Study on the Fracture Properties of Fe-based Soft Magnetic Composites
XIAO Ling1, LEI Zhongqi1, CHENG Wenjie1, LI Ming1, FAN Hongwei1, LIU Gang1, SUN Yanhua2, YU Lie2
1 Department of Basic Courses, Xi’an University of Science and Technology, Xi’an 710054; 2 State Key Laboratory for Strength and Vibration of Mechanical Structures, Xi’an Jiaotong University, Xi’an 710049
Abstract: The soft magnetic composites (SMCs) with higher flexural strength were prepared successfully by two-step heat treatment method and the relationship between the microstructure and flexural strength was investigated. The strength achieves the better value 45.3 MPa for the increase of the binding bonds between passivated iron powders and organosilicon epoxy resin (OER) with excellent dielectric properties. Energy dispersion spectrum (EDS) and finite element method (FEM) results showed that the pores and cracks produced during the SMCs preparation process were mainly distributed in the resin layer and resin-Fe interface. Under the external load, the stress distribution of the pore edge was affected by the crack, and made them expand toward the same fai-lure direction, resulting in a negative effect on the strength of SMCs. Our work suggests that the improve of the SMCs′ strength depends on the integrity of the coating resin, the further enhancement of resin/iron adhesive strength and resin layer′s strength, as well as the use of hot pressing to reduce pores.
肖玲, 雷忠琦, 程文杰, 李明, 樊红卫, 刘刚, 孙岩桦, 虞烈. Fe基软磁复合材料的断裂性能研究*[J]. 《材料导报》期刊社, 2017, 31(12): 145-148.
XIAO Ling, LEI Zhongqi, CHENG Wenjie, LI Ming, FAN Hongwei, LIU Gang, SUN Yanhua, YU Lie. Study on the Fracture Properties of Fe-based Soft Magnetic Composites. Materials Reports, 2017, 31(12): 145-148.
1 Xiao L, Sun Y H, Ding C H, et al. Influence of the component size ratio on densification and magnetic property of soft magnetic compo-sites [J]. Int J Appl Electromag Mechan,2012,39(1-4):548. 2 Xiao L, Sun Y H, Ding C H, et al. Annealing effects on magnetic properties and strength of organic-silicon epoxy resin-coated soft magnetic composites[J]. Proceedings of the Institution of Mechanical Engineers,2014,228(12):2050. 3 Shokrollahi H, Janghorban K. Effect of warm compaction on the magnetic and electrical properties of Fe-based soft magnetic compo-sites[J]. J Magn Magn Mater,2007,313(1):182. 4 Hamler A, Gorican V, Sustarsic B,et al. The use of soft magnetic composite materials in synchronous electric motor [J]. J Magn Magn Mater,2006,304(2):816. 5 Hultman L O, Jack A G. Soft magnetic composites materials and applications [C]// Proceedings of the IEEE International Electric Machines and Drives Conference.2003. 6 Taghvaei A, Shokrollahi H, Ebrahimi A, et al. Soft magnetic composites of iron-phenolic and the influence of silane coupling agent on the magnetic properties[J].Mater Chem Phys,2009,116(1):247. 7 Koohkan R, Sharafi S, Shokrollahi H, et al. Preparation of nanocrystalline Fe-Ni powders by mechanical alloying used in soft magnetic composites[J].J Magn Magn Mater,2008,320(6):1089. 8 Shokrollahi H, Janghorban K, Mazaleyrat F, et al. Investigation of magnetic properties, residual stress and densification in compacted iron powder specimens coated with polyepoxy [J]. Mater Chem Phys,2009,114(2):588. 9 Cui Y, Kliman G. Modeling of soft magnetic composites[C]//39th IAS Annual Meeting,IEEE,2004. 10 Ding D H, Li Y W, Hao H Q,et al. Grey equation between bending strength and porosity of copper-graphic composite[J]. Chin J Nonferrous Metals,1996,6(4):123(in Chinese). 丁华东, 李雅文, 浩宏奇,等.铜石墨材料抗弯强度与孔隙的关系[J].中国有色金属学报,1996,6(4):123. 11 Xiao L, Li M, Cheng W J, et al. Influence of annealing methods on the magnetic properties and flexural strength of Iron-OER soft magnetic composites[J]. Adv Mater Sci Eng:DOI:10.1155/2016/5378276.
渝公网安备50019002502923号 版权所有：《材料导报》编辑部
2017, Vol. 31 