RESEARCH PAPER |
|
|
|
|
|
Effect of Mg Content and Si on Fe-Al Reaction Layer in Solid-Liquid Diffusion Couples of Fe/Zn-Al-Mg Alloys |
MA Kun1,2, LIU Ya1,2, TU Hao1,2, SU Xuping1,2, WANG Jianhua1,2
|
1 Jiangsu Key Laboratory of Materials Surface Science and Technology, Changzhou University, Changzhou 213164;
2 Jiangsu Collaborative Innovation Center of Photovolatic Science and Engineering, Changzhou University, Changzhou 213164 |
|
|
Abstract In hot dip galvanization, the formation of Fe-Al compound layer on steel surface affects the growth and quality of coatings. Fe/(Zn-11%Al-3%Mg) and Fe/(Zn-11%Al-x%Mg-0.2%Si) solid-liquid diffusion couples were annealed at 600 ℃ for 25 min. Scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS) were adopted to study the effect of Mg content and Si on the formation of Fe-Al reaction layer. The results showed that the reaction layer in Fe/(Zn-11%Al-3%Mg) solid-liquid diffusion couple was composed of FeAl3 and Fe2Al5 phase. With the increase of Mg content, the thickness of the reaction layer in Fe/(Zn-11%Al-x%Mg-0.2%Si) diffusion couple increased firstly, then decreased and increased finally. The thickness of reaction layer was the thinnest when magnesium content was 3%. The average thickness of Fe-Al reaction layer in Fe/(Zn-11%Al-3%Mg) diffusion couple was obviously larger than that in Fe/(Zn-11%Al-3%Mg-0.2%Si) diffusion couple, which proved that Si played a role in inhibiting the formation of Fe-Al reaction layer. The results could be used for explaining the reason that there was no obvious Fe-Al inhibition layer forming in the coating of Super Dyma alloy.
|
Published: 25 March 2017
Online: 2018-05-02
|
|
|
|
1 Morimoto Y,Honda K,Nishimura K, et al. Excellent corrosion-resistant Zn-Al-Mg-Si alloy hot-dip galvanized steel sheet “super Dyma”[J]. Nippon Steel Technical Rep,2003,87(87):22. 2 Yu Kangcai, Li Jun, Liu Xin, et al. Microstructure of hot-dip galvanized Zn-Al-Mg alloy coating[J].J Shanghai Jiaotong University,2012,17(6):663. 3 Honda K, Ushioda K, Yamada W. Influence of si addition to the coating bath on the growth of the Al-Fe alloy layer in hot-dip Zn-Al-Mg alloy-coated steel sheets[J]. ISIJ Int,2011,51(11):1895. 4 De Bruycker E. Zn-Al-Mg alloy coatings: Thermodynamic analysis and microstructure-related properties[D]. Ghent: Ghent University,2005. 5 Li Q, Zhao Y Z, Luo Q, et al. Experimental study and phase diagram calculation in Al-Zn-Mg-Si quaternary system[J]. J Alloys Compd,2010,501(2):282. 6 Yin F C, Zhao M X, Liu Y X, et al. Effect of Si on growth kinetics of intermetallic compounds during reaction between solid iron and molten aluminum[J]. Trans Nonferrous Met Soc China,2013,23(2):556. 7 Tong Chen, Su Xuping, Li Zhi, et al. Research on hot-dipped Zn-6%Al-3%Mg alloy coatings intermetallics layer growth [J]. J Mater Eng,2013,7(1):54(in Chinese). 童晨,苏旭平,李智,等. 热浸镀Zn-6%Al-3%Mg镀层合金层生长研究[J]. 材料工程,2013,7(1):54. 8 Qian Weijiang, Gu Wengui. Inhibitory action of Si on growth of interfacial compound layer during hot-dip aluminizing[J].Acta Metall Sin,1994,30(9):403(in Chinese). 钱卫江,顾文桂. Si对热浸镀Al界面化合物层生长的限制作用[J].金属学报,1994,30(9):403. 9 Han Wei. Influence of Si on the growth kinetic of Fe2Al5 during reaction diffusion between Fe and Al [D]. Xiangtan: Xiangtan University,2009(in Chinese). 韩炜. Si对Fe-Al反应过程中Fe2Al5相生长动力学的影响[D]. 湘潭:湘潭大学,2009. 10 Jiang S M, Yue C F, Zhang Q F. Coating structure and corrosion resistance behavior of hot dip Zn-Al-Mg-Si alloy coating steel sheet[J]. Adv Mater Res,2014,2817(834):601. 11 Ueda K, Takahash A, Kubo Y. Investigation of corrosion resistance of pre-painted Zn-11%Al-3%Mg-0.2%Si alloy coated steel sheet through outdoor exposure test in Okinawa[J]. Metall Italiana,2012,104(3):13. 12 Ueda Kohei. Corrosion resistance of Zn-11%Al-3%Mg-0.2%Si alloy coated steel sheet in the marine atmospheric after long term outdoor exposure[C]//Galvatech’13, 9th International Conference on Zinc and Zinc Alloy Coated Steel Sheet. Beijing: Metallurgical Industry Press,2013:659. 13 Li Feng, Lv Jiashun, Yang Hongang, et al. The Experiment research of microstructure of hot-dip galvanized Zn11Al3Mg0.2Si alloy coating [J]. Surf Technol,2011(3):39(in Chinese). 李锋,吕家舜,杨洪刚,等. 热浸镀Zn11Al3Mg0.2Si合金镀层微观组织实验研究[J].表面技术,2011(3):39. 14 Lin Yuan, Yuan Xunhua, Yue Chongfeng, et al. Microstructure and corrosion resistance of hot dip Zn-Al-Mg coating [J]. Heat Treat Met,2014(4):39(in Chinese). 林源,袁训华,岳崇锋,等. 热镀锌铝镁镀层的组织和耐蚀性能[J]. 金属热处理,2014(4):39. 15 Hei Zhirong, Liu Jituo, Xie Yadan, et al. Effect of Al and Si on microstructure and corrosion resistance of hot dipping Zn-Al-Mg alloy coatings [J]. Chin J Nonferrous Met,2015,25(5):1250(in Chinese). 贺志荣,刘继拓,解亚丹,等. Al和Si对热浸Zn-Al-Mg合金镀层组织和耐腐蚀性的影响[J]. 中国有色金属学报,2015,25(5):1250. 16 任颂赞,等.钢铁金相图谱[M]. 上海:上海科学技术出版社,2003. 17 Wu G, Zhang J, Li Q, et al. Microstructure and thickness of 55 pct Al-Zn-1.6 pct Si-0.2 pct RE hot-dip coatings: Experiment, thermodynamic, and first-principles study[J]. Metall Mater Trans B,2012,43(1):198. 18 Phelan D, Xu B J, Dippenaar R. Formation of intermetallic phases on 55wt.%Al-Zn-Si hot dip strip[J]. Mater Sci Eng A,2006,420(1):144. 19 Liu Liantao. Study on the texture and structure of the composite interface of Fe-Al [D]. Kunming: Kunming University of Science and Technology,2008(in Chinese). 刘连涛. 钢-铝复合界面组织结构研究[D].昆明: 昆明理工大学,2008. 20 Pei Jiangbang, Wu Guangxin, Zhang Jieyu, et al. Microstructure and growth kinetics of high strength low-alloy steel with hot-dipping of 55%Al-Zn-1.6%Si (≤0.1%Ti)[J]. Chin J Process Eng,2013,13(1):139(in Chinese). 裴金榜,吴广新,张捷宇,等. 低合金高强钢热浸镀55%Al-Zn-1.6%Si(≤0.1%Ti)合金层的组织及生长动力学[J]. 过程工程学报,2013,13(1):139. 21 García F, Salinas-Rodríguez A, Nava-Vázquez E. The role of Ti ino-culation of Al-Zn-Si coating alloys on the formation of intermetallic compounds by interaction with solid steel[J]. Mater Sci Forum,2007,75(560):97. 22 Honda K, Sugiyama M, Ikematsu Y, et al. Role of TiAl3 fine precipitate in nucleation of the primary Al dendrite phase during solidification in hot-dip Zn-11%Al-3%Mg-0.2%Si coated steel sheet[J]. Mater Trans,2011,52(1):90.
|
|
|
|