, 田国兴, 赵欣, 余新勇, 毛超, 于雪寒, 陈玲. 三维网络结构镍钴氢氧化物/石墨烯水凝胶复合材料的合成及电化学性能[J]. 材料导报, 2024, 38(5): 22070064-7.
LIU Tingting, TIAN Guoxing, ZHAO Xin, YU Xinyong, MAO Chao, YU Xuehan, CHEN Ling. Synthesis of Ni-Co Hydroxide/Graphene Hydrogel Composites with Three-dimensional Network Structure and Their Electrochemical Performance. Materials Reports, 2024, 38(5): 22070064-7.
1 Qu H, Zhang X, Zhan J, et al. ACS Sustainable Chemistry & Engineering, 2018, 6(6), 7380. 2 Kandula S, Shrestha K R, Rajeshkhanna G, et al. ACS Applied Materials & Interfaces, 2019, 11(12), 11555. 3 Gogotsi Y, Penner R M. ACS Nano, 2018, 12(3) , 2081. 4 Yuan L, Xin N, Liu Y, et al. Journal of Colloid and Interface Science, 2021, 599, 158. 5 Zhi M, Xiang C, Li J, et al. Nanoscale, 2013, 5(1), 72. 6 Pandolfo A G, Hollenkamp A F. Journal of Power Sources, 2006, 157(1), 11. 7 Ma H, He J, Xiong D B, et al. ACS Applied Materials & Interfaces, 2016, 8(3), 1992. 8 Wang W, Zhang N, Ye Z, et al. Inorganic Chemistry Frontiers, 2019, 6(2), 407. 9 Adán-Más A, Duarte R G, Silva T M, et al. Electrochimica Acta, 2017, 240, 323. 10 Kim D K, Hwang M, Ko D, et al. Electrochimica Acta, 2017, 246, 680. 11 Wang D, Wei A, Tian L, et al. Applied Surface Science, 2019, 483, 593. 12 Xie Y, Meng Z, Cai T, et al. ACS Applied Materials & Interfaces, 2015, 7(45), 25202. 13 Shang Y, Zhang J, Xu L, et al. Journal of Colloid and Interface Science, 2018, 531, 593. 14 Wang R, Jayakumar A, Xu C, et al. ACS Sustainable Chemistry & Engineering, 2016, 4(7), 3736. 15 Hwang M, Kang J, Seong K D, et al. Electrochimica Acta, 2018, 270, 156. 16 Zhang S, Gao H, Zhou J, et al. Journal of Alloys and Compounds, 2019, 792, 474. 17 Dhibar S, Malik S. ACS Applied Materials & Interfaces, 2020, 12(48), 54053. 18 Jing C, Liu X, Liu X, et al. CrystEngComm, 2018, 20, 7428. 19 Liu Y, Teng X, Mi Y, et al. Journal of Materials Chemistry A, 2017, 5(46), 24407. 20 Li Y, Shan L, Sui Y, et al. Journal of Materials Science: Materials in Electronics, 2019, 30, 13360. 21 Huang M, Wang Y, Chen J, et al. Electrochimica Acta, 2021, 381, 138289. 22 Jin H, Yuan D, Zhu S, et al. Dalton Transactions, 2018, 47(26), 8706. 23 Wang R, Xuan H, Zhang G, et al. Applied Surface Science, 2020, 526, 146641. 24 Du Q, Su L, Hou L, et al. Journal of Alloys and Compounds, 2018, 740, 1051. 25 Li Y, Li J, Wang M, et al. Chemical Engineering Journal, 2019, 366, 33. 26 Min S, Zhao C, Zhang Z, et al. Journal of Materials Chemistry A, 2015, 3(7), 3641. 27 Wang X, Liu W S, Lu X, et al. Journal of Materials Chemistry, 2012, 22(43), 23114. 28 Wang X, Sumboja A, Lin M, et al. Nanoscale, 2012, 4, 7266. 29 Zhang J, Jiang J, Li H, et al. Energy & Environmental Science, 2011, 4(10), 4009. 30 Wang X, Liu J, Wang Y, et al. Materials Research Bulletin, 2014, 52, 89. 31 Ji J, Zhang L L, Ji H, et al. ACS Nano, 2013, 7(7), 6237. 32 Wang H, Holt C M B, Li Z, et al. Nano Research, 2012, 5(9), 605. 33 Ding R, Qi L, Jia M, et al. Electrochimica Acta, 2013, 107, 494.