材料导报  2019, Vol. 33 Issue (z1): 440-443    
  金属与金属基复合材料 |
应用于核岛主设备的RCC-M F5100与AMS 2460镀铬标准的比较
王方, 蒋恩, 米大为
上海第一机床厂有限公司,上海 201308
Comparison of Chromium Plating Standards for RCC-M F5100 and AMS 2460 Applied to Nuclear Island Main Equipment
WANG Fang, JIANG En, MI Dawei
Shanghai No.1 Machine Tool Works Co. Ltd.,Shanghai 201308
下载:  全 文 ( PDF ) ( 1295KB ) 
输出:  BibTeX | EndNote (RIS)      
摘要 核岛主设备的部分零件处在高温、高压的工况下,为了保证该类零件的使用寿命,在需要耐磨的表面及防咬的表面镀硬铬。该类零件镀硬铬的引用文件通常为法国RCC-M F5100标准或美国AMS 2460标准,二者对于镀铬及其检测方面的规定存在较大区别。本文通过比较二者在镀铬及检测方面的差异,对核岛主设备镀铬标准的制定提供一定的参考。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
王方
蒋恩
米大为
关键词:  核岛主设备  镀铬  标准  比较    
Abstract: Some parts of nuclear island main equipment are under high temperature and high pressure. In order to ensure the service life of these parts, hard chromium shall be plated on the wear-resistant surface and bite-proof surface. The reference documents for hard chromium plating on such parts are RCC-M F5100 or AMS 2460. There are some differences between the two standards for chromium plating and coating examination. By comparing the differences of chromium plating and coating testing between the two standards, this paper provides a reference for the establishment of chromium plating standard for nuclear island main equipment.
Key words:  nuclear island main equipment    chromium plating    standard    comparison
               出版日期:  2019-05-25      发布日期:  2019-07-05
ZTFLH:  TB304  
作者简介:  王方,上海第一机床厂有限公司专业副总工程师,从事核电产品表面处理工作。2008年毕业于上海交通大学,获得材料学博士学位。wangfang5 @shanghai-electric.com
引用本文:    
王方, 蒋恩, 米大为. 应用于核岛主设备的RCC-M F5100与AMS 2460镀铬标准的比较[J]. 材料导报, 2019, 33(z1): 440-443.
WANG Fang, JIANG En, MI Dawei. Comparison of Chromium Plating Standards for RCC-M F5100 and AMS 2460 Applied to Nuclear Island Main Equipment. Materials Reports, 2019, 33(z1): 440-443.
链接本文:  
http://www.mater-rep.com/CN/  或          http://www.mater-rep.com/CN/Y2019/V33/Iz1/440
1 Lindsay J H. Plating and Surface Finishing,1999,86(11),40.
2 柳木桐, 刘建华, 钟平. 科技导报,2010,28(9),112.
3 王家贵. 机械工程师,2013(5),229.
4 任雪峰, 杨培霞, 刘安敏, 等. 化学通报,2013,76(1),39.
5 王方, 夏荣芳, 龚宏伟. 第二届核电站材料与可靠性国际研讨会, 沈阳,2011.
6 张新国. 冷热工艺,2013(5),19.
7 AMS 2460, Plating chromium, SAE,2007.
8 RCC-M F5100, Chromium Plating, AFCEN,2007.
9 孙化松, 屠振密, 李永彦, 等. 材料保护,2010,43(1),25.
10 屠振密, 郑剑、李宁, 等. 表面技术,2007,36(5),59.
11 王宗雄, 王超. 专家论坛,2014(2),5.
12 王文忠. 电镀与环保,2015,35(6),50.
13 何生龙.电镀与环保,1992,12(2),1.
14 刘俊莲, 陈华三, 江冰. 电镀与涂饰,2013,32(7),14.
15 赵黎云, 钟丽萍, 黄逢春. 电镀与精饰, 2001, 23(5), 9.
16 谢洪波, 张来祥, 马学奎. 材料保护,2006,39(9),31.
17 李寒松, 王栋梁, 朱增伟, 等. 电加工与模具,2015(2),61.
18 AMS 2759/9, Hydrogen embrittlement relief (Baking) of steel parts, SAE,2003.
19 ASTM E 384, Test method for microhardness of materials, ASTM International,2011.
20 ASTM B 571, Qualitative adhesion of metallic coatings, ASTM International,2003.
21 ASTM F 519, Mechanical hydrogen embrittlement testing of plating processes and service environments, ASTM International,2003.
[1] 方瑞杰,刘军,陈建恩,王肖锋. 多耦合拘束效应对P92钢蠕变裂纹扩展行为的影响*[J]. 材料导报编辑部, 2017, 31(22): 153-158.
[2] 高文, 张津, 黄进峰, 连勇, 张乐, 马旻昱, 赵超, 张尊君, 刘凯. 身管内膛镀铬层-钢基体界面损伤退化行为研究进展*[J]. 《材料导报》期刊社, 2017, 31(13): 90-98.
[1] Bingwei LUO,Dabo LIU,Fei LUO,Ye TIAN,Dongsheng CHEN,Haitao ZHOU. Research on the Two Typical Infrared Detection Materials Serving at Low Temperatures: a Review[J]. Materials Reports, 2018, 32(3): 398 -404 .
[2] Huimin PAN,Jun FU,Qingxin ZHAO. Sulfate Attack Resistance of Concrete Subjected to Disturbance in Hardening Stage[J]. Materials Reports, 2018, 32(2): 282 -287 .
[3] Siyuan ZHOU,Jianfeng JIN,Lu WANG,Jingyi CAO,Peijun YANG. Multiscale Simulation of Geometric Effect on Onset Plasticity of Nano-scale Asperities[J]. Materials Reports, 2018, 32(2): 316 -321 .
[4] Xu LI,Ziru WANG,Li YANG,Zhendong ZHANG,Youting ZHANG,Yifan DU. Synthesis and Performance of Magnetic Oil Absorption Material with Rice Chaff Support[J]. Materials Reports, 2018, 32(2): 219 -222 .
[5] Ninghui LIANG,Peng YANG,Xinrong LIU,Yang ZHONG,Zheqi GUO. A Study on Dynamic Compressive Mechanical Properties of Multi-size Polypropylene Fiber Concrete Under High Strain Rate[J]. Materials Reports, 2018, 32(2): 288 -294 .
[6] XU Zhichao, FENG Zhongxue, SHI Qingnan, YANG Yingxiang, WANG Xiaoqi, QI Huarong. Microstructure of the LPSO Phase in Mg98.5Zn0.5Y1 Alloy Prepared by Directional Solidification and Its Effect on Electromagnetic Shielding Performance[J]. Materials Reports, 2018, 32(6): 865 -869 .
[7] ZHOU Rui, LI Lulu, XIE Dong, ZHANG Jianguo, WU Mengli. A Determining Method of Constitutive Parameters for Metal Powder Compaction Based on Modified Drucker-Prager Cap Model[J]. Materials Reports, 2018, 32(6): 1020 -1025 .
[8] WANG Tong, BAO Yan. Advances on Functional Polyacrylate/Inorganic Nanocomposite Latex for Leather Finishing[J]. Materials Reports, 2017, 31(1): 64 -71 .
[9] HUANG Dajian, MA Zonghong, MA Chenyang, WANG Xinwei. Preparation and Properties of Gelatin/Chitosan Composite Films Enhanced by Chitin Nanofiber[J]. Materials Reports, 2017, 31(8): 21 -24 .
[10] YUAN Xinjian, LI Ci, WANG Haodong, LIANG Xuebo, ZENG Dingding, XIE Chaojie. Effects of Micro-alloying of Chromium and Vanadium on Microstructure and Mechanical Properties of High Carbon Steel[J]. Materials Reports, 2017, 31(8): 76 -81 .
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed