多孔Fe24Cr金属支撑体厚度对SOFC性能的影响

doi:10.11896/cldb.23110193

Abstract
Figure/Table
References
Related Citation (5)

Download:

Full Text ( PDF ) (10233KB)
Export: BibTeX | EndNote (RIS)

Abstract The metal-supportedsolid oxide fuel cell (MS-SOFC) is expected to be used in unmanned aerial vehicles, portable power and mobile powers due to its advantages such as low cost, good mechanical properties and fast start-stop capability. In order to improve the performance and lifetime of MS-SOFC, the metal support not only needs to match the thermal expansion coefficient of electrolyte to reduce stress, but also needs high permeability to improve the diffusion and reaction rate of fuel gas. In this work, three kinds of Fe24Cr supports with different thickness of 1 mm, 0.8 mm and 0.5 mm were prepared, and their coefficient of thermal expansion were compared with the traditional 430 support. Meanwhile, the effects of the thickness on the air permeability and electrochemical performance of the support were investigated. The results showed that the coefficient of thermal expansion of Fe24Cr support is 12.74×10^-6 K^-1, which is more suitable for zirconia-based electrolyte than the traditional 430 support. Comparing with the 1 mm thick support, the 0.5 mm thick Fe24Cr support can significantly shorten the gas transmission path, increase the gas permeability by about 5 times and increase the output performance by more than 15%. At 800 ℃ the polarization impedance and ohmic impedance of the cell decrease to 0.203 Ω·cm² and 0.118 Ω·cm² respectively, and the peak power density reaches 1.215 W/cm². The distribution of relaxation times (DRT) analysis showed that the reduction of the support thickness contributes greatly to the ohmic impedance of SOFC and the rate of H₂ diffusion to the three-phase reaction interface, which can be matched well with the electrochemical performance results of the cell.

Key words： metal-supported SOFC thickness of the substrates coefficient of thermal expansion gas permeability electrochemical perfor-mance

Published: 10 January 2025 Online: 2025-01-10

CLC number:

TK91

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Pi
	SONG Chen
	DONG Dongdong
	ZENG Dengchang
	LIU Taikai
	WEN Kui
	MAO Jie
	LIU Min

Cite this article:

WANG Pi,SONG Chen,DONG Dongdong, et al. Effect of Thickness of Porous Fe24Cr Metal Support on SOFC Performance[J]. Materials Reports, 2025, 39(1): 23110193-7.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.23110193 OR https://www.mater-rep.com/EN/Y2025/V39/I1/23110193

1 Minh N Q, Shirley Meng Y. MRS Bulletin, 2019, 44(9), 682.
2 Mcpherson M, Johnson N, Strubegger M. Applied Energy, 2018, 216, 649.
3 Weber A. Fuel Cells, 2021, 21(5), 440.
4 Opakhai S, Kuterbekov K. Energies, 2023, 16(12), 4700.
5 Baldi F, Moret S, Tammi K, et al. Energy, 2020, 194, 116811.
6 Boldrin P, Brandon N P. Nature Catalysis, 2019, 2(7), 571.
7 Corigliano O, Pagnotta L, Fragiacomo P. Sustainability, 2022, 14(22), 15276.
8 Molin S, Chrzan A, Karczewski J, et al. Electrochimica Acta, 2016, 204, 136.
9 Lyu Y, Wang F, Wang D, et al. Materials Technology, 2019, 35(4), 212.
10 Chang H, Yan J, Chen H, et al. Ceramics International, 2019, 45(8), 9866.
11 Wei J, Osipova T, Malzbender J, et al. Ceramics International, 2018, 44(10), 11094.
12 Xu X H, Wu Y H, Yan Z L, et al. Advances in Mechanics, 2021, 51(1), 62 (in Chinese).
徐心海, 吴愉华, 严资林, 等. 力学进展, 2021, 51(1), 62.
13 Zhuang L L, Jin S T. Gansu Metallurgy, 2022, 44(2), 61 (in Chinese).
庄丽丽, 靳塞特. 甘肃冶金, 2022, 44(2), 61.
14 Tietz F. Ionics, 1999, 5, 129.
15 Öztürk B, Topcu A, Cora Ö N. Powder Technology, 2021, 382, 199.
16 Brandner M, Bram M, Froitzheim J, et al. Solid State Ionics, 2008, 179(27-32), 1501.
17 Bernadet L, Segura-Ruiz J, Yedra L, et al. Journal of Power Sources, 2023, 555, 232400.
18 Molin S, Gazda M, Jasinski P. Solid State Ionics, 2010, 181(25-26), 1214.
19 Oishi N, Yoo Y. ECS Transactions, 2009, 25(2), 739.
20 Cheng L. Phase-inversion fabricationand characterization of solid oxide cells. Ph. D. Thesis, University of Science and Technology of China, China, 2015 (in Chinese).
陈龙. 固体氧化物电池的相转化法制备和性能表征. 博士学位论文, 中国科学技术大学, 2015.
21 Hwang C S, Tsai C H, Hwang T J, et al. Fuel Cells, 2016, 16(2), 244.
22 Nielsen J, Persson Å H, Muhl T T, et al. Journal of the Electrochemical Society, 2018, 165(2), F90.
23 Du K, Song C, Yu M, et al. Journal of the Chinese Ceramic Society, 2022, 50(7), 1929 (in Chinese).
杜柯, 宋琛, 余敏, 等. 硅酸盐学报, 2022, 50(7), 1929.
24 Zhu Z G, Song C, Hu Y J, et al. Materials Research and Application, 2023, 17(2), 329 (in Chinese).
朱志刚, 宋琛, 胡永俊, 等. 材料研究与应用, 2023, 17(2), 329.
25 Wen J, Song C, Deng Z Q, et al. Materials Research and Application, 2020, 14(2), 116 (in Chinese).
温靖, 宋琛, 邓子谦, 等. 材料研究与应用, 2020, 14(2), 116.
26 Wen K, Liu X Z, Shao Z J, et al. Materials Research and Application, 2022, 16(1), 29 (in Chinese).
文魁, 刘学璋, 邵祉谏, 等. 材料研究与应用, 2022, 16(1), 29.
27 Manjunath N, Santhy K, Rajasekaran B. Materials Today:Proceedings, DOI: 202310.1016/j. matpr. 2023. 03. 113.
28 Dong L F, Zhang X, Dou W Y, et al. Powder Metallurgy Industry, 2016, 26(5), 25 (in Chinese).
董领峰, 张旭, 窦微英, 等. 粉末冶金工业, 2016, 26(5), 25.
29 Zhang J, Guo H, Lei L, et al. Journal of Power Sources, 2023, 562, 232725.
30 Zhang J, Lei L, Li H, et al. Journal of Power Sources, 2021, 516, 230678.
31 Fang Q, Blum L, Stolten D. ECS Transactions, 2019, 91(1), 687.
32 Fang Q, De Haart U, Schäfer D, et al. Journal of the Electrochemical Society, 2020, 167(14).
33 Xia J, Wang C, Wang X, et al. Electrochimica Acta, 2020, 349, 136328.
34 Wang Y, Marchetti B, Zhou X D. International Journal of Hydrogen Energy, 2022, 47(83), 35437.
35 Tsai C H, Yang C S, Chang C, et al. Fuel Cells, 2023, 23(4), 292.