The influence of solution treatment on microstructure and mechanical properties of GH3625 alloy sheet were investigated by OM, SEM, EDS, universal testing machine and Rockwell hardness tester and other means. The results indicated that the grains were equiaxed and there were a large number of annealing twins after the solution treatment. As solution treatment temperature was more than 1 130 ℃, the carbides in alloy almost completely dissolve into the matrix. Grain size was prompted by temperature increasing in the range of 890 ℃ to 1 190 ℃, and the energy (Qg) of grain growth was 227.18 kJ/mol. At different solution temperature, the grain size and room-temperature mechanical properties of GH3625 alloy accord with Hall-Petch relation. The main strengthening mechanism was fine grained strengthening. With the increase of temperature, the fracture mode of GH3625 alloy sheet was changed from brittle fracture to ductile fracture.
3 Zhang H B. Inconel625 alloy progress abroad[J].Special Steel Technology, 2000(3):69(in Chinese).
4
张红斌 . 国外Inconel625合金的进展[J].特钢技术, 2000(3):69.
5
4 郭建亭. 高温合金材料学[M]. 北京: 科学出版社, 2008: 87.
6
Shankar V, Rao K B S, Mannan S L . Microstructure and mechanical properties of Inconel 625 superalloy[J]. Journal of Nuclear Mate-rials, 2001,288(2-3):222.
7
Floreen S, Fuchs G E, Yang W J . “The metallurgy of alloy 625” superalloys 718, 625 and various derivatives[M]. TMS,Warrendale,PA, 1994: 13.
8
Ou X Z, Yao L, Huang Y P . Influence of solution temperature on the microstructure and mechanical properties of UNS N06625 alloy[J]. Metallic Functional Materials, 2016,23(2):55(in Chinese).
Peng C H, Chang H, Hu R , et al. Static recrystallization kinetics of Haynes230 superalloy[J]. Journal of Aeronautical Materials, 2011,31(2):8(in Chinese).
Yang G, Sun L J, Zhang L N , et al. Annihilation of deformation twins and formation of annealing twins[J]. Journal of Iron and Steel Research, 2009,21(2):39(in Chinese).
Yang G, Wang C, Zhang L Y , et al. Recovery and recrystallization mechanism in austenitic stainless steel[J]. Transactions of Materials and Heat Treatment, 2010,31(12):51(in Chinese).
Xia S, Li H, Zhou B X , et al. Control and application of annealing twins in metallic materials: Grain boundary engineering[J]. Chinese Journal of Nature, 2010,32(2):94(in Chinese).
Feng H, Song Z G, Zheng W J , et al. Effect of solution treatment on microstructure and mechanical property of Inconel690[J]. Journal of Iron and Steel Research, 2009,21(3):46(in Chinese).
Kai J J, Yu G P, Tsai C H , et al. The effects of heat treatment on the chromium depletion, precipitate evolution and corrosion resis-tance of lnconel alloy 690[J]. Metallurgical Transactions A, 1989,20:2057.
24
17 毛卫民. 金属的再结晶与晶粒长大[M]. 北京: 冶金工业出版社, 1994: 62.
25
Fang X D, Han D P, Li Y . Effect of heat treatment on microstructure and mechanical properties of GH625 alloy[J]. Hot Working Technology, 2013,42(8):204(in Chinses).
Sellars S M, Whiteman J A . Recrystallization and grain growth in hot rolling[J]. Metal Science, 1979,13:198.
28
Anelli E . Application of mathematical modelling to hot rolling and controlled colling of wire rods and bars[J]. ISIJ Interational, 1992,32:440.
29
Guo Q M, Li H T, Li D F , et al. Hot extrusion moulding process and microstructure evolution of GH625 superalloy tubes[J]. Chinese Journal of Rare Metals, 2011,35(5):684(in Chinese).
Zhong Q P, Zhao Z H, Zhang Z . Development of “Fractography” and research of fracture micromechanism[J]. Journal of Mechanical Strength, 2005,27(3):358(in Chinese).
4 Wu D, Tian L X, Ma C L , et al. Tensile fracture behavior of Ni-based single crystal superalloy[J]. Materials Review B:Research Papers, 2016,30(12):76(in Chinese).