国产M40J级石墨纤维与氰酸酯树脂的界面性能

doi:10.11896/cldb.21050130

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (7556KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to analyze the feasibility of the application of domestic M40J carbon fiber in the spacecrafts, the interfacial properties of two kinds of domestic M40J carbon fibers (GCM40J-A, GCM40J-B) and cyanate ester(BS-4) system were evaluated by SEM, AFM, TG, surface tension meter, dynamic contact angle test and IR. The results show that the surface roughness of domestic M40J carbon fibers is similar to Toyal M40J carbon fiber, and the dynamic contact angles between three kinds of carbon fibers and BS-4 are 107°(GCM40J-A), 101.5°(GCM40J-B) and 100.3°(M40J) respectively. The heat resistance temperature of the three kinds of fiber sizing agents are higher than 230 ℃, which is also higher than the curing temperature of cyanate ester. Moreover, the sizing agents of GCM40J-A and GCM40J-B have higher reactivity than that of M40J, and the interlaminar shear strengths (ILSS) of GCM40J-A/BS-4 and GCM40J-B/BS-4 are 85.9 MPa and 84.7 MPa, which are higher than that of M40J/BS-4(72.5 MPa).

Key words： carbon fiber cyanate ester surface property interfacial property mechanical property

Published: 10 September 2022 Online: 2022-09-10

CLC number:

TB33

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHAO Zhenlu
	LIU Hongxin
	ZHANG Xin
	SUN Tianfeng
	LI Yu
	CHEN Weiqiang
	GU Yizhuo
	LIANG Chunzu

Cite this article:

ZHAO Zhenlu,LIU Hongxin,ZHANG Xin, et al. Interfacial Properties of Domestic M40J Carbon Fiber/Cyanate Ester Composites[J]. Materials Reports, 2022, 36(17): 21050130-5.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21050130 OR http://www.mater-rep.com/EN/Y2022/V36/I17/21050130

1 Tang J, Stephen K. Spacecraft Environment Engineering, 2010, 27(5), 552.
2 Bansemir H, Haider O. Cryogenics, 1998, 38(1), 51.
3 Zhao Z L, Chen W Q, Zhang Y S, et al. Journal of Astronautics, 2016, 37(5), 625(in Chinese).
赵臻璐, 陈维强, 张玉生, 等. 宇航学报, 2016, 37(5), 625.
4 Wo X Y, Zhou H Z. Spacecraft Recovery & Remote Sensing, 2002, 23(3), 52(in Chinese).
沃西源, 周宏志. 航天返回与遥感, 2002, 23(3), 52.
5 Jiang L X, He S Y, Yang S Q, et al. Journal of Materials Engineering, 2001(9), 39(in Chinese).
姜利祥, 何世禹, 杨士勤, 等. 材料工程, 2001(9), 39.
6 Arnold C, Mackenzie P, Malhotra V, et al. In: International SAMPE symposium and Exhibition. Anaheim, 1992, pp.128.
7 Seungjin H, Jan T L, Yasuhiro Y, et al. Carbon, 2008, 46, 1060.
8 Dai Z S, Shi F H, Zhang B Y, et al. Applied Surface Science, 2011, 257, 6980.
9 Peng G Q, Yang J J, Cao Z H, et al. Materials Reports A:Review Papers, 2011, 25(4), 1(in Chinese).
彭公秋, 杨进军, 曹正华, 等. 材料导报:综述篇, 2011, 25(4), 1.
10 Shi F H, Dai Z S, Zhang B Y. Journal of Aeronautical Materials, 2010, 30(3), 43 (in Chinese).
石峰晖, 代志双, 张宝艳. 航空材料学报, 2010, 30(3), 43.
11 Li W D, Zhang J D, Liu G, et al. Acta Materiae Compositae Sinica, 2016, 33(7), 1484(in Chinese).
李伟东, 张金栋, 刘刚, 等. 复合材料学报, 2016, 33(7), 1484.
12 Li J F, Zhang Y T, Zhang H J, et al. Fiber Reinforced Plastics/Compo-sites, 2013(5), 28(in Chinese).
李健芳, 张娅婷, 张宏杰, 等. 玻璃钢/复合材料, 2013(5), 28.
13 Li Z R, Zhang D, Xu L H, et al. Acta Materiae Compositae Sinica, 2015, 32(4), 1218(in Chinese).
李昭锐, 张东, 徐樑华, 等. 复合材料学报, 2015, 32(4), 1218.
14 Luo Y F, Zhao Y, Duan Y X, et a1. Materials & Design, 2011, 32(2), 94l.
15 Zhang R L, Huang Y D, Su D, et al. Materials & Design, 2012, 34, 649.
16 Wang Y F, Liu G, Peng G Q, et al. Journal & Materials Engineering, 2018, 46(4), 140(in Chinese).
王迎芬, 刘刚, 彭公秋, 等. 材料工程, 2018, 46(4), 140.
17 Luo Y F, Yang Z, Zhao Y, et a1. Materials Science and Technology, 2014, 22(4), 62(in Chinese).
罗云烽, 杨喆, 肇研, 等. 材料科学与工艺, 2014, 22(4), 62.
18 Liu W D, Chen J L, Li Y, et al. Journal of Materials Engineering, 2016, 44(10), 88(in Chinese).
刘卫丹, 陈俊林, 李阳, 等. 材料工程, 2016, 44(10), 88.
19 Hao H, Li P, Ling H, et al. Fiber Reinforced Plastics/Composites, 2013(1), 30(in Chinese).
郝华, 李鹏, 凌辉, 等. 玻璃钢/复合材料, 2013(1), 30.
20 Liu J, Tian Y, Chen Y, et al. Applied Surface Science, 2010, 256(21), 6199.
21 Xu Y X, Gu Y Z, Ma Q S, et al. Acta Materiae Compositae Sinica, 2016, 33(9), 1905(in Chinese).
徐永薪, 顾轶卓, 马全胜, 等. 复合材料学报, 2016, 33(9), 1905.
22 Zhang S J, Wang R N, Liu N, et al. Journal of Materials Engineering, 2019, 47(8), 118(in Chinese).
张世杰, 王汝敏, 刘宁, 等. 材料工程, 2019, 47(8), 118.
23 Shui X Y, Liu M, Zhu Y F, et al. Acta Materiae Compositae Sinica, 2016, 33(2), 273(in Chinese).
水兴瑶, 刘猛, 朱曜峰, 等. 复合材料学报, 2016, 33(2), 273.