Research Progress on Functional Modification of SiO2 and Its Interface with Polymer Matrix
DONG Yufei1,2, MA Jianzhong1,2, LIU Chao3, BAO Yan1,2, LIN Yang3, WU Yingke1,2
1 College of Bioresources Chemical and Materials Engineering, Shaanxi University of Science and Technology, Xi’an 710021 2 National Demonstration Center for Experimental Light Chemistry Engineering Education, Shaanxi University of Science and Technology, Xi’an 710021 3 Shaanxi Collaborative Innovation Center of Industrial Auxiliary Chemistry and Technology, Shaanxi University of Science and Technology, Xi’an 710021
Abstract: As one of the most commonly used inorganic nanomaterials, nano-silica (SiO2) has been widely concerned and applied by researchers in various fields. Nano-SiO2 has been used as the modified filler, its polymer nanocomposites combine the advantages of both polymer matrix and nano-SiO2, and thus show excellent mechanical properties, thermal properties, optical properties and chemical stability, etc. However, the surface of nano-SiO2 is rich in a large amount of active silicone hydroxyl, which is easy to aggregate. So, it’s difficult to obtain uniform dispersion on the nanometer scale and good interfacial adhesion between nano-SiO2 and polymer matrix materials by general methods. Therefore, before the preparation of polymer-based nanocomposites modified by nano-SiO2, surface modification is required to improve the interfacial compatibility between SiO2 particles and polymer matrix and its dispersibility in the polymer matrix, and give it a certain degree of functionality. At present, there are many modification methods for nano-SiO2. In general, it is mainly physical modification and chemical modification, and according to different types of modified agents, it can be divided into organic modification, inorganic modification and hybrid modification. The excellent properties of polymer/nano SiO2 composites depend not only on the properties of the two components of organic polymer and inorganic nano-SiO2, but also on the interfacial structure and morphological characteristics between them. Although the volume content of interface phase is only a small part of total volume content, but the interaction between the interfaces, the differences between polymer structure and matrix structure at the interface, and the changes in the microstructure of interface phase and so on will significantly change the macro-performance of whole composite system. Therefore, the interface research between them has important scientific significance for the optimization design of nanocomposite properties. In recent years, the research of interface between polymer and inorganic nanoparticles mainly focused on two aspects. On the one hand, the physical and chemical properties of the surface of polymer and inorganic nanoparticles affect the properties at the interface. On the other hand, the interfacial interaction between polymer matrix and inorganic nanoparticles affects the properties of its composites. At present, the microstructure (such as roughness, thickness, etc.) and chemical structure (such as chemical bonding, bond energy, etc.) of the interface phase are often tested by modern instrumental analysis technology, or the molecular dynamics simulation is used to elucidate the molecular assembly structure and the mechanism of mutual interaction. Which can explain the interface performance and interface behavior more accurately from a theoretical perspective, and provide a theoretical basis and new methods for the optimal design of composites. In this paper, the research progress of organic modification, inorganic modification and hybrid modification on the functionalization of nano-SiO2 is summarized. The advantages and disadvantages of different modification methods are discussed and compared, and recent advances in the research of polymer/SiO2 interface in modern instrumental analysis characterization and molecular dynamics simulation are reviewed in detail. Finally, the future research focus of the interaction between nano-SiO2 and polymer matrix is forecasted.
董雨菲, 马建中, 刘超, 鲍艳, 林阳, 吴英柯. SiO2的功能化改性及其与聚合物基体的界面研究进展[J]. 材料导报, 2019, 33(11): 1910-1918.
DONG Yufei, MA Jianzhong, LIU Chao, BAO Yan, LIN Yang, WU Yingke. Research Progress on Functional Modification of SiO2 and Its Interface with Polymer Matrix. Materials Reports, 2019, 33(11): 1910-1918.
1 Han J X, She L J, Zhai L X, et al. Materials Review,2010,24(s1),6(in Chinese). 韩静香,佘利娟,翟立新,等.材料导报,2010,24(专辑15),6. 2 Li M, Lam J W Y, Mahtab F, et al. Journal of Materials Chemistry B,2013,1(5),676. 3 Rimola A, Costa D, Sodupe M, et al. Chemical Reviews,2013,113(6),4216. 4 Mamaeva V, Sahlgren C, Lindén M. Advanced Drug Delivery Reviews,2013,65(5),689. 5 Perez R A, Singh R K, Kim T H, et al. Materials Horizons,2017,5(4),772. 6 Suzuki R, Kishida M, Hirano T. Journal of Applied Physics,2013,114(13),133502. 7 Li X, Yang Y, Yang Q. Journal of Materials Chemistry A,2013,1(5),1525. 8 Shan W, Liao M Y. Chinese Polymer Bulletin,2006(3),1 (in Chinese). 单薇,廖明义.高分子通报,2006(3),1. 9 Gong X Q, Wang Y Q, Zhang L. Materials Review B: Research Papers,2016,30(2),52(in Chinese). 公绪强,王雅祺,张利.材料导报:研究篇,2016,30(2),52. 10 Suthabanditpong W, Takai C, Fuji M, et al. Physical Chemistry Chemical Physics,2016,18(24),16293. 11 Wang Y, Guo Y, Cui R, et al. Science & Engineering of Composite Materials,2014,21(4),471. 12 Raja V L, Kumaravel A. Polymers & Polymer Composites,2015,23(6),427. 13 He S T, Liu B C. Materials Research and Application,2016,10(2),71(in Chinese). 何淑婷,刘宝春.材料研究与应用,2016,10(2),71. 14 Ye G B. Synthesis and properties of polymer/SiO2 hybrids. Master’s Thesis, South China University of Technology, China,2015(in Chinese). 叶光宝.聚合物/SiO2杂化材料的制备与性能.硕士学位论文,华南理工大学,2015. 15 He J L, Peng S M, Zhou Y, et al. Proceedings of the CSEE,2016,36(24),6596(in Chinese). 何金良,彭思敏,周垚,等.中国电机工程学报,2016,36(24),6596. 16 Sun R. Characterisation of interfacial states in the SiO2/LDPE nanocomposite from first principles computations. Master’s Thesis, Harbin University of Science and Technology, China,2016(in Chinese). 孙蕊.纳米SiO2与聚乙烯基体界面态第一性原理计算研究.硕士学位论文,哈尔滨理工大学,2016. 17 Zhou H, Wang H, Niu H, et al. Advanced Functional Materials,2013,23(13),1664. 18 Yu M, Jambhrunkar S, Thorn P, et al. Nanoscale,2013,5(1),178. 19 Yang W, Ding P, Zhou L, et al. Applied Surface Science,2013,282(5),38. 20 Zhang H. Organically modified silica prepared by mechanochemical and the study of its composite materials. Master’s Thesis, Wuhan University of Technology, China,2014(in Chinese). 张慧.机械力化学法制备有机改性二氧化硅及其复合材料的研究.硕士学位论文,武汉理工大学,2014. 21 Cao P, Ni Y, Zou R, et al. RSC Advances,2014,5(5),3417. 22 Namvar-Mahboub M, Pakizeh M. Separation & Purification Technology,2013,119(46),35. 23 Zhang Y, Chen H, Wen Y, et al. Colloids & Surfaces A Physicochemical & Engineering Aspects,2014,441(3),16. 24 Lin B L, Cui S, Liu X Y, et al. Journal of Wuhan University of Technology (Materials Science Edition),2013,28(5),916. 25 Zhang Y H, Zhai L L, Wang Y, et al. Journal of Materials Science and Engineering,2012,30(5),93(in Chinese). 张云浩,翟兰兰,王彦,等.材料科学与工程学报,2012,30(5),93. 26 Yang L. The research of structure and properties of nano-SiO2/NR composite material. Master’s Thesis, Hainan University, China,2011(in Chinese). 杨蕾.纳米SiO2/NR复合材料结构与性能的研究.硕士学位论文,海南大学,2011. 27 Morita S, Iijima M, Tatami J. Advanced Powder Technology,2016,28(1),30. 28 Dou W, Niu Y, Liu X, et al. Journal of Sol-Gel Science and Technology,2013,68(2),302. 29 Maleki H, Dures L, Portugal A. Journal of Non-Crystalline Solids,2014,385(2),55. 30 Yuan Y, Chen N, Liu R, et al. Materials Research Bulletin,2014,50(2),392. 31 Fouconnier B, Románguerrero A, Lópezserrano F. Journal of Macromole-cular Science Part A,2016,53(7),403. 32 Sun Z, Zhang L X, Qi J L, et al. Materials & Design,2015,88,51. 33 Mallakpour S, Marefatpour F. Progress in Organic Coatings,2014,77(8),1271. 34 Mallakpour S, Naghdi M. Polymer,2016,90,295. 35 Vives S, Meunier C. Materials Letters,2013,91(2),165. 36 Wu Y T, Zhang Q F, Tong X F, et al. Journal of Shaanxi University of Science & Technology,2017,35(3),63(in Chinese). 伍媛婷,张琴帆,仝小飞,等.陕西科技大学学报,2017,35(3),63. 37 Tao Y. Surface modified of monodisperse colloidal silica and preparation of SiO2/Ag core/shell particles. Master’s Thesis, East China Normal University, China,2009(in Chinese). 陶妍.单分散二氧化硅的表面改性及二氧化硅/银复合粒子的制备.硕士学位论文,华东师范大学,2009. 38 Wang M, Tian D, Tian P, et al. Applied Surface Science,2013,283(20),389. 39 Tang M, Lin X H, Li M G, et al. Journal of Wuhan University of Techno-logy (Materials Science Edition),2016,31(4),736. 40 Police A K R, Basavaraju S, Valluri D K, et al. Journal of Materials Science & Technology,2013,29(7),639. 41 Liu C H. B2O3-modified SiO2 microwave dielectric materials. Master’s Thesis, Zhejiang University, China,2015(in Chinese). 刘聪慧.B2O3改性SiO2微波介质材料.硕士学位论文,浙江大学,2015. 42 Panice L B, Oliveira E A D, Filho R A D M, et al. Materials Science & Engineering B,2014,188(10),78. 43 Luo H. Research on hydrophobicity and thermostability of organic-inorga-nic hybrid modified phenolic. Master’s Thesis, Harbin Institute of Technology, China,2015(in Chinese). 罗浩.有机无机杂化改性酚醛疏水及耐热性能研究.硕士学位论文,哈尔滨工业大学,2015. 44 Jin I L, Lee W K. Materials Letters,2017,206(206),193. 45 Mohammed A M. Chinese Journal of Physics,2017,55(2),242. 46 Yang X, Liu X, Tang W, et al. Korean Journal of Chemical Engineering,2017,34(3),723. 47 Dang J, Guo Z, Zheng X, et al. Analytical Chemistry,2014,86(18),8943. 48 Kuzminska M, Kovalchuk T V, Backov R, et al. Journal of Catalysis,2014,320(1),1. 49 Cheng G J, Song R J, Miao J B, et al. Materials Review A: Review Papers,2012,26(6),130(in Chinese). 程国君,宋瑞娟,苗继斌,等.材料导报:综述篇,2012,26(6),130. 50 Guo Y Y. The investigation of the interface between the CNT and the rubber. Master’s Thesis, Beijing University of Chemical Technology, China,2016(in Chinese). 郭燕燕.碳纳米管/橡胶纳米复合材料界面性能研究.硕士学位论文,北京化工大学,2016. 51 Mei Z, Gu M Y. Journal of Materials Science and Engineering,1996(3),1(in Chinese). 梅志,顾明元.材料科学与工程学报,1996(3),1. 52 Ruan W H, Rong M Z, Zhang M Q. Materials Research and Application,2010,4(4),736(in Chinese). 阮文红,容敏智,章明秋.材料研究与应用,2010,4(4),736. 53 Singha S, Jana T. ACS Applied Materials & Interfaces,2014,6(23),21286. 54 Li H, Song L, Fu Y, et al. Composites Science & Technology,2017,138,169. 55 Holt A P, Griffin P J, Bocharova V, et al. Macromolecules,2014,47(5),1837. 56 Zhu J J, Zhai Q G, Li X L, et al. Chemical Research and Application,2014(7),988(in Chinese). 朱建君,翟秋阁,李晓玲,等.化学研究与应用,2014(7),988. 57 Feng J M, Liu X Q, Bao R Y, et al. RSC Advances,2015,5(91),74295. 58 Parpaite T, Otazaghine B, Taguet A, et al. Polymer,2014,55(11),2704. 59 Wei X, Zhao C, Ma J, et al. RSC Advances,2016,6(3),1870. 60 Antonelli C, Serrano B, Baselga J, et al. Materials Letters,2014,137(137),460. 61 Grenoble Z, Baldelli S. Journal of Physical Chemistry B,2013,117(34),9882. 62 Li J, Yang Y Q, Luo X, et al. Rare Metal Materials and Engineering,2013,42(3),644(in Chinese). 李健,杨延清,罗贤,等.稀有金属材料与工程,2013,42(3),644. 63 Yan L M. Theory and practice of molecular dynamics simulation, Science Press, China,2013(in Chinese). 严六明.分子动力学模拟的理论与实践,科学出版社,2013. 64 Jiang Q. The interface modification and molecular dynamics simulation of carbon nanotube and polyimide and fabrication and characterization of carbon nanotube reinforced polyimide composite. Master’s Thesis, Donghua University, China,2013(in Chinese). 姜茜.碳纳米管与聚酰亚胺界面优化、分子动力学模拟及其复合材料的结构性能表征.硕士学位论文,东华大学,2013. 65 Feng T T, Qin Y D. Science and Technology Innovation Herald,2015(23),248. 冯婷婷,秦宜德.科技创新导报,2015(23),248. 66 Dai S, Liu Y, Zhang J, et al. Composite Interfaces,2017,24(9),897. 67 Wei Q, Zhang Y, Wang Y, et al. Journal of Materials Science,2017,52(21),12889. 68 Nicola A D, Avolio R, Monica F D, et al. RSC Advances,2015,5(87),71336.