低温回火的SIMP钢在铅铋共晶合金下的液态金属脆化敏感性研究

doi:10.11896/cldb.25030039

Abstract
Figure/Table
References
Related Citation (3)

Download:

Full Text ( PDF ) (51958KB)
Export: BibTeX | EndNote (RIS)

Abstract This work systematically examines the effects of temperature and strain rate on liquid metal embrittlement (LME) susceptibility of silicon-enhanced ferritic/martensitic SIMP steel in lead-bismuth eutectic (LBE) environments, with emphasis on elucidating the underlying mechanisms. To simulate irradiation-induced hardening, SIMP steel was tempered at 500 ℃, a reduced temperature compared to conventional proces-sing. Slow strain rate tensile (SSRT) tests were conducted on 500 ℃-tempered specimens in both argon and oxygen-saturated LBE at temperatures ranging from 350 ℃ to 550 ℃, with strain rates varying between 2×10^-6 s^-1 and 1×10^-5 s^-1. Comparative analyses were performed against reference specimens tempered at 760 ℃. Results demonstrated threre is a pronounced LME susceptibility in 500 ℃-tempered specimens at 350 ℃ and 400 ℃, evidenced by a marked reduction in total elongation and quasi-brittle fracture morphology. Notably, this embrittlement vanishes at 550 ℃, where ductile fracture characteristics and full elongation recovery are observed. In contrast, 760 ℃-tempered specimens exhibited no LME across all tested conditions. Strain rate dependence studies reveal that LME persists at both low (2×10^-6 s^-1) and high (1×10^-5 s^-1) strain rates for 500 ℃-tempered steel; however, sensitivity is significantly amplified at lower strain rates. The research results should provide an important basis for understanding the service performance of SIMP steel in LBE environment.

Key words： SIMP steel liquid metal embrittlement lead-bismuth eutectic slow strain rate tensile tests

Published: 25 April 2026 Online: 2026-05-06

CLC number:

TL341

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Jie
	QIN Bo
	FU Xiaogang
	LONG Bin

Cite this article:

ZHANG Jie,QIN Bo,FU Xiaogang, et al. Study on Embrittlement Sensitivity of SIMP Tempered at Low Temperature in Liquid Metal Under Lead-Bismuth Eutectic Alloy[J]. Materials Reports, 2026, 40(8): 25030039-10.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.25030039 OR https://www.mater-rep.com/EN/Y2026/V40/I8/25030039

1 Murty K L, Charit I. Journal of Nuclear Materials, 2008, 383(1-2), 189.
2 Alberto P, Fradera J, Sadaba S, et al. Fusion Engineering and Design, 2022, 178, 113.
3 Zhang J. Corrosion Science, 2009, 51(6), 1207.
4 Colombo M, Cammi A, Memoli V, et al. Progress in Nuclear Energy, 2010, 52(8), 715.
5 Lorusso P, Bassini S, et al. Progress in Nuclear Energy, 2018(105), 318.
6 Aiello A, Azzati M, et al. Journal of Nuclear Materials, 2004, 335(2), 169.
7 Van den Bosch J, Bosch R W, et al. Journal of Nuclear Materials, 2008, 376(3), 322.
8 Gong X, Chen H, Wang Z, et al. Journal of Nuclear Materials, 2022, 563, 153641.
9 Van den Bosch J, Coen G, et al. Journal of Nuclear Materials, 2012, 429(1-3), 105.
10 Legris A, Nicaise G, Vogt J B, et al. Journal of Nuclear Materials, 2002, 301(1), 70.
11 Stoloff N S, Johnston T L. Acta Metallurgica, 1963, 11(4), 251.
12 Westwood A R C, Kamdar M H. Philosophical Magazine, 1963, 8(89), 787.
13 Lynch S P. Metallurgical and Materials Transactions A, 2013, 44(3), 1209.
14 Hancock P C, Ives M B. Quarterly, 1971, 10(3), 207.
15 Glickman E E. Interface Science, 2003, 11, 451.
16 Gordon P, An H H. Metallurgical Transactions A, 1982, 13, 457.
17 Dmukhovskaya I G, Popovich V V. Materials Science, 1983, 18(6), 461.
18 Long B, Dai Y. Journal of Nuclear Materials, 2008, 376(3), 341.
19 Long B, Tong Z, Gröschel F, et al. Journal of Nuclear Materials, 2008, 377(1), 219.
20 Huang Z Y, Xiao Y, Hou Q Y, et al. Iron & Steel, 2015, 50(8), 6(in Chinese).
黄贞益, 肖亚, 侯清宇, 等. 钢铁, 2015, 50(8), 6.
21 Ganeev A, Nikitina M, Sitdikov V, et al. Materials, 2018, 11(4), 627.
22 Liu J, Yan W, Sha W, et al. Journal of Nuclear Materials, 2016, 473, 189.
23 Zhang L L. A study on the role and mechanism of Si in nuclear SIMP steel. Ph. D. Thesis, University of Science and Technology of China, China, 2021(in Chinese).
张玲玲. 核用SIMP钢中Si元素的作用机理研究. 博士学位论文, 中国科学技术大学, 2021.
24 Chen Z X, Xu X C, Wang B, et al. Chinese Journal of Engineering, 2012, 34(3), 7(in Chinese).
陈振湘, 许晓嫦, 王斌, 等. 工程科学学报, 2012, 34(3), 7.
25 Huang B, Guo Z B, Shuai L T, et al. Failure Analysis and Prevention, 2021, 16(6), 5(in Chinese).
黄蓓, 郭占兵, 帅林涛, 等. 失效分析与预防, 2021, 16(6), 5.
26 Sarikaya M, Jhingan A K, Thomas G. Metallurgical Transactions A, 1983, 14(5), 1121.
27 Xu Z Y. Martensitic transformation and martensite, Beijing Science Press, China, 1999, pp. 66(in Chinese).
徐祖耀. 马氏体相变与马氏体, 北京科学出版社, 1999, pp. 66.
28 Wang H, Yan W, Shi Q Q, et al. Heat Treatment of Metals, 2018, 43(5), 7(in Chinese).
王海, 严伟, 石全强, 等. 金属热处理, 2018, 43(5), 7.
29 Zhang L, Wang Z P, Liu J N, et al. Foundry Technology, 2003, 24(6), 3(in Chinese).
张路, 王正品, 刘江南, 等. 铸造技术, 2003, 24(6), 3.
30 Gong X, Sun L, Zhang F, et al. Corrosion Science, 2022, 208, 110522.
31 Gong X, Hu F, Chen J, Wang H, et al. Journal of Nuclear Materials, 2020, 537, 152196.
32 Gong X, Marmy P, Qin L, et al. Journal of Nuclear Materials, 2016, 468, 35.
33 Hadjem-Hamouche Z, Auger T, Guillot I. Corrosion Science, 2009, 51(11), 2580.
34 Dai Y, Long B, Groeschel F. Journal of Nuclear Materials, 2006, 356(1-3), 222.
35 Ersoy F, Verbeken K, Gavrilov S. Materials Science and Engineering: A, 2021, 800, 140259.
36 Ye C, Vogt J B, Serre I P. Materials Science and Engineering: A, 2014, 608, 242.