脉冲电子束作用下热障涂层微观结构及热循环性能

doi:10.11896/j.issn.1005-023X.2018.13.010

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2343KB)
Export: BibTeX | EndNote (RIS)

Abstract High-current pulsed electron beam (HCPEB) treatment was conducted on thermal barrier coatings (TBCs) prepared by air plasma sprayed (APS) technology. The effects of HCPEB irradiation on the microstructure and thermal cycling behavior of TBCs were investigated. The thermal cycling test was carried out by using a muffle furnace, and each cycle consisted of holding at 950 ℃ in air and cooling by water quenching. The microstructure and phase composition of the coatings before and after HCPEB irradiation were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD).The XRD results revealed that the content of monoclinic (m) phase in the yttria stabilized zirconia (YSZ) topcoat was reduced after HCPEB irradiation. Besides, the width of peaks became wider and peak locations slightly shifted, which indicated the grain refinement and residual stress generation. The remelting of the coating surface, the elimination of thermal sprayed defects, the reduced surface roughness, as well as a conti-nuous micro-crack network perpendicular to the surface and columnar grains in the remelted layer, could be observed by SEM for the HCPEB irradiated YSZ topcoat. Thermal cycling test results confirmed the failure of the initial YSZ coating after 250 cycles, as the overall spalling occurred. Contrastively, no obvious signs of spallation appeared for the irradiated coating, and only the propagation of horizontal cracks can be observed. Our experiment validated the higher thermal cycling resistance of the HCPEB-TBCs.

Key words： YSZ topcoat high-current pulsed electron beam (HCPEB) microstructure thermal cycling behavior

Published: 01 August 2018

CLC number:

TB321

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WU Jian
	GUAN Qingfeng
	CAI Jie
	LYU Peng
	ZHANG Conglin
	LI Chen

Cite this article:

WU Jian,GUAN Qingfeng,CAI Jie, et al. Microstructure and Thermal Cycling Behavior of the Surface-modified Thermal Barrier Coatings by High-current Pulsed Electron Beam[J]. Materials Reports, 2018, 32(13): 2202-2207.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.13.010 OR http://www.mater-rep.com/EN/Y2018/V32/I13/2202

1 Peters M, Fritscher K, Staniek G, et al. Design and properties of thermal barrier coatings for advanced turbine engines[J].Materialwissenschaft Und Werkstofftechnik,1997,28(8):357.
2 Wang Q W, Mao W G, Yu M. Analysis of heat-insulating perfor-mance of air plasma sprayed thermal barrier coating systems[J].Materials Review B:Research Papers,2011,25(9):125(in Chinese).
王千文,毛卫国,喻明.等离子喷涂热障涂层隔热性能分析方法[J].材料导报:研究篇,2011,25(9):125.
3 Padture N P, Gell M, Jordan E H. Thermal barrier coatings for gas-turbine engine applications[J].Science,2002,296(5566):280.
4 Stecura S. New ZrO₂-Y₂O₃plasma-sprayed coatings for thermal barrier applications[J].Thin Solid Films,1987,150(1):15.
5 Cai J, Guan Q F, Yang S Z, et al. Microstructural characterization of modified YSZ thermal barrier coatings by high-current pulsed electron beam[J].Surface & Coatings Technology,2014,254(18):187.
6 Gong W B, Sha C K, Sun D Q, et al. Microstructures and thermal insulation capability of plasma-sprayed nanostructured ceria stabilized zirconia coatings[J].Surface & Coatings Technology,2006,201(6):3109.
7 Drexler J M, Shinoda K, Ortiz A L, et al. Air-plasma-sprayed thermal ba-rrier coatings that are resistant to high-temperature attack by glassy deposits[J].Acta Materialia,2010,58(20):6835.
8 Rabiei A, Evans A G. Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings[J].Acta Materialia,2000,48(15):3963.
9 Liu D X, Chen R H. Current status and development direction of aircraft power technology in the world[J].Journal of Beijing University of Aeronautics and Astronautics,2002,28(5):490(in Chinese).
刘大响,程荣辉.世界航空动力技术的现状及发展动向[J].北京航空航天大学学报,2002,28(5):490.
10 Ghasemi R, Shoja-Razavi R, Mozafarinia R, et al. The influence of laser treatment on thermal shock resistance of plasma-sprayed nanostructured yttria stabilized zirconia thermal barrier coatings[J].Ceramics International,2014,34(8):347.
11 Ahmadi-Pidani R, Shoja-Razavi R, Mozafarinia R, et al. Improving the thermal shock resistance of plasma sprayed CYSZ thermal bar-rier coatings by laser surface modification[J].Optics and Lasers in Engineering,2012,50(5):780.
12 Batista C, Portinha A, Ribeiro R M, et al. Morphological and microstructural characterization of laser-glazed plasma-sprayed thermal barrier coatings[J].Surface & Coatings Technology,2006,200(9):2929.
13 Grosdidier T, Zou J X, Bolle B, et al. Grain refinement, hardening and metastable phase formation by high current pulsed electron beam (HCPEB) treatment under heating and melting modes[J].Journal of Alloys and Compounds,2010,504(8):S508.
14 Cai J, Lv P, Guan Q F, et al. Thermal cycling behavior of thermal barrier coatings with MCrAlY bond coat irradiated by high-current pulsed electron beam[J].ACS Applied Materials & Interfaces,2016,8(47):32541.
15 Moon J, Choi H, Kim Y, et al. Cooling rate effect on phase transformation of plasma sprayed partially stabilized zirconia[J].Journal of Materials Science Letters,2001,20(17): 1611.
16 Zhu C, Li P, Javed A, et al. An investigation on the microstructure and oxidation behavior of laser remelted air plasma sprayed thermal barrier coatings[J].Surface & Coatings Technology,2012,206(18):3739.
17 Kim B K, Hahn J W, Han K R. Quantitative phase analysis in tetragonal-rich tetragonal/monoclinic two phase zirconia by raman spectroscopy[J].Journal of Materials Science Letters,1997,16(8):669.
18 Lima R S, Kucuk A, Berndt C C. Integrity of nanostructured partially stabilized zirconia after plasma spray processing[J].Materials Science and Engineering A,2001,313(1-2):75.
19 Cai J, Ji L, Yang S Z, et al. Deformation mechanism and microstructures on polycrystalline aluminum induced by high-current pulsed electron beam[J].Chinese Science Bulletin,2013,58(20):2507.
20 Wang C X. Surface modification of coating irradiation by high current plulsed electrom beam[D].Dalian:Dalian University of Technology,2011(in Chinese).
王存霞.强流脉冲电子束辐照陶瓷涂层表面改性[D].大连:大连理工大学,2011.
21 Cai J, Ji L, Yang S Z, et al. Surface microstructure and stress cha-racteristics inpure zirconium after high current pulsed electron beam irradiation[J].Acta Physica Sinica,2013,62(15):328(in Chinese).
蔡杰,季乐,杨盛志,等.强流脉冲电子束作用下金属锆的微观结构与应力状态[J].物理学报,2013,62(15):328.
22 Mou R D, Lu F, He L M, et al. Application and development of thermal barrier coating technology in aeroengine[J].Thermal Spray Technology,2009,1(1):53(in Chinese).
牟仁德,陆峰,何利民,等.热障涂层技术在航空发动机上的应用与发展[J].热喷涂技术,2009,1(1):53.
23 Zhang H S, Geng G Q, Du K K, et al. Application of thermal spraying and electron beam physical vapor deposition in preparation of thermal barrier coatings[J].Materials Review A:Review Papers,2009,23(7):98(in Chinese).
张红松,耿国强,杜可可,等.热喷涂及电子束物理气相沉积技术在热障涂层制备中的应用[J].材料导报:综述篇,2009,23(7):98.