Abstract: Based on new martensite stainless steel electrode used in hot working die overlaying welding, with adding CrN to electrode coat to realize nitrogen alloying, this paper aimed to research the effort of CrN addition on microstructure, hardness and high temperature wear property of deposited metal. The results indicate that the microstructure of deposited metal are martensite and a small amount of residual austenite. The quantity of carbon nitrides in deposited metal gradually increased with the increase of nitrogen content, accompanied with refined and homogeneous microstructure and improvement of hardness and wear resistance. It also reveals hardness of deposited metal reaches maximum (51.3HRC) when 3% CrN is added. Moreover, nitrogen alloying improves the resistance to temper softening of deposited metals, and at the same time the friction and wear resistance is superior to that of non-nitrogen alloying deposited metals.
靳军, 孙俊生, 孙洪根, 卢庆亮, 许京伟, 杨云. 热作模具表面氮合金化堆焊金属的组织和性能[J]. 材料导报, 2019, 33(19): 3184-3188.
JIN Jun, SUN Junsheng, SUN Honggen, LU Qingliang, XU Jingwei, YANG Yun. Microstructure and Performance of Nitrogen Alloying Deposited Metalon Hot Working Dies Surface. Materials Reports, 2019, 33(19): 3184-3188.
Zhang Q R. Hot Working Technology,2014,43(14),156(in Chinese).张庆荣.热加工工艺,2014,43(14),156.2 Yu W X, Yan Z L, Liu C X, et al. Hot Working Technology,2015,44(24),25(in Chinese).喻文新,闫忠琳,刘承鑫,等.热加工工艺,2015,44(24),25.3 Pan X H, Zhu Z C. Die & Mould Manufacture,2006(4),78(in Chinese).潘晓华,朱祖昌.模具制造,2006(4),78.4 Xia P C, Han G P, Xie K, et al. Transactions of Materials and Heat Treatment,2014,35(1),109(in Chinese).夏鹏成,韩冠朋,谢鲲,等.材料热处理学报,2014,35(1),109.5 Hang S M. Transactions of Materials and Heat Treatment,2009,30(1),161(in Chinese).黄尚猛.材料热处理学报,2009,30(1),161.6 Gualco A,Svoboda H G,Surian E, et al. Materials and Design,2010,51(9),4165.7 Borrego L P, Pires J T B, Costa J M, et al. Engineering Failure Analysis,2008,16(2),596.8 Li W B, Guan J. Hot Working Technology,2006,35(7),75(in Chinese).李文彬,官军.热加工工艺,2006,35(7),75.9 Tang F. High wear-resistant iron-based overlaying welding electrode and its organization and properties of the hardfacing layer. Master’s Thesis, Xiangtan University, China,2014(in Chinese).唐方.铁基高温耐磨堆焊焊条及其堆焊合金的组织和性能.硕士学位论文,湘潭大学,2014.10 Liu R P. In: The 9th China International Forging Conference and the 2007 National Forging Company Director Conference Paper. Beijing,2007,pp.227(in Chinese).刘仁培.第九届中国国际锻造会议暨2007年全国锻造企业厂长会议论文,北京,2007,pp.227.11 Kamachi Mudali U, Baldev R. High nitrogen steels and stainless steels-manufacturing, properties and applications, Chemical Industry Press, China,2006,pp.51(in Chinese).Kamachi Mudali U, Baldev R.高氮钢和不锈钢-生产、性能与应用,化学工业出版社,2006,pp.51.12 Yang K. Deposit and metallurgical behavior of nitrogen-alloying hardfacing alloy. Ph.D. Thesis, Huazhong University of Science and Technology, China,2009(in Chinese).杨可.氮合金化堆焊硬面合金及其冶金行为研究.博士学位论文,华中科技大学,2009.13 Chen J X. Steelmaking common chart data manual, Metallurgical Industry Press, China,1984(in Chinese).陈家祥.炼钢常用图表数据手册,冶金工业出版社,1984.14 Sun H G. Study of working die remanufacturing surfacing electrode. Master’s Thesis, Shandong University, China,2016(in Chinese).孙洪根.热作模具再制造用堆焊焊条的研究.硕士学位论文,山东大学,2016.15 Zhang D T, Shi B D. Non-metallic inclusions in steel, National Defense Industry Press, China,1980(in Chinese).张德堂,施炳弟.钢中非金属夹杂物图谱,国防工业出版社,1980.16 Gao Y. Effect of the surface nitriding treatment on the high temperature wear and thermal fatigue properties of the new high Cr hot work steel. Master’s Thesis, Jilin University, China,2011(in Chinese).高原.新型高Cr热作模具钢表面软氮化处理对热疲劳和高温磨损的影响.硕士学位论文,吉林大学,2011.