Abstract: HR3C is widely used in superheater and reheater of ultra supercritical unit due to its great high-temperature mechanical properties and high-temperature antioxidant properties. In order to promote its industrial application and improve the parameter efficiency of the unit, it is urgent to conduct in-depth research on HR3C heat resistant steel, especially the relationship between the precipitation and the property during long-term service. The research progress of HR3C microstructure, precipitation evolution, the influence of alloyed elements on precipitated phase, oxidation behavior during service, hardness, mechanical properties, aging strength, impact toughness, corrosion resistance, welding properties and fatigue properties are briefly described. Then the reason for the sharp decline of impact toughness after the service is analyzed in this review. Finally, the critical issues in the further research of HR3C is also prospected.
封帆, 王美玲, 李振华, 陆永浩. 超超临界机组用HR3C奥氏体耐热钢研究进展[J]. 材料导报, 2021, 35(9): 9186-9195.
FENG Fan, WANG Meiling, LI Zhenhua, LU Yonghao. Research Progress of Austenitic Heat Resistant Steel HR3C Used for Ultra Supercritical Unit. Materials Reports, 2021, 35(9): 9186-9195.
1 Liu Z D, Cheng S C, Bao H S, et al. Iron & Steel,2009,44(6),1(in Chinese). 刘正东,程世长,包汉生,等.钢铁,2009,44(6),1. 2 Yang D, Xu H. Boiler Manufacturing,2006(2),6(in Chinese). 杨冬,徐鸿.锅炉制造,2006(2),6. 3 Li S H, Liu L, Peng H W. Coal Processing & Comprehensive Utilization,2020(2),65(in Chinese). 李少华,刘利,彭红文.煤炭加工与综合利用,2020(2),65. 4 Chen T K. World Sci-Tech R & D,2005(6),42(in Chinese). 陈听宽.世界科技研究与发展,2005(6),42. 5 Hu P. Electric Power Construction,2005(6),29(in Chinese). 胡平.电力建设,2005(6),29. 6 Tian Y L. Metal Working,2009(16),66(in Chinese). 田彦来.金属加工,2009(16),66. 7 Yang H C, Xie X Y, Zhang L, et al. Power Equipment,2009(2),122(in Chinese). 杨华春,谢逍原,张林,等.发电设备,2009(2),122. 8 Tian L Q. Investigation on the microstructure and properties of austenitic heat resistant steel HR3C. Master's Thesis, Shandong University of Technology, China,2012(in Chinese). 田丽倩.奥氏体耐热钢HR3C的显微组织和力学性能研究.硕士学位论文,山东理工大学,2012. 9 Li X M, Zhang Z W, Du B S, et al. Materials for Mechanical Enginee-ring,2019(8),51(in Chinese). 李新梅,张忠文,杜宝帅,等.机械工程材料,2019(8),51. 10 Luo K J, Zhao Y F, Zhang L, et al. Transactions of Materials and Heat Treatment,2017,38(7),79(in Chinese). 罗坤杰,赵彦芬,张路,等.材料热处理学报,2017,38(7),79. 11 Yang Y H, Zhu L H, Wang Q J, et al. Materials Science and Engineering A,2014,608,164. 12 Terada M, Saiki M, Costa I, et al. Journal of Nuclear Materials,2006,358(1),40. 13 Lv Y N, Liu S T, Zhang H J. Chinese Journal of Power Engineering,2013,33(10),822(in Chinese). 吕一楠,刘树涛,张红军.动力工程学报,2013,33(10),822. 14 Li X M, Zhang Z W, Li W, et al. Hot Working Technology,2019,48(4),68(in Chinese). 李新梅,张忠文,李文,等.热加工工艺,2019,48(4),68. 15 Hu Z F, Zhang Z. Materials Science and Engineering: A,2018,742,451. 16 Okada H, Igarashi M, Yamamoto S, et al. In: Proceedings of ASME 2007 Pressure Vessels and Piping Conference. USA,2007,pp.181. 17 Zhang Z, Hu Z, Tu H, et al. Materials Science and Engineering A,2016,681,74. 18 Yang G, Sun L J, Zhang L N, et al. Journal of Iron and Steel Research,2009,21(2),39(in Chinese). 杨钢,孙利军,张丽娜,等.钢铁研究学报,2009,21(2),39. 19 Wang H. Study on precipitation kinetics of σ phase in HR3C austenitic stainless steel. Master's Thesis, Dalian University of Technology, China,2016(in Chinese). 王慧.HR3C钢中σ相析出动力学研究.硕士学位论文,大连理工大学,2016. 20 Yin Z, Cai H, Liu H G. Proceedings of the CSEE,2011,31(29),103(in Chinese). 殷尊,蔡晖,刘鸿国.中国电机工程学报,2011,31(29),103. 21 Iseda A, Okada H, Semba H, et al. Energy Materials,2007,2(4),199. 22 Cao T S, Cheng C Q, Zhao J, et al. Acta Metallurgica Sinica(English Letters),2019,32(11),1355. 23 Guan K S, Xu X D, Zhang Y Y, et al. Engineering Failure Analysis,2005,12(4),623. 24 Yang Y H, Zhu L H, Jiang Y, et al. Transactions of Materials and Heat Treatment,2013,34(z2),106(in Chinese). 杨亚红,朱丽慧,姜筠,等.材料热处理学报,2013,34(z2),106. 25 Yang X Y. Microstructure evolution and fracture behavior of 316LN austenitic stainless steel for nuclear power plant during hot deformation. Ph.D. Thesis, University of Science and Technology Beijing, China,2016(in Chinese). 杨晓雅.核电用316LN奥氏体不锈钢热变形组织演变与断裂行为.博士学位论文,北京科技大学,2016. 26 Bai J M, Yuan Y, Zhang P, et al. Materials Science and Engineering: A,2020,784,138943. 27 Bai Y, Zhang Z, Yan Y. Materials at High Temperatures,2019,36(4),344. 28 Oliveira M P D, Zhang W, Yu H Y, et al. In: Energy Materials 2014. China,2014,pp.271. 29 Bai J M. Effect of Co, Cr and C on microstructure and mechanical properties of modified HR3C during long-time aging. Master's Thesis, Xi'an University of Technology, China,2019(in Chinese). 白佳铭.Co、Cr、C对改性HR3C长期时效组织及力学性能的影响.硕士学位论文,西安理工大学,2019. 30 Yang L, Qing W, Dong H W, et al. Materials Chemistry and Physics,2020,239,122306. 31 Mu C H, Yang Z, Zhao X B, et al. Hot Working Technology,2018,47(2),23(in Chinese). 牟春华,杨征,赵新宝,等.热加工工艺,2018,47(2),23. 32 Peng B C, Zhang H, Hong J, et al. Materials Science and Engineering A,2011,528(10),3625. 33 Fang X D, Wang Y, Fan G W, et al. Journal of Materials Engineering,2017,45(6),112(in Chinese). 方旭东,王岩,范光伟,等.材料工程,2017,45(6),112. 34 Huang Z P, Hu Z F, Wang Q J, et al. Metallic Functional Materials,2013,20(1),19(in Chinese). 黄竹平,胡正飞,王起江,等.金属功能材料,2013,20(1),19. 35 Fang Y Y, Zhao J, Li X N. Acta Metallurgica Sinica (English Letters),2010,46(7),844. 36 Tamura M, Kato Y, Sakasegawa H. ISIJ International,2002,42(12),1444. 37 Ashby M F, Gandhi C, Taplin D M R. Acta Metallurgica,1979,27(5),699. 38 Zhen Z J. Boiler Technology,2011,42(4),46(in Chinese). 郑子杰.锅炉技术,2011,42(4),46. 39 Zhao X B, Hou B R, Yang Z, et al. Special Casting & Nonferrous Alloys,2017,37(7),711(in Chinese). 赵新宝,侯本睿,杨征,等.特种铸造及有色合金,2017,37(7),711. 40 Zhang Z W, Li X M, Du B S, et al. Heat Treatment of Metals,2015,40(10),57(in Chinese). 张忠文,李新梅,杜宝帅,等.金属热处理,2015,40(10),57. 41 Zhang X P, Wang P. Electric Welding Machine,2010,40(2),117(in Chinese). 张学鹏,王萍.电焊机,2010,40(2),117. 42 Chai C G. Advanced Materials Research,2014,891-892,377. 43 He J J, Sandström R, Vujic S. In: 21st European Conference on Fracture. Italy,2016,pp.2. 44 Peng J, Gao Y, Dai Q, et al. Acta Metallurgica Sinica,2019,55(6),773(in Chinese). 彭剑,高毅,代巧,等.金属学报,2019,55(6),773. 45 Natesan K, Park J H. International Journal of Hydrogen Energy,2007,32(16),3689. 46 Wang Y K, Liu G M, Zhao C, et al. Surface Technology,2019,48(11),365(in Chinese). 汪元奎,刘光明,赵超,等.表面技术,2019,48(11),365. 47 Zhao Y R. Study on creep property and oxidation behavior of 9Cr-6Co-2W-1Mo ferritic creep resistant steels. Master's Thesis, Wuhan University of Science and Technology, China,2018(in Chinese). 赵妍蓉.9Cr-6Co-2W-1Mo铁素体耐热钢蠕变性能及氧化行为的研究.硕士学位论文,武汉科技大学,2018. 48 Zhao S Q, Xie X S. Special Steel,2004,24(6),36(in Chinese). 赵双群,谢锡善.特殊钢,2004,24(6),36. 49 Gao T, Wang J, Dong N, et al. Metallurgical Research & Technology,2019,116(4),401. 50 Xie X F. Stress corrosion cracking and fatigue behavior of cold drawn 316 austentic stainless steel. Ph.D. Thesis, Shanghai Jiao Tong University, China,2017(in Chinese). 谢兴飞.冷拔316奥氏体不锈钢应力腐蚀开裂与疲劳行为.博士学位论文,上海交通大学,2017. 51 Li X M, Zhang Z W, Wei Y Z, et al. Hot Working Technology,2016,45(5),236(in Chinese). 李新梅,张忠文,魏玉忠,等.热加工工艺,2016,45(5),236. 52 Wang Z. Investigation of the corrosion behavior and passive film degration for austentic stainless steel in H2S-containing environment. Ph.D. Thesis, University of Science and Technology Beijing, China,2018(in Chinese). 王竹.奥氏体不锈钢在H2S环境下的腐蚀行为与钝化膜演化研究.博士学位论文,北京科技大学,2018. 53 Wright I G, Pint B A. In: Corrosion 2002—57th Annual Conference & Exposition. Houston,2002,pp.3810. 54 Sarver J M, Tanzosh J M, Mohammed S. In: 28th International Technical Conference on Coal Utilization & Fuel Systems. USA,2003,pp.469. 55 Hansson A N, Montgomery M. Materials Science Forum,2006,39(1045),181. 56 Wu Z Q, Chang Z, Bai Y. Journal of Iron and Steel Research,2015,27(4),51(in Chinese). 吴增强,常征,白银.研究学报,2015,27(4),51. 57 Wang J, Qiao Y, Dong N, et al. Oxidation of Metals,2018,89(5-6),713. 58 Yang Z, Lu J T, Zhao X B, et al. Journal of Chinese Society of Power Engineering,2015,35(10),859(in Chinese). 杨珍,鲁金涛,赵新宝,等.动力工程学报,2015,35(10),859. 59 Li J J, Ma H D, Wang Y G, et al. Energies,2019,12(3),521.