Abstract: Ti-1100 as-cast alloys with different contents of Yb2O3 were prepared by tungsten electrode non-consumption arc furnace. The WDW-300 electronic universal testing machine was used to compress the alloy at temperatures of 25—800 ℃ and strain rate of 10-4—10-2 s-1. The effect of Yb2O3 on the mechanical properties of Ti-1100 as-cast alloy was investigated. Scanning electron microscopy was used to observe the microstructure changes and compression fracture appearance of the alloy. The results show that the yield strength of Ti-1100 alloy was improved obviously by the addition of Yb2O3. At 25—600 ℃, the alloy with Yb2O3 content of 0.45wt% had the best compression yield strength improvement. At 800 ℃, the alloy had the highest compressive yield strength when the Yb2O3 content is 0.60wt%. The grain size and α lamellar spacing of Ti-1100 alloy were refined obviously by adding Yb2O3. The plastic deformation ability of the alloy with Yb2O3 content of 0.45wt% is obviously enhanced.
贾宝华, 刘翔, 顾永强, 李革. Yb2O3对Ti-1100铸态合金高温力学性能的影响[J]. 材料导报, 2020, 34(4): 4087-4092.
JIA Baohua, LIU Xiang, GU Yongqiang, LI Ge. Effect of Yb2O3 on Mechanical Properties of Ti-1100 As-cast Alloy Under High Temperature. Materials Reports, 2020, 34(4): 4087-4092.
1 Jia B H, Song W D, Tang H P, et al. Rare Metal Materials and Engineering, 2014,43(9),2157(in Chinese). 贾宝华, 宋卫东, 汤慧萍, 等. 稀有金属材料与工程, 2014, 43(9), 2157. 2 Zeng L Y, Zhao Y Q, Hong Q, et al. Titanium Industry Progress, 2012,29(5),1(in Chinese). 曾立英, 赵永庆, 洪权, 等. 钛工业进展, 2012, 29(5), 1. 3 Cui W F, Hong Q, Liu C M, et al. Journal of Northeastern University(Natural Science), 2003,24(6),572(in Chinese). 崔文芳, 洪权, 刘春明, 等. 东北大学学报(自然科学版), 2003, 24(6), 572. 4 Deng J, Yang G J. Rare Metal Materials and Engineering, 1993,22(5),1(in Chinese). 邓炬, 杨冠军. 稀有金属材料与工程, 1993, 22(5), 1. 5 Zeng L Y, Hong Q, Zhao Y Q, et al. Rare Metal Materials and Engineering, 2014, 43(10),2407(in Chinese). 曾立英, 洪权, 赵永庆, 等. 稀有金属材料与工程, 2014, 43(10), 2407. 6 Mei Tangfang, Hong Quan, Zhao Yongqing, et al. Hot Working Techno-logy, 2010,39(24),11(in Chinese). 梅汤芳, 洪权, 赵永庆, 等. 热加工工艺, 2010, 39(24), 11. 7 Liu J Y, Wang W Y, Chen Y Y,et al. Transactions of Materials and Heat Treatment, 2017, 38(7),44(in Chinese). 刘冀尧, 王文焱, 陈玉勇, 等. 材料热处理学报, 2017, 38(7), 44. 8 Hang W J, Wang W Y, Zhang H Y, et al. Chinese Journal of Rare Me-tals, 2017, 41(3),245(in Chinese). 黄文君, 王文焱, 张豪胤, 等. 稀有金属, 2017, 41(3), 245. 9 Wang K S, Tan J F, Hu P, et al. Materials Science and Engineering:A, 2015,636,415. 10 Kyosuke U, Shinichiro N, Takayuki N. Materials Transactions, 2013,54(2),161. 11 Yu S R, Zhang X P, He Z M, et al. Journal of Biomedical Engineering, 2004, 21(1),102(in Chinese). 于思荣, 张新平, 何振明, 等. 生物医学工程学杂志, 2004, 21(1), 102. 12 Song X, Niinomi M, Nakai M, et al. Materials Science and Engineering:C, 2012, 32,542. 13 Hotta S, Yamada K, Murakami T, et al. ISIJ International, 2006, 46(1),129. 14 Castro V D, Leguey T , Munoz A, et al. Materials Science and Enginee-ring:A, 2005,400-401,345. 15 Li B L, Wang T B, Han P, et al. Materials Science Forum, 2017, 898,586. 16 Zhu J B, Hu Z, Yan H,et al. Hot Working Technology, 2014,43(14),39(in Chinese). 诸建彬, 胡志, 闫洪, 等. 热加工工艺, 2014, 43(14), 39. 17 Zhang D P, Tian Z, Tang D X, et al. Chinese Journal of Rare Metals, 2010,34(2),202(in Chinese). 张德平, 田政, 唐定骧, 等. 稀有金属, 2010, 34(2), 202. 18 Xu C X, Wang X, Zhang J S, et al. Rare Metal Materials and Enginee-ring, 2014,43(8),1809. 19 Zhang S, Yang C C, Zu S Q, et al. Hot Working Technology, 2014,43(15),7(in Chinese). 张烁, 杨翠翠, 俎世琦, 等. 热加工工艺, 2014, 43(15), 7. 20 Zhao M L, Luo L M, Wang S, et al. Rare Metal Materials and Enginee-ring, 2016, 45(12),3181(in Chinese). 赵美玲, 罗来马, 王爽, 等. 稀有金属材料与工程, 2016, 45(12), 3181.