冷拉减面率对C形环用Inconel X-750丝材组织性能的影响*

doi:10.11896/j.issn.1005-023X.2017.022.020

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (993KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to study the effect of cold drawn area reduction ratio on microstructure and properties of Inconel X-750 alloy, especially the effect on the shape, distribution, quantity and size of γ' phase, the X-750 wires which had 0%, 30%, 60% cross section reduction rate (CSRR) were prepared and subsequently aging-treated at 650 ℃, 730 ℃, 810 ℃, respectively. With the quantitative analysis, aging temperature had little effect on grain size but great effect on the quantity, size and shape of γ' phase. Nevertheless, CSRR had significant influence on the grain size of X-750 wires, and it played a major role in fine grain strengthening. The quantity and volume fraction of γ' precipitate could be improved to some extent, and the size could be diminished by increasing CSRR, which resulted in enhancing further precipitation strengthening effect.The X-750 wires were aging-treated at 730 ℃ for 16 hours by standard process, then after being processed into springs, they were made into some C-rings finally. Under the given experimental conditions,it was proved that both the rebound amount and leakage rate met the requirements and the sealing performance was favorable.

Key words： superalloy,Inconel X-750 alloy,cold drawn area reduction ratio,C-type sealing ring,γ' precipitate

Published: 08 May 2018

CLC number:	TB34
	TG356.4
	O657.99

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HE Qinsheng
	ZOU Xingzheng
	LI Fang
	LI Zheng
	TANG Rui
	ZHAO Anzhong

Cite this article:

HE Qinsheng,ZOU Xingzheng,LI Fang, et al. Effect of Cold Drawn Area Reduction on Microstructure and Properties of Inconel X-750 Wire Used for C Ring[J]. Materials Reports, 2017, 31(22): 100-106.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.022.020 OR http://www.mater-rep.com/EN/Y2017/V31/I22/100

1 Heckl A, Neumeier S, Cenanovic S, et al. Reasons for the enhanced phase stability of Ru-containing nickel-based superalloys[J]. Acta Mater, 2011,59(17):6568.
2 Wang J, Zhou L, Sheng L, et al. The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure[J]. Mater Des, 2012,39(39):59.
3 Sims C T, Ha W C. The superalloys[M]. NY: John Wiley & Sons, 1972.
4 Yao D Z, Zeng Y P, Du H J, et al. Effect of thermal exposure on microstructure and mechanical properties of GH4145 alloy[J]. Trans Mater Heat Treat, 2015,36(11):37(in Chinese).
姚大志, 曾燕屏, 杜毫杰,等. 高温时效对GH4145合金显微组织与力学性能的影响[J]. 材料热处理学报, 2015,36(11):37.
5 Liu J, Cao J, Lin X, et al. Microstructure and mechanical properties of diffusion bonded single crystal to polycrystalline Ni-based superalloys joint[J]. Mater Des, 2013,49:622.
6 Zuo G, Hao S X, Yin X L. Research of “C”-ring for advanced pressurized water reacter[J]. Nucl Power Eng, 2002,23(2):108(in Chinese).
左国, 郝守信, 尹小龙. 先进压水堆“C”形环研究[J]. 核动力工程, 2002,23(2):108.
7 刘纯一,郑俊铭,黄伟峰. 对我国核电标准体系总体设计的几点看法[J]. 核标准计量与质量,2010(2):2.
8 Liao C J, Wang D L, Wang H R, et al. Features and applications of typical non-conventional type metal seals[J]. Cryogenics, 2014(4):56(in Chinese).
廖传军, 王道连, 王洪锐,等. 典型异型金属密封的特点及应用[J]. 低温工程, 2014(4):56.
9 Ma K, Cai R L,Lu X G, et al. Study on deformational characteristics of the C-ring for reaction pressure vessels[J]. Press Vessel Technol, 2016,33(1):17(in Chinese).
马凯, 蔡仁良, 励行根,等. 反应堆压力容器用 C 形密封环的变形特性研究[J]. 压力容器, 2016,33(1):17.
10 Jia X H, Chen H M, Li X G, et al. Analysis on the mechanical and sealing properties of metallic C ring[J]. Lubric Eng, 2014,39(11):4(in Chinese).
贾晓红, 陈华明, 励行根,等. 金属C形环力学性能及密封特性分析[J]. 润滑与密封, 2014,39(11): 4.
11 Souza G R X D, Gabriel S B, Dille J, et al. Work hardening and aging contribution on the mechanical properties of X-750 nickel-based superalloy[J]. Mater Sci Eng A, 2013,564(3):104.
12 Valle J A D, Picasso A C, Romero R. Work-hardening in Inconel X-750: Study of stageⅡ[J]. Acta Mater, 1998,46(6):1986.
13 Lothongkum G, Khuanlieng W, Homkrajai W, et al. Effect of pre-heat treatments on nano γ' precipitation and mechanical properties in wrought nickel base superalloy X-750[J]. Acta Mater, 2006,12:10.
14 Valle J A D, Picasso A C, Alvarez I, et al. Age-hardening behavior of Inconel X-750 superalloy[J]. Scr Mater, 1999,41(3):241.
15 Wang J J, Guo H, Zhou Y Z, et al. Effects of trace elements on properties of modified Inconel X-750 alloys[J]. Heat Treat Met, 1997(9):5(in Chinese).
王家军, 郭晖, 周亦胄, 等. 微量元素对InconelX-750改型合金性能的影响[J]. 金属热处理, 1997(9):5.
16 Ducki K J, Hetmańczyk M, Kuc D. Analysis of the precipitation process of the intermetallic phases in a high-temperature Fe-Ni austenitic alloy[J]. Mater Chem Phys, 2003,81(2):490.
17 Zhao S Q, Xie X S. Properties and microstructure after long-term aging at different temperatures for a new nickel base super alloy[J]. Acta Metall Sin, 2003,39(4):402(in Chinese).
赵双群, 谢锡善. 一种新型镍基高温合金长期时效后的组织和性能[J]. 金属学报, 2003, 39(4):402.
18 Yang Y Q, Luo X, Huang B. Microstructure of Inconel X-750 superalloy[J]. Trans Mater Heat Treat, 2007,28(8):3(in Chinese).
杨延清,罗贤,黄斌. InconelX-750高温合金的组织变化[J]. 材料热处理学报, 2007,28(8):3.
19 Gao X L, Xia T D, Wang X J, et al. Present research status for metals refinement methods[J]. Met Funct Mater, 2009,16(6):62(in Chinese).
高晓龙, 夏天东, 王晓军,等. 金属晶粒细化方法的研究现状[J]. 金属功能材料, 2009,16(6):62.
20 Wang J J, Guo H, Zhou Y Z, et al. Influence of cold-working on microstructure and properties of a modified Inconel X-750 alloy[J]. Spec Steel, 1997(5):15(in Chinese).
王家军, 郭晖, 周亦胄,等. 冷变形对InconelX-750改型合金组织性能的影响[J]. 特殊钢, 1997(5):15.
21 Nembach E, Pesicka J, Mohles V, et al. The effects of a second aging treatment on the yield strength of γ'-hardened NIMONIC PE16-polycrystals having γ'-precipitate free zones[J]. Acta Mater, 2005,53(8):2487.
22 余永宁, 刘国权. 体视学:组织定量分析的原理和应用[M]. 北京: 冶金工业出版社, 1989.