POLYMERS AND POLYMER MATRIX COMPOSITES |
|
|
|
|
|
Preparation and Microstructure Characterization of Thermoplastic Polyurethane Modified Epoxy Resin |
SONG Chengzhe, ZHANG Guanhua*, QU Fenglai, FENG Liangyong
|
Liaoning Provincial Transportation Planning and Design Institute Co., Ltd., Shenyang 110111, China |
|
|
Abstract In order to obtain a flexible epoxy resin, a thermoplastic polyurethane elastomer (TPU) prepolymer prepared by polytetrahydrofuran ether diol (PTMEG) and diphenylmethane diisocyanate (MDI) was used to modify epoxy resin (E-51). The optimal mixing ratio of epoxy resin, TPU prepolymer and curing agent in polyurethane modified epoxy resin was obtained by testing mechanical properties such as tensile strength, elongation at break and bending strength. Microscopic properties of polyurethane modified epoxy resin were characterized by infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), thermogravimetry (TG) and scanning electron microscopy (SEM). The results showed that when the optimum reaction temperature of polyurethane prepolymer modified EP was 80 ℃, the content of polyurethane prepolymer was 20%, and the optimal mixing scheme of A and B components was 2∶1, the mechanical properties of the modified EP system was the best. Modified EP with surface drying time was 3.5 h, complete drying time was 9 h, tensile strength was 53.1 MPa, elongation at break was 153.34%, bending strength was 48.14 MPa, bending deformation was 13.61 mm, bonding strength was 1.89 MPa, T5% and T10% were 386.4 ℃ and 437.2 ℃, respectively, glass transition temperature was -27.9 ℃. The modification mechanism of polyurethane EP was analyzed by FTIR and SEM. It was found that the modification of polyurethane EP achieved the desired effect, and the process belonged to the category of chemical modification. This study can provide a theoretical basis for the reasonable selection of polyurethane modifier for epoxy resin.
|
Published: 25 May 2023
Online: 2023-05-23
|
|
Fund:Transportation Technology Project of Liaoning Province (201915). |
|
|
1 Wang P P, Tian X G, Zhang R, et al. Journal of Materials in Civil Engineering, 2021, 33(8), 1. 2 Chen Y, Wu X B, Tan X M, et al. China Adhesives, 2021, 30(4), 236 (in Chinese). 陈勇, 吴喜兵, 谭晓明, 等. 中国胶粘剂, 2021, 30(4), 236. 3 Li X, Lei B. China Adhesives, 2021, 30(4), 270 (in Chinese). 李兴, 雷斌. 中国胶粘剂, 2021, 30(4), 270. 4 Mueller M, Valasek P. The International Journal of Electrical Enginee-ring & Education, 2018, 505, 554. 5 Shariati M, Farzi G, Dadrasi A. Construction and Building Materials, 2015, 78, 362. 6 Rafal J, Michal D, Marek N, et al. Industrial & Engineering Chemistry Research, 2021, 60(5), 2178. 7 Li H L, Li T, Qi X H, et al. Polymer Materials Science and Enginee-ring, 2020(7), 15 (in Chinese). 李会录, 李涛, 祁向花, 等. 高分子材料科学与工程, 2020(7), 15. 8 Zhang Y Y, Wei J J, Kong L, et al. New Chemical Materials, 2021, 49(11), 1(in Chinese). 张艺媛, 魏建军, 孔林, 等. 化工新型材料, 2021, 49(11), 1. 9 Bahia H U, Anderson D A, Christensen D W. Association of Asphalt Pa-ving Technologists, 1992, 61, 117. 10 Zhou A J, Li C C, Li S G. China Syntehtic Fiber Industry, 2013, 36(2), 46 (in Chinese). 周爱军, 李长存, 黎树根. 合成纤维工业, 2013, 36(2), 46. 11 Merino D H, Driscoll B O, Harris P J, et al. Polymer Chemistry, 2018, 30(14), 4077. 12 Li W B, Zhou C, Cao C B, et al. Chinese Journal of Biomedical Engineering, 2011, 30(1), 130 (in Chinese). 李文波, 周晨, 曹成波, 等. 中国生物医学工程学报, 2011, 30(1), 130. 13 Liu Y J. Polyurethane industry(2nd Ed. ), Chemical Industry Press, China, 2012 (in Chinese). 刘益军. 聚氨酯工业(第二版), 化学工业出版社, 2012. 14 Liu H, Dong M Y, Huang W J, et al. Journal of Materials Chemsitry A, 2015, 17(5), 266. 15 Wang C, Xiao X, Lu Y, et al. Construction and Building Materials, 2019, 227(10), 1. 16 Li C Y, Gu Z Y, Liao H. China Adhesives, 2018, 27(11), 24 (in Chinese). 李翠影, 古忠云, 廖宏. 中国胶粘剂, 2018, 27(11), 24. 17 Jiangsu Zhonglu Engineering Technology Research Institute Co. , Ltd. . Technical guide for the treatment of colored polyurethane and modified epoxy resin surfaces on highway pavements, China Communications Press, China, 2018, pp.1 (in Chinese). 江苏中路工程技术研究院有限公司. 公路路面彩色聚氨酯及改性环氧树脂表面处治技术指南, 人民交通出版社, 2018, pp.1. 18 Allaoui A, Bai S, Cheng H M, et al. Composites Science and Technology, 2020, 62(15), 1993. 19 Seibold S, Schafer A, Lohstroh W, et al. Journal of Applied Polymer Science, 2008, 108(1), 264. 20 Ezquerra T A, Connor M T, Roy S, et al. Composite Science and Techno-logy, 2001, 61, 903. 21 Xiang Q, Xiao F P. Construction and Building Materials, 2020, 235, 2. 22 Cong P, Tian Y, Liu N, et al. Journal of Applied Polymer Science, 2016, 133(21), 321. 23 Kang Y, Song M, Pu L, et al. Construction and Building Materials, 2015, 76, 343. 24 Jiang L, Hu K, Liu Z, et al. Advances in Polymer Technology, 2018, 37(3), 830. 25 Liu Y, Zhang J, Jiang Y, et al. Construction and Building Materials, 2018, 165, 163. |
|
|
|