氧化石墨烯/聚酯树脂涂层的制备及耐腐蚀性能

doi:10.11896/cldb.20030152

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (3659KB)
Export: BibTeX | EndNote (RIS)

Abstract Graphene was widely used in the field of anticorrosive coatings because of its excellent properties such as good barrier property, high mechanical strength and large specific surface area. Graphene oxide with good dispersion was added into polyester resin powder and the po-lyester coating with different contents of GO was prepared on 6063 aluminum alloy substrate pretreated with silane coupling agent by electrostatic spraying technology. The composition of silane film was analyzed by EDS spectrum and corrosion resistance of silane membrane was evaluated by electrochemical experiments; nano-indentation test was used to characterize the adhesion between coating and substrate; the effect of GO on the corrosion resistance of polyester coating was studied by immersion test and neutral salt spray test. The results showed that the corrosion potential of silane film was -0.831 V, which was higher than that of Zr-Ti film (-0.967 V), and the corrosion current density of silane film was 5.361×10^-8 A/cm², which was lower than that of Zr-Ti film (8.350×10^-8 A/cm²). Compared with the TiZr film, the silane film had higher self-corrosion potential, lower self-corrosion current density and better corrosion resistance. The critical load value L_C1 and L_C2 of the coating on the substrate surface pretreated with silane coupling agent were 2 035.71 mN and 3 066.66 mN, respectively, which were higher than those pretreated by Zr-Ti film (1 667.40 mN), and the adhesion between the coating and the substrate was stronger. Compared with the polyester coating without GO, the polyester coating with a mass fraction of 0.5% GO had the lowest weight loss and weight loss rate, and the surface of polyester coating showed fewer pores and corrosion pits after the 1 000 h salt spray experiment, so its corrosion resistance was evidently enhanced. Thus, the corrosion resistance of the coating was significantly improved when GO was added to the polyester resin coating with a mass fraction of 0.5%.

Key words： silane coupling agent grapheme oxide polyester coating electrostatic spraying technology corrosion resistance

Published: 04 June 2021

CLC number:

TL214

About author:: Mingyan Cao entered Hohai University to pursue her master's degree in September 2018. Her main research interests are preparation and corrosion resistance of GO/organic coatings.
Yuping Wu received her Ph.D. from Southeast University, and has been working in Hohai University as a full professor in materials science since then. Her current research interests involve material surface engineering and metal materials. Up to now, she has published more than 80 peer-reviewed papers in international prestigious journals, and been awarded more than 10 invention patents.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CAO Mingyan
	YU Aibin
	WU Yuping
	QIAO Lei
	CHENG Jie

Cite this article:

CAO Mingyan,YU Aibin,WU Yuping, et al. Preparation of GO/Polyester Resin Coatings and Its Corrosion Resistance[J]. Materials Reports, 2021, 35(10): 10227-10231.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.20030152 OR http://www.mater-rep.com/EN/Y2021/V35/I10/10227

1 Yu Y G, Ou Y M, Shen G K, et al. Polyurethane Industry, 2018, 33(3), 1 (in Chinese).
于运歌, 欧耀明,沈国康,等. 聚氨酯工业,2018,33(3), 1.
2 Hayatgheib Y, Ramezanzadeh B, Kardar P, et al. Corrosion Science, 2018, 133, 358.
3 Cui M, Ren S, Chen J, et al. Applied Surface Science, 2017, 397, 77.
4 Pourhashem S, Vaezi M R, Rashidi A. Surface and Coatings Technology, 2017, 311(Complete), 282.
5 Yang L H, Wan Y X, Qin Z L, et al. Corrosion Science, 2018, 130, 85.
6 Yang N, Yang T, Wang W, et al. Journal of Hazardous Materials, 2019, 377, 142.
7 Zhou D H, Qu J E, Wang H R, et al. Materials Reports, 2016,30(32), 504 (in Chinese).
周东浩, 屈钧娥, 王海人, 等.材料导报, 2016,30(专辑28), 504.
8 Jiang F W, Zhao W J, Wu Y M, et al. Applied Surface Science, 2019, 479, 963.
9 Ramezanzadeh B, Niroumandrad S, Ahmadi A, et al. Corrosion Science, 2016,103, 283.
10 Wang J F, Lin L, He D N.Materials Reports, 2018, 32(S2), 111 (in Chinese).
王敬锋, 林琳, 何丹农.材料导报, 2018, 32(S2), 111.
11 He Q, Ma A B, Jiang J H, et al. Journal of Functional Materials, 2013, 44(S2), 176 (in Chinese).
何青,马爱斌,江静华,等.功能材料, 2013, 44(S2), 176.
12 Zhou C, Hong M, Yang Y, et al. Applied Surface Science, 2019, 484, 663.
13 Cui M J, Ren S M, Wang Y G, et al. Surface Technology, 2019, 48(6), 46 (in Chinese).
崔明君,任思明,王永刚,等.表面技术, 2019, 48(6), 46.
14 Zhang X R, Ma R, Du A, et al. Applied Surface Science, 2019, 484, 819.
15 Ramezanzadeh B, Ghasemi E, Mahdavian M, et al. Carbon, 2015, 93, 555.
16 Batan A, Mine N, Douhard B, et al. Chemical Physics Letters, 2010, 493, 107.
17 Arkles B.Chemtech, 1997,7, 766.
18 Zhang Y Q, Yang L X, Xie P B. Materials Protection, 2017, 50(12), 75 (in Chinese).
张焱琴, 杨丽霞, 谢鹏波.材料保护, 2017, 50(12), 75.
19 Wang L, Xuan T P, Zhou Y, et al.Electroplating & Pollution Control, 2012, 32(6), 9 (in Chinese).
汪亮, 宣天鹏, 周赟, 等.电镀与环保, 2012, 32(6), 9.
20 Nan R Z.Powder coating and coating technology, the third edition, Che-mical Industry Press, China, 2014, pp.214 (in Chinese).
南仁植.粉末涂料与涂装技术, 第三版, 化学工业出版社, 2014, pp.214.
21 Jiang L, Syed J A, Gao Y Z, et al. Applied Surface Science, 2018, 440, 1019.
22 Liu Q, Ma R N, Du A, et al. Applied Surface Science, 2019,480, 651.
23 Cao C N. Electrochemical principles of corrosion (3rd edition), Chemical Industry Press, China, 2008 (in Chinese).
曹楚南. 腐蚀电化学原理(第三版),化学工业出版社, 2008.
24 Beake B D, Vishnyakov V M, Harris A J. Surface and Coatings Technology, 2017, 309, 673.
25 Wang X X, Fu H L, Jiang M Y, et al. Journal of Coatings Technology and Research, 2019, 16(4), 975.
26 Xing T J, Ying L X, Wu C X, et, al.Anti-Corrosion Methods and Mate-rials, 2019, 66(4), 449.
27 Ding J H, Zhao H Y, Zheng Y,et al. Carbon, 2018, 138, 203.
28 Zhong F, He Y, Wang P Q, et al. Applied Surface Science, 2019, 488, 809.
29 Liu S, Gu L, Zhao H C, et al. Journal of Materials Science and Technology, 2016, 32, 429.
30 Cui M J, Ren S M, Zhao H C, et al.Chemical Engineering Journal, 2018, 335, 263.