浸泡腐蚀对泡沫铝-环氧树脂复合材料弯曲性能的影响*

doi:10.11896/j.issn.1005-023X.2017.022.022

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (630KB)
Export: BibTeX | EndNote (RIS)

Abstract Foam aluminum-epoxy composites with two types of foam aluminum pore size were prepared. The specimens were soaked in the distilled water and seawater respectively. The curves between moisture rate and soaking time were obtained. The effect on the flexural properties of specimens in soak corrosion were studied by three point bending experiment. It was found that the moisture rate of composites increased with the increase of soaking time, and the moisture rates of composites soaking in seawater were higher than that of composites soaking in distilled water. The flexural mechanical properties of foam aluminum-epoxy were greatly reduced by soaking corrosion. The flexural strength and stiffness of specimens with coupling agent were higher than that of specimens without coupling agent. Especially for the composites with foam aluminum pore size of 2 mm, the flexural strength and stiffness increased by 51.7% and 65.4%, respectively. Additionally, the flexural strength and stiffness of specimens with foam aluminum pore size of 1 mm are higher than that of specimens with foam aluminum pore size of 2 mm.

Key words： foam aluminum epoxy resin soaking corrosion flexural mechanical properties

Published: 08 May 2018

CLC number:

TB333

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	YU Wei
	XUE Hailong

Cite this article:

YU Wei,XUE Hailong. Effect of Soaking Corrosion on Flexural Properties of Foam Aluminum-Epoxy Composites[J]. Materials Reports, 2017, 31(22): 111-115.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.022.022 OR http://www.mater-rep.com/EN/Y2017/V31/I22/111

1 Banhart J. Manufacture characterization and application of cellular metals and metal foams[J]. Prog Mater Sci, 2001,46:559.
2 Zhao W X, Zhao N Q, Guo X Q. Study progress for new type functional materials of foam aluminum[J]. Heat Treatment Metals, 2004,29(6):7(in Chinese).
赵万祥, 赵乃勤, 郭新权. 新型功能材料泡沫铝的研究进展[J]. 金属热处理, 2004,29(6):7.
3 Mu J C, Xi H F, Long Z Q. Study on the mechanics and energy absorb property of aluminum foam in different void rate and different aperture[J]. Experiment Mechan, 2009,24(3):223(in Chinese).
穆建春, 习会峰, 龙志勤. 不同孔隙率及孔径泡沫铝的力学与吸能特性研究[J]. 实验力学, 2009,24(3):223.
4 Tilbrook M T, Moon R J, Hoffman M. On the mechanical properties of alumina-epoxy composites with an interpenetrating network structure[J]. Mater Sci Eng A, 2005,393:170.
5 Yu Y H, Liang B. Calculation of effective elastic modulus of foamed aluminum/epoxy resin composite based on IPC material[J]. Mater Mechan Eng, 2008,32(11):90(in Chinese).
于英华, 梁冰. 基于网络交织复合材料预测泡沫铝/环氧树脂复合材料的有效弹性模量[J]. 机械工程材料, 2008,32(11):90.
6 Xie Y L, Wang R, Lin Z R, et al. Compressive mechanical properties of foam aluminum/modified epoxy composite[J]. Ordnance Mater Sci Eng, 2010, 33(5):49(in Chinese).
谢永亮, 王瑞, 林振荣, 等. 泡沫铝/改性环氧树脂复合材料压缩力学性能的试验研究[J]. 兵器材料科学与工程, 2010,33(5):49.
7 Yu W, Li H J, Zhao Z, et al. Compressive mechanical properties of foam aluminum-epoxy interpenetrating phase composites[J]. Acta Materiae Compositae Sinica, 2012,29(4):377(in Chinese).
余为, 李慧剑, 赵钊, 等. 泡沫铝/环氧树脂互穿相复合材料压缩力学性能[J]. 复合材料学报, 2012,29(4):377.
8 Yu W, Yang L, Liu X J, et al. Studies on elastic constants of foam aluminum/epoxy composites with two pore shapes[J]. J Yanshan University, 2013,37(3):278(in Chinese).
余为, 杨柳, 刘学瑾, 等. 两种孔隙形状泡沫铝/环氧树脂复合材料弹性常数研究[J]. 燕山大学学报, 2013,37(3):278.
9 Xu P, Yang K, Yu Y H. Research on damping property of foam aluminum-epoxy resin composite[J]. Hot Working Technology, 2013,42(16):110(in Chinese).
徐平, 杨昆, 于英华. 泡沫铝-环氧树脂复合材料阻尼性能的研究[J]. 热加工工艺, 2013,42(16):110.
10 Liu Y, Gong X L. Compressive behavior and energy absorption of metal porous polymer composite with interpenetrating network structure[J]. Trans Nonferrous Metals Soc China, 2006,16:439.
11 Qi M S, Zhang J N, Yang W, et al. Research on shock cushioning performance of foamed aluminium polyurethane composite structure[J]. Packag Eng, 2010,31(19):6(in Chinese).
齐明思, 张晋宁, 杨卫, 等. 泡沫铝-聚氨酯复合结构的缓冲性能研究[J]. 包装工程, 2010,31(19):6.
12 Xie W H, Du H T, Li S C. Experimental study on dynamic mechanical performance of polyurethane aluminum foams composites [J]. Acta Materiae Compositae Sinica, 2011,28(3):103(in Chinese).
谢卫红, 杜红涛, 李顺才. 聚氨酯泡沫铝复合材料动态力学实验[J]. 复合材料学报, 2011,28(3):103.
13 Wang R, Lin Z R, Lu Y S, et al. Dynamic compression experimental study and energy absorption of aluminum foam composite materials[J]. Ordnance Mater Sci Engi, 2010,33(6):40(in Chinese).
王瑞, 林振荣, 卢玉松, 等. 泡沫铝复合材料的动态压缩试验研究和吸能分析[J]. 兵器材料科学与工程, 2010,33(6):40.
14 Dukhan N, Rayess N, Hadley J. Characterization of aluminum foam-polypropylene interpenetrating phase composites: Flexural test results[J]. Mechan Mater, 2010,42(2):134.
15 Zhang Y, Chen L, Chen R J, et al. Dynamic mechanical property experiment and constitutive model establishment of polyurethane foam aluminum[J]. Explosion Shock Waves, 2014,34(3):373(in Chinese).
张勇, 陈力, 陈荣俊, 等. 聚氨酯泡沫铝动力学性能实验及本构模型研究[J]. 爆炸与冲击, 2014,34(3):373.
16 Periasamy C, Tippur H V. Experimental measurements and numerical modeling of dynamic compression response of an interpenetrating phase composite foam[J]. Mechan Res Commun, 2012,43:57.
17 Li H J, Liu Z L, Yu W, et al. Electromagnetic shielding and mechanical properties of foam aluminum/epoxy composite[J]. Mater Rev:Res, 2015,29(4):150(in Chinese).
李慧剑, 刘泽良, 余为, 等. 泡沫铝/环氧树脂复合材料电磁屏蔽及力学性能实验[J]. 材料导报:研究篇, 2015,29(4):150.
18 Qi M, Sun L, Wang X, et al. High on shock-cushioning and energy-absorption-performance analysis on aluminum foam-polyurethane composite[J]. Metall Mining Industry, 2015,7(3):303.
19 Liu S, Li A, He S, et al. Cyclic compression behavior and energy dissipation of aluminum foam-polyurethane interpenetrating phase composites[J]. Compos Part A, 2015,78:35.
20 Ray B C. Temperature effect during humid ageing on interfaces of glass and carbon fibers reinforced epoxy composites[J]. J Colloid Interface Sci, 2006,298(1):111.
21 Zhang H, Yang J H, Li H B, et al. Effects of hydrothermal aging on properties of epoxy resin[J]. Ordnance Mater Sci Eng, 2010,33(3):41(in Chinese).
张晖,阳建红,李海斌,等. 湿热老化环境对环氧树脂性能影响研究[J]. 兵器材料科学与工程, 2010,33(3):41.
22 Yu W, Li H J, Liang X, et al. Mechanical properties of HGM/epoxy and foam aluminum-HGM/epoxy with natural aging[J]. Acta Materiae Compositae Sinica, 2013,30(4):66(in Chinese).
余为,李慧剑,梁希,等. 自然老化对空心玻璃微珠/环氧树脂及泡沫铝-空心玻璃微珠/环氧树脂力学性能的影响[J]. 复合材料学报, 2013,30(4):66.
23 Doyle G, Pethrick R A. Environmental effects on the ageing of epoxy adhesive joints[J]. Int J Adhes Adhes, 2009,29(1):77.
24 Gao Y L, Zhou E P, Yun H L, et al. Aging behavior of epoxy/Al adhesive joint in sodium chloride aqueous solution[J]. Therm Osetting Resin, 2011,26(3):18(in Chinese).
高岩磊, 周二鹏, 郧海丽, 等. 环氧/铝胶接接头在氯化钠水溶液中的老化行为[J]. 热固性树脂, 2011,26(3):18.
25 Xu Z R, Gao Y L. Molecular simulation of moisture aging to epoxy resin/uranium[J]. Synthet Mater Aging Application, 2014,43(4):9(in Chinese).
徐作瑞, 高云亮. 环氧树脂/铝界面湿气老化性能的分子模拟[J]. 合成材料老化与应用, 2014,43(4):9.