Abstract: The reason of the leakage of the control rod drive mechanism's Ω weld base metal is mainly the stress corrosion cracking (SCC). Stress corrosion tests were carried out to investigate the stress corrosion behavior of the Ω weld base metal in different water environments as the normal operating condition of the reactor plant and the abnormal condition inside the Ω weld. The test results showed that, the abnormal water environment inside the Ω weld which was rich in dissolved oxygen and chlorine ion can decline the stress corrosion resistance of the base metal, make the material more sensitive to the SCC and promote the crack expanding. Simultaneity, some advice was also proposed in this article to optimize the water environment inside the Ω weld.
魏乔苑, 李跃忠, 赵毛毛, 冉小兵. 水环境对控制棒驱动机构Ω焊缝母材应力腐蚀的影响[J]. 材料导报, 2020, 34(Z1): 462-465.
WEI Qiaoyuan, LI Yuezhong, ZHAO Maomao, RAN Xiaobing. Effect of Water Environment on Stress Corrosion Property of the Control RodDrive Mechanism's Ω Weld Base Metal. Materials Reports, 2020, 34(Z1): 462-465.
1 Structural Integrity Associates, Inc. California: Structural Integrity Associates, Inc.,1997. 2 H. Barrault. Paris: EDF,2006. 3 凌礼恭,贾盼盼,孙海涛,等.核安全,2016,15(2),64. 4 郑晓敏.核安全,2007(2),24. 5 US. NCR. Washington: US Nuclear Regulatory Commission, 2008. 6 丁亚平,徐雪莲.腐蚀与防护,2001,22(11),489. 7 Kiyeshi Takanabe, Takashi Miyake, Yasumi Nagura.Nuclear Engineering and Design,2002,214,25. 8 凌礼恭,王徐颖,陆永浩,等.材料导报:综述篇,2016,30(7),111. 9 Hyres J W. Virginia: BWXT Services,2003. 10 Pezze C M, Wilson I L W. In: Preceeding of 4th International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactor. Georgia: ANS/NAS,1989. 11 Peter L Andresen, Martin M Morra. Journal of Nuclear Materials,2008,383,97.
渝公网安备50019002502923号 版权所有：《材料导报》编辑部
2020, Vol. 34 