Abstract: The microstructure and mechanical properties in the inertia friction welded (IFW) dissimilar joints of K447A+GH4169 were studied. The results show that the flash of K447A+GH4169 IFW joint was mainly generated by GH4169. Fine recrystallization zone was formed near the friction interface on both sides of K447A and GH4169. Fine γ' phase which was precipitated dispersed in the weld zone (WZ) after heat processing. Most of δ phase in the weld zone of GH4169 side was dissolved and part of δ phase was dissolved in thermo-mechanical affected zone (TMAZ).After aging treatment, no δ phase precipitation was found in the zone of TMAZ and WZ. The result of elements interdiffusion zone by electron probe microanalysis (EPMA) was observed. The tensile strength of GH4169+K447A IFW joints were equal to K447A base metal,the time of high temperature endurance testing exceeded 75 h.
1 Li A L,Tang X,Cao L M,et al. Effects of HIP temperature on microstructure and mechanical properties of K447A superalloy[J].Journal of Aeronautical Materials,2012,32(2):13(in Chinese). 李爱兰,汤鑫,曹腊梅,等.热等静压温度对K447A高温合金显微组织及性能的影响[J].航空材料学报,2012,32(2):13. 2 师昌绪,陆达.中国高温合金四十年[M].北京:中国科学技术出版社,1996:145. 3 Li M Q, Yao X Y, Luo J, et al. Study of flow stress model of the nickel-based superalloy GH4169 at high temperature deformation[J].Acta Metallurgica Sinica,2007,43(9):937(in Chinese). 李淼泉,姚晓燕,罗皎,等.镍基GH4169合金高温变形流动应力模型研究[J].金属学报,2007,43(9):937. 4 Zhang C B,Zhou J,Zhao Y S,et al.Microstructure and mechanical properties of inertia friction welding joint of AMS6308 steel at diffe-rent heat treatment state[J].Transactions of the China Welding Institute,2012,36(7):21(in Chinese). 张春波,周军,赵玉珊,等.不同热处理状态AMS6308钢惯性摩擦焊接头组织及力学性能[J].焊接学报,2012,36(7):21. 5 Wang F F,Li W Y,Chen L,et al.Numerical study on influence of axial pressure on inertia friction welding[J].Transactions of the China Welding Institute,2012,33(2):41(in Chinese). 王非凡,李文亚,陈亮,等.轴向压力对惯性摩擦焊的影响数值分析[J].焊接学报,2012,33(2):41. 6 Li W Y,Wang F F.Modeling of continuous drive friction welding of mild steel[J].Materials Science and Enginnering A,2011,528(18):5921. 7 Gao M. Preferential coarsening of γ" precipitates in Inconel 718 du-ring creep[J].Metallurgy and Material Transaction,1996,27(11):391. 8 Sandararaman M. Some aspects of the precipitation of metastable intermetallic phases in Inconel 718[J]. Metallurgy Transaction A,1992,23(7):2015. 9 Ji S D,Liu J G,Zhang L G,et al. Effect of material flow on flash formation during continuous driven friction welding[J].Transactions of the China Welding Institute,2013,34(4):31(in Chinese). 姬书得,刘建光,张利国,等.材料流动对连续驱动摩擦焊飞边形成的影响[J].焊接学报,2013,34(4):31.