表面镀Ni碳纤维增强Cu基复合材料的制备和表征

doi:10.11896/j.issn.1005-023X.2018.14.025

Abstract
Figure/Table
References
Related Citation (4)

Download:

Full Text ( PDF ) (2510KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to enhance the interface bonding strength between carbon fiber and the Cu-based composites, uniformly nickel coating with controlled thickness of 1 μm was electroplated on the short carbon fibers. Afterwards, the Cu coating with a thickness of about 6 μm is prepared. Based on that, the Nickel coated carbon fiber reinforced copper matrix composites was prepared by spark plasma sintering with Ni-Cu coated carbon fibers under 20 MPa at 800 ℃ for 5 min. Meanwhile, the carbon fiber reinforced copper with the same volume fraction of Cf was prepared under the same sintering conditions. The morphology and the phase composition of the Ni coating were characterized by SEM and XRD respectively. Furthermore, the surface and fracture morphology and the interface of Cf and Cu were researched through SEM equipped with EDS. The tensile mechanical properties of nickel-coated carbon fibers and copper-coated carbon fibers were preliminarily studied by the electronic tensile testing machine. Results show that the tensile strength of the nickel-coated carbon fibers were higher than that of the uncoated fibers,while the elongation was slightly reduced compared with the uncoated fibers. No delamination of Ni coating occurs during the tensile process, which can be attributed to the stronger bonding strength between Cf and Ni coating. The Ni-coated carbon fibers reinforced Cu-based composites (Cf/Cu(Ni)) show higher plastic deformation fracture and the mechanical properties of Cf/Cu(Ni) than that of Cf/Cu composites. The tensile strength of Cf/Cu(Ni) was about 20% higher than that of the Cf/Cu composites.

Key words： carbon fibers Cu-based composites Ni-Cu duplex coating tensile property

Published: 31 July 2018

CLC number:

TB333

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	JIA Jiangang
	GAO Changqi
	LIU Diqiang
	JI Genshun
	XUE Xiangjun
	GUO Tieming
	HAO Xiangzhong

Cite this article:

JIA Jiangang,GAO Changqi,LIU Diqiang, et al. Preparation and Characterization of Ni-coated Carbon Fiber Reinforced Cu-based Composites[J]. Materials Reports, 2018, 32(14): 2462-2466.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.14.025 OR http://www.mater-rep.com/EN/Y2018/V32/I14/2462

1 Bradley A Newcomb. Processing, structure, and properties of carbon fibers[J]. Composites Part A: Applied Science and Manufactu-ring,2016,91:262.
2 朱和国,张爱文.复合材料原理[M].北京:国防工业出版社,2013:22.
3 Su Q Q, Li W W, Liu L, et al. Application and progress in development of the carbon fibre reinforced copper matrix composite[J]. Materials Review A:Review Papers,2010,24(3):76(in Chinese).
苏青青,李薇薇,刘磊,等.碳纤维增强铜基复合材料的最新研究进展和应用[J].材料导报:综述篇,2010,24(3):76.
4 Gao Q, Wu Y Y, Zhang G D, et al. Effect of carbon fiber on pro-perty of copper-graphite composite materials[J]. The Chinese Journal of Nonferrous Metals,2000,10(s1):97(in Chinese).
高强,吴渝英,张国定,等.碳纤维对铜-石墨复合材料性能的影响[J].中国有色金属学报,2000,10(s1):97.
5 Shirvanimoghaddam K, Hamim S U, Akbari M K, et al. Carbon fiber reinforced metal matrix composites: Fabrication processes and properties[J]. Composites Part A: Applied Science and Manufactu-ring,2017,92:70.
6 Ouyang W J, Jia J G, Ma Q, et al. Preparation and characterization of Cf/Cu composite based on copper-plating process of short carbon fibres[J]. Acta Materiae Compositae Sinica,2016,33(12):2824(in Chinese).
欧阳雯婧,贾建刚,马勤,等.基于短切碳纤维表面均匀包覆铜层工艺的Cf/Cu复合材料的制备与表征[J].复合材料学报,2016,33(12):2824.
7 Zhu Z, Kuang X, Carotenuto G, et al. fabrication and properties of carbon fibre-reinforced copper composite by controlled three-step electrodeposition[J]. Journal of Materials Science,1997,32(4):1061.
8 Liu L, Tang Y P, Zhao H J. Fabrication and properties of short carbon fibers reinforced copper matrix composites[J]. Journal of Materials Science,2008,43(3):974.
9 Wan Y Z, Wang Y L, Luo H L, et al. Effects of fiber volume fraction, hot pressing parameters and alloying elements on tensile strength of carbon fiber reinforced copper matrix composite prepared by continuous three-step elec-trodeposition[J]. Materials Science and Engineering A,2000,288(1):26.
10 Lee S B, Matsunaga K, Ikuhara Y, et al. Effect of alloying elements on the interfacial bonding strength and electric conductivity of carbon nano-fiber reinforced Cu matrix composites[J]. Materials Science and Engineering A,2007,449-451(13):778.
11 Inoue Y, Kim J H, Yonezawa S, et al. Enhanced mechanical strength of nickel-copper-coated carbon FIBER/Magnesium alloy composites fabricated using powder metallurgy[J]. Chemistry Letters,2012,41(5):531.
12 Sorcoi L A, Constantinescu V R, Buharu M V, et al. Mechanical and technological properties of sintered Cu-Ni compacts[J]. Advanced Materials Research,2007,23:75.
13 Han B H, Luo T J, Yao G C, et al. Nickel plating on carbon fiber[J]. Non-ferrous Ming and Metallurgy,2006,22(2):37(in Chinese).
韩变华,罗天骄,姚广春,等.碳纤维镀镍[J].有色矿冶,2006,22(2):37.
14 Cheng T, Jia J G, Ma Q, et al. Deposition of homogeneous copper layer on short carbon fibers using electro-chemical method[J]. Transactions of Materials and Heat Treatment,2014,35(9):167(in Chinese).
程韬,贾建刚,马勤,等.短碳纤维表面电沉积均匀镀铜工艺研究[J].材料热处理学报,2014,35(9):167.
15 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.碳纤维-单丝拉伸性能的测定:GB/T31290-2014[S].北京:中国标准出版社,2014.
16 Yang Y F,Zhang X J, Tian Y H. Test methods for tensile properties of carbon fibers multfilament and mono-filament[J]. Physical Testing and Chemical Analysis (Part A: Physical Testing),2013,49(7):441(in Chinese).
杨延风,张学军,田艳红.碳纤维复丝和单丝拉伸性能测试方法[J].理化检验-物理分册,2013,49(7):441.
17 Hua Z S, Yao G C, Ma J, et al. XPS analysis of nickel layers on carbon fibers[J]. The Chinese Journal of Non-ferrous Metals,2011,21(1):165(in Chinese).
华中胜,姚广春,马佳,等.碳纤维表面镍镀层的XPS分析[J].中国有色金属学报,2011,21(1):165.
18 Hua Z S, Liu Y H, Yao G C, et al. Preparation and characterization of nickel-coated carbon fibers by electroplating[J].Journal of Mate-rials Engineering and Performance,2012,21(3):324.
19 Wan Y Z, Wang Y L, Luo H L, et al. Relationship between elastic behavior and interfacial bonding strength for carbon fiber reinforced copper composites[J]. Journal of Mate-rials Science Letters,2000,19(3):183.