Abstract: This article is prepared for bring the boric acid (BA) and phenylboronic acid (PBA) into phenolic resin (NR), which preparing borate modi-fied phenolic resin to study its curing process, and also improving the use of borate modified phenolic resin as the matrix and glass fiber as the reinforcement. The effect of different boron modification on the friction and wear properties of phenolic resin was prepared. The results showed that both BA and PBA modification can introduce a borate structure into the cured resin, thereby improving the thermal stability of the PR significantly. In addition, the introduction of boric acid esters reduced the friction of PR. Among them, when the PBA content is 30 phr, the friction coefficient is reduced to 0.16 effectively. The SEM showed that the borate can improve the interfacial adhesion performance of the phenolic resin, which improving the friction performance of the modified phenolic resin as efficiently as well.
作者简介: 王亚楠,2018年6月于西安交通大学获得硕士学位,毕业后至今在西安航空学院任教,主要从事酚醛树脂的改性及树脂结构与性能关系的研究。参与了西安市科技局和其他横向项目,研究成果主要发表在Reactive and Functional Polymers、Polymer Degradation and Stability和Organic Letters等国内外期刊,申请专利两项。
引用本文:
王亚楠, 曹凤香, 王永锋, 曹静, 李兆, 吴坤尧. 玻璃纤维增强硼酸酯改性酚醛树脂复合材料的摩擦学性能研究[J]. 材料导报, 2021, 35(18): 18210-18215.
WANG Yanan, CAO Fengxiang, WANG Yongfeng, CAO Jing, LI Zhao, WU Kunyao. Tribology of Glass Fiber Reinforced Borate Modified Phenolic Resin Composite. Materials Reports, 2021, 35(18): 18210-18215.
1 Baekeland L H. Industrial & Engineering Chemistry Research, 1909, 1, 149. 2 Huang F.Phenolic resin and its application, Chemical Industry Press, China,2011 (in Chinese). 黄发荣.酚醛树脂及其应用, 化学工业出版社, 2011. 3 Charles U. Pittman J,Gui Z L.Journal of Inorganic and Organometallic Polymers and Materials, 2006, 16(1), 43. 4 Parameswaran P S, Abraham B T, Thachil E T.Progress in Rubber Plastics Recycling Technology, 2010, 26(1), 31. 5 Mirzapour A, Asadollahi M H, Baghshaei S, et al.Composites Part A: Applied Science and Manufacturing, 2014, 63, 159. 6 Wang D, Gao J, Xu W F, et al.Advanced Materials Research, 2011, 327, 115. 7 Akbar N Q, Hossein R M, Mehdi S K, et al. Journal of Thermal Analysis and Calorimetry, 2017, 128(2), 1027. 8 Qiang M, Zhang S, Lin H, et al.Refractories, 2005, 39(2), 119. 9 Feng L B, Li H, Hao X Z, et al. Journal of Materials Engineering, 2013(9),75(in Chinese). 冯利邦, 李晖, 郝相忠, 等.材料工程, 2013(9), 75. 10 Abdalla M O, Ludwick A,Mitchell T. Polymer, 2003, 44(24), 7353. 11 Zhang W F, Liu C L, Ying Y G, et al.Materials Chemistry and Physics, 2010, 121(1), 89. 12 Chen Z, Chen Y, Li W, et al.Polymer Materials Science & Engineering, 2013, 29(5), 96. 13 Ding J, Huang Z, Qin Y, et al. In:2015 International Conference on Materials and Chemical Engineering. Suzhou,China, 2015, pp.1047. 14 Qian C X, Zhao H K, Xiong Y M, et al. Journal of Functional Materials. 2006, 37(7),1114(in Chinese). 钱春香, 赵洪凯, 熊佑明, 等.功能材料, 2006, 37(7), 1114. 15 Wang S, Jing X, Wang Y, et al. Polymer Degradation and Stability, 2014, 99, 1. 16 Wang S, Wang Y, Bian C, et al. Applied Surface Science, 2015, 331, 519. 17 Wang S J, Wang Y, Wang Y N, et al. In: Conference Record of the 30ND CCSS Congress. Hangzhou, China,2016, pp. 65 (in Chinese). 王淑娟, 王勇, 王亚楠, 等. 30届中国化学会学术年会. 杭州, 2016, pp. 65. 18 Yu J, Zhao W S, Li L L.Chemical Research, 2017, 28(5), 560(in Chinese). 于静, 赵文善, 李路路.化学研究, 2017, 28(5), 560. 19 Zhang L, Wang Y G, Li J S, et al. Lubrication Engineering, 2010, 35(8),67(in Chinese). 张立, 王永刚, 李久盛, 等.润滑与密封, 2010, 35(8), 67. 20 Sun L G, Wang Y G, Zhang L, et al. Lubrication Engineering, 2010(1),52(in Chinese). 孙令国, 王永刚, 张立, 等.润滑与密封, 2010(1), 52. 21 Gao J, Su X, Xia L. International Journal of Polymeric Materials & Polymeric Biomaterials, 2005, 54(10), 949. 22 Yu H J, Ma J, Gao D P, et al. Chinese Journal of Energetic Materials, 2014, 22(1), 1. 23 Qiu J, Wang G J, Feng Y B. Journal of Tongji University (Natural Science), 2007, 35(3), 381 (in Chinese). 邱军, 王国建, 冯悦兵.同济大学学报(自然科学版), 2007, 35(3), 381. 24 Bijwe J, Nidhi, Majumdar N, et al. Wear, 2005, 259(7), 1068. 25 Jiang H, Wu S, Yuan Z, et al. Polymer Degradation & Stability, 2012, 97 (8), 1527. 26 Gao J, Liu Y, Wang F. European Polymer Journal, 2001, 37(1), 207. 27 Gao J, Su X, Xia L. International Journal of Polymeric Materials, 2005, 54(10), 949. 28 Kim G M, Young J O, Chang K J. Journal of Applied Physics, 2013, 114(22), 1553.