Preparation of Cross-linked P(VDF-CTFE-DB)/PMN-PT-Sm Nanocomposite Films and Their Dielectric and Energy Storage Performances
HE Tingrui1,2, WANG Yiping1, LI Xiongjie1,2, CHEN Peng1,2, HU Querui1,2, YANG Ying1, NING Honglong3
1 State Key Laboratory of Mechanics and Control of Mechanical Structures, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China 2 College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China 3 State Key Laboratory of Luminescent Materials and Devices, Institute of Polymer Optoelectronic Materials and Devices, School of Materials Science and Engineering, South China University of Technology, Guangzhou 510640, China
Abstract: Afluoropolymer with double bonds (P(VDF-CTFE-DB)) was synthesized via controlled dehydrochlorination of poly(vinylidene fluoride-co-chlorotrifluoroethylene) (P(VDF-co-CTFE)). High permittivity component of samarium-doped Pb(Mg1/3Nb2/3)O3-PbTiO3 (PMN-PT-Sm) ferroelectric was selected as the inorganic composite phase, and the cross-linkable P(VDF-CTFE-DB) was used as polymer matrix. Cross-linking P(VDF-CTFE-DB)/PMN-PT-Sm composite film was synthesized by reacting the free radical initiator. The dielectric properties, breakdown strength, energy-storage performances, and solvent resistance of the P(VDF-CTFE-DB)/PMN-PT-Sm nanocomposite films were investigated. As a result, the dielectric constant increases with increasing the volume fraction of PMN-PT-Sm nanoparticles. A maximal dielectric constant of 65 at 100 Hz associated with a dielectric loss of only about 0.058 was obtained in the P(VDF-CTFE-DB)/PMN-PT-Sm nanocomposite film with 30% of PMN-PT-Sm nanoparticle addition. It is experimentally found that the cross-linked network structure has a great influence on the breakdown strength, energy storage performances and compatibility of P(VDF-CTFE-DB)/PMN-PT-Sm nanocomposite films. The significantly improved breakdown strength up to 3 200 kV/cm and the highest discharge energy density of about 9.7 J/cm3 for the cross-linking P(VDF-CTFE-DB)/PMN-PT-Sm nanocomposite film with 20% of PMN-PT-Sm have been achieved. Constructing cross-linked networks among P(VDF-CTFE-DB) and PMN-PT-Sm nanoparticles could be an effective way to decrease the leakage current and dielectric loss, as well as to enhance the breakdown strength and the energy storage performances in the polymer nanocomposites.
何亭睿, 王一平, 李雄杰, 陈朋, 胡悫睿, 杨颖, 宁洪龙. 可交联型P(VDF-CTFE-DB)/PMN-PT-Sm纳米复合薄膜的制备及介电和储能性能[J]. 材料导报, 2020, 34(18): 18152-18158.
HE Tingrui, WANG Yiping, LI Xiongjie, CHEN Peng, HU Querui, YANG Ying, NING Honglong. Preparation of Cross-linked P(VDF-CTFE-DB)/PMN-PT-Sm Nanocomposite Films and Their Dielectric and Energy Storage Performances. Materials Reports, 2020, 34(18): 18152-18158.
1 Ji W, Deng H, Sun C, et al. Composites Science and Technology, 2019, 172, 117. 2 Pan Z, Yao L, Liu J, et al. Journal of Materials Chemistry C, 2019, 7(2), 405. 3 Prateek, Bhunia R, Siddiqui S, et al. ACS Applied Materials & Interfaces, 2019, 11(15), 14329. 4 Barshaw E J, White J, Chait M J, et al. IEEE Transactions on Magne-tics, 2006, 43(1), 223. 5 Dai Z H, Li T, Gao Y, et al. Composites Science and Technology, 2019, 169, 142 6 Xie Y, Jiang W, Fu T, et al. ACS Applied Materials & Interfaces, 2018, 10(34), 29038. 7 Chen G, Lin X, Li J, et al. Ceramics International, 2018, 44(13), 15331. 8 Cho S D, Lee S Y, Hyun J G, et al. Journal of Materials Science: Materials in Electronics, 2005, 16(2), 77. 9 Yu K, Wang H, Zhou Y C, et al. Journal of Applied Physics, 2013, 113(3), 034105. 10 Li F, Lin D, Chen Z, et al. Nature Materials, 2018, 17(4), 349. 11 Cheng Z, Zhou W, Zhang C, et al. Journal of Polymer Science Part B: Polymer Physics, 2018, 56(2), 193. 12 Bai D P, Tan S B, Zhang Z Z.Polymer Materials Science and Enginee-ring, 2013, 29(9), 15(in Chinese). 白德鹏, 谭少博, 张志成. 高分子材料科学与工程, 2013, 29(9), 15. 13 Cheburkov Y, Moore G G I. Journal of Fluorine Chemistry, 2003, 123(2), 227. 14 Tan S, Li J, Gao G, et al.Journal of Materials Chemistry, 2012, 22(35), 18496. 15 Lu X, Zhang L, Tong Y, et al. Composites Part B: Engineering, 2019, 168, 34. 16 Tang Y, Shuang X, Xie Y, et al. Composites Science & Technology, 2016, 124, 10. 17 Lee Y J, Ham S R, Kim J H, et al. Scientific Reports, 2018, 8(1), 2045. 18 Zhang X, Li B W, Dong L, et al. Advanced Materials Interfaces, 2018, 5(11), 2196.