硅质机制砂改性剂的机理研究与应用

doi:10.11896/j.issn.1005-023X.2017.024.012

Abstract
Figure/Table
References
Related Citation (10)

Download:

Full Text ( PDF ) (895KB)
Export: BibTeX | EndNote (RIS)

Abstract Because of the high content of stone powder and the ability of stone powder to absorb water reducing agent, the workability of concrete prepared by siliceous machine-made sand is poor. A small molecule surfactant, referred to as modifier, was prepared to improve the occurrence of siliceous sand. Firstly, the composition, morphology and characteristics of machine-made sand powder were analyzed. Then, the expansion degree of mortar of different stone powder with and without the addition of modifier was compared and applied in two kinds of siliceous machine-made sand concrete. Finally, the mechanism of modifier was analyzed by means of particle size analysis, micrograph, SEM and Zeta potential. Experimental results show that the modified agent of siliceous mechanism sand can effectively increase the degree of expansion of concrete mortar which improve the initial slump effectively and reduce slump loss of concrete. And it has little influence on the strength. The modified agent is mainly used to improve the workability of the siliceous mechanism sand concrete by complexation with strong dispersion and adsorption,and reduce the negative influence.

Key words： siliceous machine-made sand sandstone powder modifier water reducing agent

Published: 25 December 2017 Online: 2018-05-08

CLC number:

TU525

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Guangtian
	LIU Juanhong
	SUI Baolong
	CHEN Zhaoyang

Cite this article:

ZHANG Guangtian,LIU Juanhong,SUI Baolong, et al. Mechanism Study and Application of the Modifier for Siliceous Machine-made Sand[J]. Materials Reports, 2017, 31(24): 56-62.

URL:

https://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.024.012 OR https://www.mater-rep.com/EN/Y2017/V31/I24/56

1 Song Shaomin, Liu Juanhong, Xu Guoqiang. The summarize and study of the application of limestone powder in concrete[J]. China Concret,2009(12):38(in Chinese).
宋少民,刘娟红,徐国强. 石灰石粉在混凝土中应用的综述与研究[J]. 混凝土世界,2009(12):38.
2 Liu Zhanao,Zhou Mingkai,Li Beixing.Research progresson influence of microfines on manufactured sand concrete′s performance[J]. Mater Rev:Rev, 2014, 28(10): 100(in Chinese).
刘战鳌,周明凯,李北星. 石粉对机制砂混凝土性能影响的研究进展[J]. 材料导报:综述篇,2014,28(10):100.
3 Chen Jianxiong, Li Hongfang, Chen Hanbin. Study of super high strength concrete containing super fine limestone powder and titanium slag powder[J]. J Build Mater, 2005,8(6):672.
4 Zhou Yongxiang, Wang Yonghai, Wang Siya, et al. The characteristic of limestone powder and its effect on performance of concrete[J].Constr Technol,2014(9):23(in Chinese).
周永祥,王永海,王思娅,等.石灰石粉的特性及对混凝土性能的影响[J].施工技术,2014(9):23.
5 Cai Jiwei. Research of effects and mechanism of micro fine aggergate concretes[D]. Wuhan:Wuhan University of Technology,2006(in Chinese).
蔡基伟. 石粉对机制砂混凝土性能的影响及机理研究[D]. 武汉:武汉理工大学,2006.
6 周昱程,等.机制砂中硅质石粉含量对混凝土流动性能的影响及改善[C]//第八届全国特种混凝土技术交流会论文集.中国土木工程学会混凝土及预应力分会混凝土质量专业委员会,2017:8.
7 Sui Baolong,Yuan Jie, Zhang Guangtian,et al. An overview of the effects of mud content on the performance of concrete and its control methods[J]. Fiy Ash Cormprutil, 2016(4):61(in Chinese).
隋宝龙,袁杰,张广田,等. 含泥量对混凝土性能的影响及解决方法[J]. 粉煤灰综合利用,2016(4):61.
8 Zhang Guangtian, Gao Zhenguo, Liu Juanhong. Effect of different molecular weight of PASP on the performance of concrete[J].China Concr Cem Products,2016(5):12(in Chinese).
张广田,高振国,刘娟红.不同分子量聚天冬氨酸对混凝土性能的影响[J]. 混凝土与水泥制品,2016(5):12.
9 Tang Yuchao, Chen Liang, Luo Zuoqiu,et al. Development and performance research of new high-plastic-superretarding admixture[J]. Mater Rev, 2015, 29(S1):354(in Chinese).
唐玉超,陈良,罗作球,等. 新型高保塑超缓凝剂的研制与性能研究[J]. 材料导报,2015,29(专辑25):354.
10Ma Kunlin, Long Guangcheng, Xie Youjun,et al. Rheological properties of compound pastes-cement-fly ash-limestone powder[J]. J Chin Ceram Soc,2013(5):582(in Chinese).
马昆林,龙广成,谢友均,等. 水泥-粉煤灰-石灰石粉复合浆体的流变性能[J]. 硅酸盐学报,2013(5):582.
11Ezziane K, et al.Evaluation of rheological parameters of mortar containing various amounts of mineral addition with polycarboxylate superplasticizer[J].Constr Build Mater, 2014,70:549.
12Miao C W, Ran Q P, Liu J P, et al.New generation amphoteric comb-like copolymer superplasticizer and its properties[J].Polym Polym Compos, 2011,19(1):1.
13Fu Shifeng, Zhang Guangtian, Liu Juanhong. Study on mechanical and durability of recycled lightweight aggregate concrete[J].Building Struct, 2016(12):41(in Chinese).
付士峰,张广田,刘娟红. 再生轻骨料自密实混凝土力学和耐久性能研究[J]. 建筑结构,2016(12):41.
14Jalal M, et al.Comparative study on effects of class F fly ash, nano silica and silica fume on properties of high performance self compacting concrete[J].Constr Build Mater, 2015,94:90.
15Shen Yeqing, Zhai Chao,Sun Chengyu. Influence of molding process on the structure and performance of hardened cement pastes[J].Mater Rev: Rev,2016,30(8):100(in Chinese).
沈业青,翟超,孙成玉. 水泥材料成型过程对硬化体结构与性能的影响[J]. 材料导报:综述篇,2016,30(8):100.
16Guo W J, Sun N, Qin J J, et al.Synthesis and properties of an amphoteric polycarboxylic acid-based superplasticizer used in sulfoaluminate cement[J].J Appl Polym Sci, 2012,125(1):283.
17Zhang Ronghua, Zhu Zhiliang, Deng Shouquan, et al. Study on the coordination chemistry of ATMP with Ca²⁺, Mg²⁺ in aqueoussolution[J]. Ind Water Treatment, 2003,23(7):25(in Chinese).
张荣华, 朱志良, 邓守权, 等. ATMP 对钙、镁离子阻垢作用机理的配位化学研究[J].工业水处理,2003,23(7):25.
18秦廉. 复合屏蔽剂对高含泥量骨料混凝土性能的改善效果及其机理[C]//2011年混凝土与水泥制品学术讨论会论文集.中国硅酸盐学会混凝土与水泥制品学分会,2011:7.
19Lei L, Plank J. A concept for a polycarboxylate superplasticizer possessing enhanced clay tolerance[J]. Cem Concr Res, 2012,42(10):1299.