6013-T4铝合金不同温度下的动态流变应力及组织演变

doi:10.11896/j.issn.1005-023X.2017.010.018

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (1375KB)
Export: BibTeX | EndNote (RIS)

Abstract The dynamic compression tests of 6013-T4 aluminum alloy were conducted at the temperatures of 25 ℃, 100 ℃, 200 ℃, 300 ℃ and 400 ℃, at the strain rates of 1 000 s-1, 2 000 s-1, 3 000 s-1, 4 000 s-1 and 5 000 s-1 by split Hopkinson pressure bar (SHPB), the true stress-true strain curves were obtained. The microstructure evolution of dynamic compression test specimens under different test conditions was observed by means of transmission electron microscopy (TEM). Results show that the flow stress of 6013 aluminum alloy has weak sensitivity to the strain rate but strong sensitivity to temperature. The effect of strain rate and temperature on microstructure of 6013 aluminum alloy is remarkable, the dislocation density increased with the increase of strain rate and decreased with the increase of temperature. Based on the experimental data, the constitutive parameters of the Johnson-Cook model of 6013 aluminum alloy were obtained and the constitutive model was built. The constitutive model can well predict the flow stress of 6013 aluminum alloy compared with the experimental results.

Key words： aluminum alloy dynamic compression microstructure evolution constitutive model

Published: 08 May 2018

CLC number:

TG146.2

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	TANG Xu
	LI Luoxing
	YE Tuo
	LI Rongqi

Cite this article:

TANG Xu,LI Luoxing,YE Tuo, et al. Dynamic Flow Stress and Microstructure Evolution of 6013-T4 Aluminum Alloy at Different Temperatures[J]. Materials Reports, 2017, 31(10): 87-91.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.010.018 OR http://www.mater-rep.com/EN/Y2017/V31/I10/87

1 Ma H, Huang L, Tian Y, et al. Effects of strain rate on dynamic mechanical behavior and microstructure evolution of 5A02-O aluminum alloy[J]. Mater Sci Eng A,2014,606:233.
2 Liu W J, Zhong L P. Status of heat treatment process for 6××× series aluminum alloys[J]. Mater Rev,2012,26(S1):137(in Chinese).
刘文静, 钟利萍. 6×××铝合金热处理工艺的研究概况[J]. 材料导报,2012,26(专辑19):137.
3 Xue X G, Zhang S Q. Study on properties of 6013 aluminium alloy extruded shapes[J]. Aluminium Fabrication,2003,26(2):46(in Chinese).
薛学功, 章四琪. 6013 铝合金挤压型材性能的研究[J]. 铝加工,2003,26(2):46.
4 Liu Z D, Wang G, Feng Y C, et al. High-strain-rate constitutive parameters of 6061 aluminum alloys[J]. Mining Metall Eng,2011,31(6):120(in Chinese).
刘再德, 王冠, 冯银成, 等. 6061铝合金高应变速率本构参数研究[J]. 矿冶工程,2011,31(6):120.
5 Peng Y, Wang G, Zhu T, et al. Dynamic mechanical behaviors of 6082-T6 aluminum alloy[J]. Adv Mech Eng,2013(12):878016.
6 Bedir F. Modeling approach and plastic deformation analysis of 6063 aluminum alloy during compression at elevated temperatures[J]. Mater Des,2013,49:953.
7 Zhou G P, Chang Z L, Chen S, et al. Mechanical property and microstructure of Mg-Li alloys under high strain rate impact load[J]. Rare Metal Mater Eng,2012,41(3):514(in Chinese).
邹广平, 唱忠良, 陈思, 等. 冲击载荷作用下 Mg-Li 合金的力学性能及显微组织[J]. 稀有金属材料与工程,2012,41(3):514.
8 Zhu Yao. Experimental research on mechanical properties of AA 7055 aluminum alloys at different temperatures and strain rates[D]. Harbin: Harbin Institute of Technology,2010(in Chinese).
朱耀. AA7055 铝合金在不同温度及应变率下力学性能的实验研究[D]. 哈尔滨:哈尔滨工业大学,2010.
9 Gao Z G, Zhang X M, Chen M A, et al. Effect of temperature on dynamic yield stress and microstructure of 2519A aluminum alloy at high strain rate[J]. Rare Metal Mater Eng,2009,38(5):881(in Chinese).
高志国, 张新明, 陈明安, 等. 温度对 2519A 铝合金高应变速率下动态屈服应力及显微组织的影响[J]. 稀有金属材料与工程,2009,38(5):881.
10 Weng Shuchu. Study on the dynamic microstructural evolution of the 7150 aluminum alloy during hot deformation[D]. Changsha: Hunan University,2012(in Chinese).
翁舒楚. 7150 铝合金热变形过程中动态组织演变规律研究[D]. 长沙:湖南大学,2012.
11 Liu M, Jiang T, Jun W, et al. Aging behavior and mechanical pro-perties of 6013 aluminum alloy processed by severe plastic deformation[J]. Trans Nonferrous Metals Soc China,2014,24(12):3858.
12 Lee W S, Chen T H, Lin C F, et al. Impact deformation behaviour and dislocation substructure of Al-Sc alloy[J]. J Alloys Compd,2010,493(1):580.
13 Lee W S, Chen T H. Rate-dependent deformation and dislocation substructure of Al-Sc alloy[J]. Scr Mater,2006,54(8):1463.
14 Liu A Q, Huang X C. Identification of high-strain-rate material parameters in dynamic Johnson-Cook constitutive model[J]. Appl Mathematics Mechanics,2014,35(2):219(in Chinese).
柳爱群, 黄西成. 高应变率变形的 Johnson-Cook 动态本构模型参数识别方法[J]. 应用数学和力学,2014,35(2):219.
15 Wu Y F, Li S H, Hou B, et al. Dynamic flow stress characteristics and constitutive model of aluminum 7075-T651[J]. Chinese J Nonferrous Metals,2013(3):658(in Chinese).
武永甫, 李淑慧, 侯波, 等. 铝合金 7075-T651 动态流变应力特征及本构模型[J]. 中国有色金属学报,2013(3):658.