Abstract: In order to study the fatigue properties of self-piercing riveted(SPR) T joints, three sets of T joints (1420 aluminum-lithium alloys joined with itself (AA joints), with H62 copper alloys (HA joints) and with 410 stainless steel(SA joints)) were prepared. Fatigue test were conducted on the basis of peeling test. The effectiveness of test data was analyzed by two-parameter Weibull distribution, and the equations of fatigue load-fatigue life curves were calculated by least square method. Scanning electron microscope was adopted to observe the appearance of the joints fracture. The results show that the fatigue life of SA joints was the most sensitive to the load fluctuation which were loaded on joints, and fatigue life decreased with the increasing relative slippage. The weak point of the joints transferred from rivets to sheets. From micro-view, the fracture features of crack initiation region is flatter than the fracture features of crack transient zone which are mainly the intergranular fracture or the dimple.
1 Mucha J. A study of quality parameters and behavior of self-piercing riveted aluminum sheets with different joining conditions[J]. J Mech Eng,2011,57(4):323. 2 Pickin C G, et al. Joining of lightweight sandwich sheets to aluminum using self-pierce riveting[J]. Mater Des,2007,28(8):2361. 3 Lu Yi, He Xiaocong, Wang Yifeng, et al. Effect of local heat treatment on the mechanical properties of steel-titanium self-piercing riveted joints[J]. Mater Rev:Res,2015,29(5):120(in Chinese). 卢毅, 何晓聪, 王医锋, 等. 局部热处理对钢-钛自冲铆接头力学性能的影响[J]. 材料导报:研究篇,2015,29(5):120. 4 Zhou Changrong, Pan Qinglin, Zhu Chaoming,et al. Development and study of new types aluminum-lithium alloys[J]. Mater Rev,2004,18(5):30(in Chinese). 周昌荣, 潘青林, 朱朝明, 等. 新型铝锂合金的研究和发展[J]. 材料导报,2004,18(5):30. 5 He Xiaocong, Zhao Lun, Deng Chengjiang, et al. Self-piercing riveting of similar and dissimilar metal sheets of aluminum alloy and copper alloy[J]. Mater Des,2015,65:923 6 Zhao Lun, He Xiaocong, Xing Baoying, et al. Influence of sheet thickness on fatigue behavior and fretting of self-piercing riveted joints in aluminum alloy 5052[J]. Mater Des,2015,87:1010. 7 He Xiaocong. An approximate method via coefficient of variation for strength prediction of self-piercing riveted joints[C]//Applied Mechanics and Materials. Luoyang, China,2010:334. 8 Se-Hyung kang, Ho-Kyung Kim. Fatigue strength evaluation of self-piercing riveted Al-5052 joints under different specimen configurations[J]. Int J Fatigue,2015,80:58. 9 Xing Baoying, He Xiaocong, Wang Yuqi, et al. Static mechanical properties and failure mechanism of self-piercing riveted aluminum alloy joint[J]. Trans China Welding Institution,2016,37(6):47(in Chinese). 邢保英, 何晓聪, 王玉奇, 等. 铝合金自冲铆接头疲劳性能及失效机理[J]. 焊接学报,2016,37(6):47. 10 Karbhari V M, Wang Q. Influence of triaxial braid denier on ribbon-based fiber reinforced dental composites [J]. Dental Mater,2007,23(8):969. 11 何明鉴. 机械构件的微动疲劳[M]. 北京:国防工业出版社,1994:33. 12 Zhao Lun, He Xiaocong, Lu Yi, et al. Mechanism of fretting fatigue damage on single-lap self-piercing riveted joints of 5052 aluminum alloy[J]. Hot Working Technol,2016,45(5):16(in Chinese). 赵伦, 何晓聪, 卢毅, 等. 5052铝合金单搭自冲铆接头微动疲劳损伤机理研究[J]. 热加工工艺,2016,45(5):16. 13 熊峻江. 疲劳断裂可靠性工程学[M]. 北京:国防工业出版社,2008:4. 14 钟群鹏, 赵子华. 断口学[M]. 北京:高等教育出版社,2006:200.
渝公网安备50019002502923号 版权所有：《材料导报》编辑部
2017, Vol. 31 