高速列车用铝合金型材激光-MIG复合焊工艺特性和接头性能

doi:10.11896/cldb.21110142

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (7783KB)
Export: BibTeX | EndNote (RIS)

Abstract Laser-hybrid welding is an ideal technique to realize high-quality, high-efficiency and low-cost welding manufacturing of aluminium alloy body for high-speed train. Laser-MIG hybrid welding procedure tests were carried out on 6A01-T5 aluminium alloy profiles with thickness of 3 mm, which used for high-speed train body. The influence rules of welding parameters on weld formation and porosity defects were studied. The microstructures characteristic, microhardness distribution, tensile and fracture properties were also investigated. The results indicated that adopted lower laser power, lower arc current or lower welding speed was beneficial to reduce porosity defects when the weld penetration met the requirements. From fusion zone center to base material, the microstructures consisted of equiaxed zone, columnar zone, partially melted zone, over-aged zone and the base material. Compared with the arc active zone, the equiaxed grain was smaller and the width of the partially melted zone was narrower. The joints were softened, the lowest microhardness value was appeared in the weld zone, and the width of the heat affected zone was about 1.5 mm. The average tensile strength of the joints reached to 197.5 MPa, which was 80.6% of the base metal, the fractures occurred in the weld seam and the fracture morphology showed obvious ductile fracture features. The fracture strength of the joints was 93.5 MPa, the fracture crack initiated in the weld surface, and the fracture morphology of the crack propagation zone showed typical mixed fracture features with ductile fracture and brittle fracture.

Key words： laser-MIG hybrid welding 6A01-T5 aluminium ally weld formation porosity defect microstructure characteristic mechanical property

Published: 25 June 2023 Online: 2023-06-20

CLC number:

TG456.7

Fund:Scientific Research Funding Projects of Education Department of Liaoning Province (JDL2020026), and the China Postdoctoral Science Foundation (2019M650053).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	MA Guolong
	ZHANG Zhiyi
	MAO Zhendong
	LI Gangqing
	HAN Xiaohui
	YANG Zhibin

Cite this article:

MA Guolong,ZHANG Zhiyi,MAO Zhendong, et al. Processing Characteristics and Joints Properties of Laser-MIG Hybrid Welding for Aluminium Alloy of High-speed Trains[J]. Materials Reports, 2023, 37(12): 21110142-6.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21110142 OR http://www.mater-rep.com/EN/Y2023/V37/I12/21110142

1 Wang D, Zhang C, Wang C, et al. International Journal of Advanced Manufacturing Technology, 2018, 94(9-12), 4247.
2 Tuo W H, Yang S L, Yang W T, et al. Materials Reports, 2015, 29(20), 105 (in Chinese).
庹文海, 杨尚磊, 杨文涛, 等. 材料导报, 2015, 29(20), 105.
3 Malopheyev S, Vysotskiy I, Kulitskiy V, et al. Materials Science and Engineering A, 2016, 662, 136.
4 Gou G Q, Zhang M, Chen H, et al. Materials and Design, 2015, 85, 309.
5 Ascari A, Fortunato A, Orazi L, et al. Optics and Laser Technology, 2012, 44(5), 1484.
6 Chen H, Gou G Q, Zhu Z T, et al. Electric Welding Machine, 2015, 45(5), 11 (in Chinese).
陈辉, 苟国庆, 朱宗涛, 等. 电焊机, 2015, 45(5), 11.
7 Liu C N, Hu W H. Metal Processing (Cold Machining), 2016(S1), 555 (in Chinese).
刘春宁, 胡文浩. 金属加工(冷加工), 2016(S1), 555.
8 Olsen F O. Hybrid laser-arc welding, Woodhead Publishing, UK, 2009, pp. 216.
9 Wang W, Wang H, Chen H, et al. Transactions of the China Welding Institution, 2019, 40(7), 55 (in Chinese).
王伟, 王浩, 陈辉, 等. 焊接学报, 2019, 40(7), 55.
10 Li X Y, Wang X P, Lei Z, et al. Transactions of the China Welding Institution, 2015, 36(6), 96 (in Chinese).
李小宇, 王小朋, 雷振, 等. 焊接学报, 2015, 36(6), 96.
11 Zhang D F, Yang Y, Wang T J, et al. Materials Reports, 2015, 29(6), 121 (in Chinese).
张德芬, 杨阳, 王同举, 等. 材料导报, 2015, 29(6), 121.
12 Zhang D F, Zhu Y, Zhang H T, et al. Materials Reports, 2016, 30(Z1), 474 (in Chinese).
张德芬, 朱亚, 张宏涛, 等. 材料导报, 2016, 30(Z1), 474.
13 Liu T, Zhao Y Q, Zhou X D, et al. Chinese Journal of Lasers, 2020, 47(11), 1102004 (in Chinese).
刘婷, 赵艳秋, 周旭东, 等. 中国激光, 2020, 47(11), 1102004.
14 Zhang C, Gao M, Wang D Z, et al. Journal of Materials Processing Technology, 2017, 240, 217.
15 Han X H, Yang Z B, Ma Y, et al. Optics and Laser Technology, 2020, 132, 106511.
16 Tian Z Q, Ma G L, Shi Y Y, et al. Electric Welding Machine, 2016, 46(9), 24 (in Chinese).
田志骞, 马国龙, 石业勇, 等. 电焊机, 2016, 46(9), 24.
17 Tao W, Yang Z B, Shi C Y, et al. Journal of Alloys and Compounds, 2017, 699, 638.
18 Chang B, Allen C, Blackbum J, et al. Physics Procedia, 2013, 41, 478.
19 Han X H, Yang Z B, Ma Y, et al. Metals, 2020, 10, 407.
20 Acherjee B. Optics and Laser Technology, 2018, 99, 60.