Abstract: TiZr3V6 alloy was prepared by plasma arc melting technique. The microstructure and phase composition of TiZr3V6 alloy were studied by scanning electron microscope, energy spectrum analysis, X-ray diffraction analysis. The results show that TiZr3V6 alloy was composed of dendritic V based solid solution phase, ZrV2 phase and α-Zr phase. After hydrogen absorption saturation, the alloy was composed of V16Zr8H36.29 phase, VH2.01 phase and ZrH1.801 phase, and powdered into particles that existed a large number of micro-cracks.
1 Zhang Y, Wei X Y, Mao C H,et al. Journal of Alloys and Compounds,2009,485,200. 2 Marenco N, Allegato G, Konstner H, et al. DAVID final activity report.Germany:ISIT,IST-027240,2009. 3 Benvenuti C, Chiggiato P, Cicoira F, et al.Journal of Vacuum Science & Technology A, 1998, 16(1),148. 4 Tominetti S, Amiotti M.Proceedings of the IEEE, 2002,90(4),540. 5 万玉金.吸气剂,江苏科学技术出版社,1983. 6 Chiggiato P, Pinto P C.Thin Solid Films, 2006, 515(2),382. 7 Benvenuti C, Cazeneuve J M, Chiggiato P, et al.Vacuum, 1999, 53,219. 8 Benvenuti C, Chiggiato P, Cicoira F, et al.Vacuum,1998,50,57. 9 Prodromides A E, Scheuerlein C, Taborelli M.Vacuum,2001,60,35. 10 Benvenuti C, Chiggiato P, Pinto P C,et al.Vacuum,2001,60,57. 11 Klein B, Redeker A, Züchner H.International Journal of Research in Physical Chemistry and Chemical Physics, 1993, 181(1),95. 12 Hsu Y S, Perng T P. Journal of Alloys and Compounds,1995,227(2), 180. 13 Jain Ankur, Jain R K, Agarwal Shivani, et al.International Journal of Hydrogen Energy, 2007, 32, 2445.
渝公网安备50019002502923号 版权所有：《材料导报》编辑部
2020, Vol. 34 