苯基硅橡胶泡沫的制备及阻尼性能

doi:10.11896/cldb.18090240

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (9977KB)

Suppl. Info.
Export: BibTeX | EndNote (RIS)

Abstract The phenyl silicone rubber foam was prepared by chemical foaming method. The kinetics of phenyl silicone rubber in the vulcanization foaming process was investigated. The damping properties of the phenyl silicone rubber system with foam structure were studied. The phenyl silicone rubber foam with different cell and density can be prepared by adjusting the vulcanization processing temperature and the amount of foaming agent. The damping property of the foam is obviously better than that of the solid rubber. The effective damping temperature range of the phenyl silicone rubber foam with cell diameter of about 100 μm and density of 0.74 g/cm³ is 47 ℃ higher than that of the solid rubber, and the damping peak is increased by 14%.

Key words： phenyl silicone rubber foam dynamics damping property

Published: 16 May 2019

CLC number:

TQ333.93

About author:: Yang Hu is currently studying in Southwest University of Science and Technology, under the guidance of teacher Lu Al and Mr. Zhao Qi.Since March 2017, he has been co-educated and learned at China Academy of Engineering Physics.
Qi Zhao received Ph.D. degree at Beijing Institute of Technology. He is currently an associate professor in China Academy of Engineering Physics Institute of Chemical Mate-rials, mainly engaged in polymer mate-rials research work.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HU Yang
	ZHAO Qi
	LU Ai
	WANG Zhiyong
	SHEN Simin

Cite this article:

HU Yang,ZHAO Qi,LU Ai, et al. Preparation and Damping Properties of Phenyl Silicone Rubber Foam[J]. Materials Reports, 2019, 33(10): 1752-1755.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.18090240 OR http://www.mater-rep.com/EN/Y2019/V33/I10/1752

1 Yao S R. Means to widen the temperature range of high damping behavior by IPN formatiom, Lancaster Technology Publishing Company,US,1994.
2 Yue Y, Zhang H, Zhang Z, et al.Composites Science and Technology,2013, 86, 1.
3 Nouri N M, Saadat-Bakhsh M. Journal of Coatings Technology and Research, 2017,14(2), 477.
4 Wu Weili, Wang Jun. Silicon, 2018,10(5),1903.
5 Deepak Sethi,Ranvijai Ram, Dipak Khastgir.Polymer International, 2017, 66(9),1295.
6 Sun Q J. Silicone Material, 2005,19(6), 13(in Chinese).
孙全吉.有机硅材料,2005,19(6), 13.
7 Hujare P P, Sahasrabudhe A D.Procedia Materials Science, 2014, 5, 726.
8 Xiong X, Wang J Y, Jia H B, et al. Polymer Composites, 2013,35(8), 1466.
9 Wu C F, Otani Y, Namiki N,et al.Journal of Applied Polymer Science, 2001,82(7), 1788.
10 Wang J Y, Jia H B, Ding L F,et al.Polymers for Advanced Technologies, 2015,26(9), 1168.
11 Hujare P P, Sahasrabudhe A D.Procedia Materials Science, 2014,5, 726.
12 Tang Z H, Xie Z J, Qu L L,et al.China Rubber Industry,2007,54(10),610(in Chinese).
唐振华,谢志坚,曲亮靓,等.橡胶工业,2007,54(10),610.
13 Banhart J, Baumeister J,Weber M.Materials Science and Engineering: A, 1996,205(1-2), 221.
14 Golovin I S, Sinning H R, Arhipov I K, et al. Materials Science and Engineering: A, 2004, 370(1-2), 531.
15 Scarpa F, Pastorino P, Garelli A, et al.Physica Status Solidi (B), 2005,242(3), 681.
16 Subramaniam K, Das A, Heinrich G.Composites Science and Technology,2011,71(11), 1441.
17 Song L Y, Li Z H, Li L B, et al.RSC Advances, 2016,6(103), 101470.
18 Ghaemy M, Rostami A A, Omrani A.Polymer International, 2010, 55 (3),279.
19 Wu J R, Wang X, Huang G S,et al. Polymer,2013,54(13),3314.
20 Chang M C O, Thomas D A, Sperling L H. Journal of Applied Polymer Science, 1987,34(1), 409.
21 Wang Q, Huang G S, Yu L J, et al.The World Rubber Industry, 2008, 35(6),20(in Chinese).
王强, 黄光速, 于连江, 等.世界橡胶工业,2008, 35(6),20.