再生混凝土微粉在碱激发胶材体系中的作用效应研究

doi:10.11896/cldb.22020043

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (20022KB)
Export: BibTeX | EndNote (RIS)

Abstract The recycled concrete powder (RCP) contains a large amount of SiO₂, CaO, Al₂O₃ and a small amount of unhydrated cement, which can be used as supplementary cementing materials (SCMs) through physical or chemical excitation. The resource utilization of recycled concrete powder is of great significance to save raw materials and dispose of waste. In this work, alkali-activated cementitious materials with different RCP substitution rates were prepared, and their fluidity, mechanical properties, microscopic characterization and hydration process were studied. The results show that the addition of RCP improves the fluidity of alkali-activated cementitious materials, and the fluidity of alkali-activated cementitious materials increase by 2%—12% at 10%—40% substitution rate. When RCP content is 10%, the compressive strength of alkali slag cementitious material increase by 13%. Inactive particles in RCP fill the pores and form dense microstructure. Since the inactive particles in RCP hinder the reaction between alkali solution and slag, the introduction of RCP delays the emergence of the second exothermic peak and decreases the early exothermic rate of alkali-activated cementitious materials.

Key words： alkali-activated recycled fine powder fluidity mechanical property hydration heat

Published: 10 October 2023 Online: 2023-09-28

CLC number:

TU528

Fund:National Natural Science Foundation of China (51878365).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WAN Xiaomei
	CHE Xueping
	ZHU Yaguang
	YU Qi
	JIANG Lulu

Cite this article:

WAN Xiaomei,CHE Xueping,ZHU Yaguang, et al. Investigation on the Effect of Recycled Concrete Powder in Alkali-activated Cementitous Materials[J]. Materials Reports, 2023, 37(19): 22020043-7.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22020043 OR http://www.mater-rep.com/EN/Y2023/V37/I19/22020043

1 Yazdani M, Kabirifar K, Frimpong B E, et al. Journal of Cleaner Production, 2021, 280, 124138.
2 Yue G B, Ma Z M, Liu M, et al. Construction and Building Materials, 2020, 245, 118419.
3 Wu H Y, Zuo J, Zillante G, et al. Journal of Cleaner Production, 2019, 240, 118163.
4 Zheng L, Wu H Y, Zhang H, et al. Construction and Building Materials, 2017, 136, 405.
5 Zhang C B, Hu M H, Di Maio F, et al. Science of the Total Environment, 2022, 803, 149892.
6 Nedeljković M, Visser J, Šavija B, et al. Journal of Building Enginee-ring, 2021, 38, 102196.
7 Guo H, Shi C J, Guan X M, et al. Cement and Concrete Composites, 2018, 89, 251.
8 Tam V W Y, Wattage H, Le K N, et al. Construction and Building Materials, 2021, 270, 121490.
9 Li S J, Gao J M, Li Q Y, et al. Construction and Building Materials, 2021, 267, 120976.
10 Oliveira T C F, Dezen B G S, Possan E. Journal of Cleaner Production, 2020, 273, 123126.
11 Tang Q, Ma Z M, Wu H X, et al. Cement and Concrete Composites, 2020, 114, 103807.
12 He Z M, Shen A Q, Wu H S, et al. Construction and Building Materials, 2021, 274, 122113.
13 Robayo-Salazar R A, Mejía-Arcila J M, de Gutiérrez R M. Journal of Cleaner Production, 2017, 166, 242.
14 Villaquirán-Caicedo M A, de Gutiérrez R M. Construction and Building Materials, 2021, 281, 122599.
15 Ulugöl H, Kul A, Yıldırım G, et al. Journal of Cleaner Production, 2021, 280, 124358.
16 Robayo-Salazar R A, Rivera J F, de Gutiérrez R M. Construction and Building Materials, 2017, 149, 130.
17 Sun Z Q, Cui H, An H, et al. Construction and Building Materials, 2013, 49, 281.
18 Lin W S. Effect of the recycled powder on cement hydration and concrete performance. Master's Thesis, Fuzhou University, China, 2018 (in Chinese).
林尾妹. 再生粉体对水泥水化及混凝土性能的影响. 硕士学位论文, 福州大学, 2018.
19 Liu C. Research on preparation and application of alkali activated recycled concrete powder cementitious material. Master's Thesis, Yangzhou University, China, 2021 (in Chinese).
刘聪. 碱激发再生微粉胶凝材料制备及其应用研究. 硕士学位论文, 扬州大学, 2021.
20 Dai J X, Shi X S, Wang Q Y, et al. Materials Reports, 2021, 35(9), 9077 (in Chinese).
代金芯, 石宵爽, 王清远, 等. 材料导报, 2021, 35(9), 9077.
21 Yang D, Pang L X, Song D, et al. Bulletin of the Chinese Ceramic Society, 2021, 40(9), 3005 (in Chinese).
杨达, 庞来学, 宋迪, 等. 硅酸盐通报, 2021, 40(9), 3005.
22 Zawrah M F, Gado R A, Feltin N, et al. Process Safety and Environmental Protection, 2016, 103, 237.
23 Reig L, Tashima M M, Borrachero M V, et al. Construction and Building Materials, 2013, 43, 98.
24 Yip C K, Van Deventer J S J. Journal of Materials Science, 2003, 38(18), 3851.
25 Bassani M, Tefa L, Coppola B, et al. Journal of Cleaner Production, 2019, 234, 71.
26 Tan L F, Qu B, Shi C J, et al. Materials Reports, 2020, 34(12), 12057(in Chinese).
覃丽芳, 曲波, 史才军, 等. 材料导报, 2020, 34(12), 12057.
27 Xu X F, Tang S W, He Z. Bulletin of the Chinese Ceramic Society, 2021, 40(12), 3903(in Chinese).
徐晓飞, 汤盛文, 何真. 硅酸盐通报, 2021, 40(12), 3903.
28 Chen G F, Gao J M, Zhao Y S. Journal of Southeast University (Natural Science Edition), 2020, 50(5), 858 (in Chinese).
陈高丰, 高建明, 赵亚松. 东南大学学报(自然科学版), 2020, 50(5), 858.
29 Zhao S. Study on hydration character of alkali-activated slag cement. Master's Thesis, Chongqing University, China, 2012 (in Chinese).
赵爽. 碱矿渣水泥水化特性研究. 硕士学位论文, 重庆大学, 2012.