SiO<sub>2</sub>纳米颗粒在润滑领域中的研究与应用现状

doi:10.11896/cldb.23080225

Abstract
Figure/Table
References
Related Citation (2)

Download:

Full Text ( PDF ) (25327KB)
Export: BibTeX | EndNote (RIS)

Abstract In recent years, the maintenance or replacement of materials caused by friction loss has brought huge economic losses. In order to reduce the loss of materials as much as possible, the design and development of materials with self-lubricating function has become a research hotspot. Because of its small size and high surface activity, nanoparticles have exhibited excellent tribological properties, and have received extensive attention in tribology field. Among them, SiO₂ nanoparticles have excellent tribological properties due to their high hardness and sphericity. The application of SiO₂ nanoparticles in the field of self-lubrication can be divided into liquid lubrication and solid lubrication. The liquid field refers to that when SiO₂ nanoparticles are added to the liquid lubricant as an additive, the lubrication effect of the lubricant can be significantly enhanced. The solid field refers to the fact that the wear resistance of raw materials can be significantly enhanced when SiO₂ nanoparticles are compounded with other particles to make solid self-lubricating composites and further applied to paint/coating designs. Currently, most researchers mainly elaborate on one of the above two types of application fields, which makes readers lack a comprehensive understanding and thinking about the practical application of SiO₂ nanoparticles. Therefore, this review mainly introduces the lubrication mechanism and influencing factors of SiO₂ nanoparticles, and discusses the relevant research and application status of SiO₂ nanoparticles in the field of liquid lubrication and solid lubrication in detail, including the relevant surface treatment and modification means adopted in practical application. The role and great potential of SiO₂ nanoparticles in improving polymer matrix self-lubricating materials in solid self-lubricating composites were introduced. Finally, the application and development of SiO₂ nanoparticles in the field of self-lubrication are described and prospected.

Key words： SiO₂ nanoparticles liquid lubrication solid lubrication

Published: 10 March 2024 Online: 2024-03-18

CLC number:

TB321

Fund:National Natural Science Foundation of China (52378217).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CHEN Jin
	LI Mohan
	RUAN Wenlin
	SUN Tao
	LIU Xiaoying

Cite this article:

CHEN Jin,LI Mohan,RUAN Wenlin, et al. Research and Application Status of SiO₂ Nanoparticles in Lubrication Field[J]. Materials Reports, 2024, 38(5): 23080225-9.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.23080225 OR http://www.mater-rep.com/EN/Y2024/V38/I5/23080225

1 Rahman I A, Padavettan V. Journal of Nanomaterials, 2012, 2012, 132424.
2 Jiang X F, Tang X N, Tang L H, et al. Ceramics International, 2019. 45(6), 7673.
3 Stober W, Finkw A, Bohn E. Journal of Colloid and Interface Science, 1968, 26, 62.
4 Rong M Z , Zhang M Q, Ruan W H. Materials Science and Technology, 2013, 22(7), 787.
5 Li X H, Zhi C, Zhang Z J, et al. Applied Surface Science, 2006, 252(22), 7856.
6 Meng Fanming, Cheng Zhitao, Gong Jiayu, et al. Journal of Tribology, 2021, 41(5), 680(in Chinese).
孟凡明, 程志涛, 巩加玉, 等. 摩擦学学报, 2021, 41(5), 680.
7 Li C, Friedrich K. Tribology International, 2010, 43(12), 2355.
8 Esfe M H, Saedodin S , Toghraie D. International Communications in Heat and Mass Transfer, 2022, 130, 105771.
9 Esfe M H, Ardeshiri E M, Toghraie D. Tribology International, 2023, 179, 108153.
10 Haghighi E B, Utomo A T, Ghanbarpour M, et al. International Communications in Heat and Mass Transfer, 2015, 68, 32.
11 Huminic G, Huminic A. International Communications in Heat and Mass Transfer, 2016, 71, 118.
12 Hamzah M H, Sidik N A C, Ken T L, et al. International Journal of Heat and Mass Transfer, 2017, 115, 630.
13 Sarkar J, Ghosh P, Adil A. Renewable and Sustainable Energy Reviews, 2015, 43, 164.
14 Barbés B, Páramo R, Blanco E, et al. Journal of Thermal Analysis and Calorimetry, 2012, 111(2), 1615.
15 Esfe M H, Saedodin S. Journal of Thermal Analysis and Calorimetry, 2014, 119(2), 1205.
16 Murshed S M S, Leong K C, Yang C. International Journal of Thermal Sciences, 2008, 47(5), 560.
17 Esfe M H , Saedodin S, Mahian O, et al. Journal of Thermal Analysis and Calorimetry, 2014, 117(2), 675.
18 Esfe M H, Saedodin S. Experimental Thermal and Fluid Science, 2014, 55, 1.
19 Esfe M H, Saedodin S, Bahiraei M, et al. Journal of Thermal Analysis and Calorimetry, 2014, 118(1), 287.
20 Meng F M. Journal of Chongqing University, 2013, 36(2), 121(in Chinese).
孟凡明. 重庆大学学报, 2013, 36(2), 121.
21 Lv T, Xu X F, Yu A B, et al. Journal of Materials Processing Technology, 2021, 290, 116964.
22 Sharif M Z, Azmia W H, Mamat R, et al. International Communications in Heat and Mass Transfer, 2018, 92, 56.
23 张育新, 马小飞, 孙庆, 等. 中国专利, CN109054930B, 2021.
24 张育新, 姜德彬, 马小飞, 等. 中国专利, CN108977253B, 2021.
25 Tang Z L, Li S H. Current Opinion in Solid State and Materials Science, 2014, 18(3), 119.
26 Flores-Castañeda M, Camps E, Camacho-López M, et al. Journal of Alloys and Compounds, 2015, 643, 67.
27 Wu Y Y, Tsui W C, Liu T C. Wear, 2007, 262(7-8), 819.
28 Li X L, Ling Y L, Zhang G L, et al. Composites Part B: Engineering, 2020, 196, 108133.
29 Liu G, Li X, Qin B, et al. Tribology Letters, 2004, 17, 961.
30 Sia S Y, Bassyony E Z, Sarhan A A D. The International Journal of Advanced Manufacturing Technology, 2014, 71(5-8), 1277.
31 Xie H M, Jiang B, He J J, et al. Tribology International, 2016, 93, 63.
32 Mahara M, Singh Y. Materials Today: Proceedings, 2020, 28, 1412.
33 Zawawi N N M, Azmi W H, Ghazali M F. Wear, 2022, 492-493, 204238.
34 Asadi M, Asadi A. International Communications in Heat and Mass Transfer, 2016, 76, 41.
35 Chen S Y, Liang J, Wellbun D, et al. Journal of Northeastern University(Natural Science Edition), 2015, 36(3), 378(in Chinese).
陈岁元, 梁京, Wellbun Dan, 等. 东北大学学报(自然科学版), 2015, 36(3), 378.
36 Shen Y D, Lei W W, Tang W T, et al. Wear, 2022, 488-489, 204175.
37 Sankar E, Duraivelu K. Materials Today: Proceedings, 2022, 68, 2387.
38 Lee K, Hwang Y, Cheong S, et al. Tribology Letters, 2009, 35(2), 127.
39 Wang X, Lin Z B. Surface and Coatings Technology, 2021, 421, 127440.
40 Meera K M S, Sankar R M, Murali A, et al. Colloids Surf B Biointerfaces, 2012, 90, 204.
41 Li M, Su B, Zhou B, et al. Applied Surface Science, 2020, 508, 145187.
42 He S T, Liu B C. Applied Chemical Engineering, 2017, 46(4), 693(in Chinese).
何淑婷, 刘宝春. 应用化工, 2017, 46(4), 693.
43 Liu L, Zhou W. Tribology International, 2017, 114, 315.
44 Yang Y W, Wang N, Ren J F, et al. Materials Reports, 2019, 33(19), 3242(in Chinese).
杨亚文, 王娜, 任俊芳, 等. 材料导报, 2019, 33(19), 3242.
45 Zhou X, Qiu S L, Liu L X, et al. Composites Part B: Engineering, 2019, 167, 599.
46 Wang N, Wang H G, Ren J F, et al. Materials & Design, 2020, 195, 109069.
47 Jiang S, Wang S, Han X H, et al, Chemical Progress, 2023, 42(11), 5811(in Chinese).
姜帅, 王姗, 韩旭辉, 等, 化工进展, 2023, 42(11), 5811.
48 Qi J L, Lin J H, Jia L G, et al. Vacuum, 2015, 123, 136.
49 Wang J, Hu J J, Liu Y, et al. Chemical Engineering and Equipment, 2017(12), 258(in Chinese).
王静, 胡建军, 刘妤, 等. 化学工程与装备, 2017(12), 258.
50 Liu X S, Zhou X C, Yang C Z, et al. Wear, 2022, 490-491, 204191.
51 Zhang C, Xu J Y, Sun G D, et al. Wear, 2021, 470-471, 203621.
52 Liu Y Y, Yao Z P, Zhang P, et al. Tribology International, 2023, 189, 108980.
53 Han Y, Wang J H, Ge X H, et al. Polymer Bulletin, 2023, 36(10), 1302(in Chinese).
韩阳, 王金伙, 葛晓宏, 等. 高分子通报, 2023, 36(10), 1302.
54 Qi Y, The research on characteristics of tribological transfer films of PEEK/PTFE composites reinforced with nanoparticles. Ph.D. Thesis, Lanzhou University of Science and Technology, China, 2020(in Chinese).
祁渊. 纳米粒子增强PEEK/PTFE 复合材料摩擦转移膜特性研究. 博士学位论文, 兰州理工大学, 2020.
55 Liu T, Rhee S K, Lawson K L. Wear, 1980, 60, 1.
56 Ma J. Research on tribological property of mesoporous silica reinforced polyimide-matrix composites. Ph.D. Thesis, Yanshan University, China, 2018(in Chinese).
马建. 介孔二氧化硅改性聚酰亚胺基复合材料的摩擦学性能研究. 博士学位论文, 燕山大学, 2018.
57 Hu J F, Zhang L L, Sun Z. Chemical Management, 2022(16), 145(in Chinese).
胡剑飞, 张丽丽, 孙震. 化工管理, 2022(16), 145.
58 Liu S X, Nano-inorganic/organic silicc on hybrid UV curable coatings. Master's Thesis, Lanzhou University of Science and Technology, China, 2008(in Chinese)
刘诗鑫. 纳米无机/有机硅杂化UV涂料的研制. 硕士学位论文, 兰州理工大学, 2008.
59 Das G, Karak N. Polymer Degradation and Stability, 2009, 94(11), 1948.
60 Bakunin V N, Suslov A Y. Kuzmina G N, et al. Journal of Nanoparticle Research, 2003, 6, 273.
61 Wei M, Hu Q L, Zhang L M, et al. Materials Reports, 2014, 28(4), 95(in Chinese).
魏铭, 胡巧玲, 张联盟, 等, 材料导报, 2014, 28(4), 95.
62 Wu Y, Properties of polyimide/modified nanosilica hybrid films. Master's Thesis,Donghua University, China, 2009(in Chinese).
吴瑶. 聚酰亚胺/改性纳米二氧化硅复合薄膜的性能研究. 硕士学位论文, 东华大学, 2009.
63 Li H Y, Li S, Li F B, et al. Journal of Colloid and Interface Science, 2018, 528, 92.
64 Guo Q B, Lau K T, Rong M Z, et al. Wear, 2010, 269(1-2), 13.
65 Hwang C. Min Y. Seong Y J, et al. Colloids and Surfaces B: Biointerfaces, 2019, 184, 110503.
66 Zhu Y Q, Li H X, Ji L, et al. Journal of Tribology, 2023, 43(9), 1083(in Chinese).
朱永琪, 李红轩, 吉利等, 摩擦学学报, 2022, 2023, 43(9), 1083.