| Wear Performance of SiCp/A356 Aluminum Metal Matrix Composites |
| YE Yun, HE Guoqiu, DAI Liquan, LU Qi, LIU Xiaoshan, LU Shiquan
|
| Shanghai Key Laboratory for R&D and Application of Metallic Functional Materials, School of Materials Science and Engineering, Tongji University, Shanghai 201804; |
|
|
|
|
Abstract Under the condition of dry friction, the friction coefficient and wear rate of the aluminum metal matrix composites with 20 vol% silicon carbide particle were measured over a load range of 2-20 MPa at sliding velocities of 200 r/min and 400 r/min. In addition, the wear performance is studied and the mechanism diagram of friction and wear at different loads and sliding friction speed is established through microstructure analysis by SEM and elemental analysis by EDS. The results show that when loads and friction speed were relatively low, the main wear mechanism was slight particle wear, accompanied by oxidation wear. When load reached 10 MPa, the process turned from slight wear to severe wear, and delamination wear appeared gradually. At last, severe adhesive wear occured on the surface of the material with the load of 20 MPa and sliding speed of 400 r/min.
|
|
Published: 02 May 2018
|
|
|
|
|
1 Zhang Datong, Li Yuanyuan, Long Yan. A review on the progress of aluminum matrix composites[J]. Light Alloy Fabrication Tech-nol,2000,28(1):5(in Chinese).
张大童,李元元,龙燕.铝基复合材料研究进展[J]. 轻合金加工技术,2000,28(1):5.
2 Kaczmar J W, Pietrzak K, Wlosinski W. The production and application of metal matrix composite materials[J]. J Mater Processing Technol,2000,106:58.
3 Davis J R. Aluminum and aluminum alloys[M]. New York:ASM International,1993:18.
4 Sahin Y. Preparation and some properties of SiC particle reinforced aluminium alloy composites[J]. Mater Des,2003,24(8):671.
5 Goni J, Mitxelena I, Coleto J. Development of low cost metal matrix composites for commercial applications[J]. Mater Sci Technol,2000,16(7-8):743.
6 Zeuner T, et al. Developing trends in disc bralke technology for rail application[J]. Mater Sci Technol,1998,14(9-10):857.
7 Vencl A, Rac A, Bobic I. Tribological behaviour of Al-based MMCs and their application in automotive industry[J]. Tribol Ind,2004,26(3-4):31.
8 Kamat S V, Hirth J P, Mehrabian R. Mechanical properties of particulate-reinforced aluminum-matrix composites[J].Acta Metall,1989,37(9):2395.
9 Prasad S V, Asthana R. Aluminum metal-matrix composites for automotive applications: Tribological considerations[J]. Tribol Lett,2004,17(3):445.
10 Daoud A, El-khair M T A. Wear and friction behavior of sand cast brake rotor made of A359-20vol% SiC particle composites sliding against automobile friction material[J]. Tribol Int,2010,43(3):544.
11 Cao L, Wang Y, Yao C K. The wear properties of an SiC-whisker-reinforced aluminium composite[J]. Wear,1990,140(2):273.
12 Bhushan B. Introduction to tribology[M]. New York:John Wiley & Sons,2013.
13 Chung S, Hwang B H. A microstructural study of the wear beha-viour of SiCp/Al composites[J]. Tribology Int,1994,27(5):307.
14 Ge Xiaolan, Xu Xiaojing, et al. Effect of grain size and content of SiCp on tribology characterization of SiCp/Al composites[J]. Trans Nonferrous Metals Soc China,2005,15(3):458(in Chinese).
戈晓岚,许晓静,等.SiCp含量和尺寸对Al基复合材料摩擦学特性的影响[J].中国有色金属学报,2005,15(3):458.
15 Lu Qi, He Guoqiu, Yang Yang, et al. The friction and wear properties of silicon carbide particle reinforced aluminum matrix composite[J]. Metal Funct Mater,2015,22(2):41(in Chinese).
卢棋,何国球,杨洋,等.SiC颗粒增强铝基复合材料的摩擦磨损性能研究[J].金属功能材料,2015,22(2):41.
16 Umanath K, Palanikumar K, Selvamani S T. Analysis of dry sliding wear behaviour of Al6061/SiC/Al2O3 hybrid metal matrix compo-sites[J]. Composites Part B: Eng,2013,53(1):159.
17 Alidokht S A, Abdollah-Zadeh A, Assadi H. Effect of applied load on the dry sliding wear behaviour and the subsurface deformation on hybrid metal matrix composite[J]. Wear,2013,305(1):291.
|
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2017, Vol. 31 