SMA490BW钢对接接头高周疲劳性能的机理探究

doi:10.11896/j.issn.1005-023X.2018.12.013

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (4527KB)
Export: BibTeX | EndNote (RIS)

Abstract The influences of stress concentration, grain refinement and residual stress on the high cycle fatigue of SMA490BW steel butt joints were systematically analyzed by the comparative fatigue test, and the dominant factor was obtained. The fatigue fracture morphology observation was conducted through a scanning electron microscope to determine failure modes of the welded joints with and without ultrasonic impact treatment (UIT). The results showed that both UIT and mechanical polishing treatment could improve the specimen’s fatigue life to certain extents. And eliminating the weld reinforcement will lead to a remarkable promotion of welded joint’s fatigue life (nearly 100 times larger) compared with the original welded joints. It can be concluded that the contribution ratios of stress concentration, grain refinement and residual compressive stress on the life extension of the welded joint are about 58%,29% and 13%, respectively. The fatigue failure of welded joints mostly comes from the surface of weld toe, and the fatigue crack initiation position shift to the internal defect after UIT.

Key words： ultrasonic impact treatment (UIT) high cycle fatigue residual stress grain refinement stress concentration failure mechanism

Published: 20 July 2018

CLC number:

TG113

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HE Bolin
	JIN Hui
	ZHANG Zhisen
	XIE Xuetao
	DING Jianghao

Cite this article:

HE Bolin,JIN Hui,ZHANG Zhisen, et al. Mechanism of Improving the High Cycle Fatigue Property of SMA490BW Steel Butt Joint[J]. Materials Reports, 2018, 32(12): 2008-2014.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.12.013 OR http://www.mater-rep.com/EN/Y2018/V32/I12/2008

1 Shen Caiyu. Fatigue strength analysis of the welded bogie frame for railway vehicle[D]. Chengdu: Southwest Jiaotong University,2014(in Chinese).
沈彩瑜.铁道车辆转向架构架疲劳强度研究[D].成都:西南交通大学,2014.
2 Ding Ran. Study on fatigue reliability of welded bogie frame for high-speed railway under uncertainties[D]. Chengdu: University of Electronic Science and Technology of China,2013(in Chinese).
丁然.认知不确定性下高速铁道客车转向架焊接构架疲劳可靠性研究[D].成都:电子科技大学,2013.
3 He Bolin, Zhang Zhisen, Xie Xuetao, et al. Influence of loading environment on ultra-high-cycle fatigue of alloy material[J]. Journal of East China Jiaotong University,2016,33(5):51(in Chinese).
何柏林,张枝森,谢学涛,等.加载环境对合金超高周疲劳行为的影响[J].华东交通大学学报,2016,33(5):51.
4 Hong Youshi, Liu Xiaolong, Lei Zhengqiang, et al. The formation mechanism of characteristic region at crack initiation for very-high-cycle fatigue of high-strength steels[J]. International Journal of Fatigue,2016,89:108.
5 Crupi V, Epasto G, Guglielmino E, et al. Analysis of temperature and fracture surface of AISI4140 steel in very high cycle fatigue regime[J]. Theoretical and Applied Fracture Mechanics,2015,80:22.
6 Hui Weijun, Zhang Yongjian, Zhao Xiaoli. Very high cycle fatigue properties of Cr-Mo low alloy steel containing V-rich MC type carbides[J]. Materials Science & Engineering A,2016,651:311.
7 Lv Zongmin, He Bolin, Yu Yingxia. Influence of ultrasonic impact on the very high cycle fatigue properties of welded cross joint for high-speed train bogie[J]. Materials Review B: Research Papers,2017,31(10):77(in Chinese).
吕宗敏,何柏林,于影霞.超声冲击对高速列车转向架焊接十字接头超高周疲劳性能的影响[J].材料导报:研究篇,2017,31(10):77.
8 Teng Chengxin, Zuo Song, Zhao Kun, et al. Progress in surface modification of welded joints[J]. Surface Technology,2014,43(4):149(in Chinese).
滕诚信,左松,赵琨,等.焊接接头表面改性的研究进展[J].表面技术,2014,43(4):149.
9 Wei Guangqian, et al. Analysis of the reasons welded metal structure failure and preventive measures[J]. Modern Manufacturing Technology and Equipment,2016(4):119(in Chinese).
韦广前,等.基于金属结构件焊接失效的原因分析及预防措施[J].现代制造技术与装备,2016(4):119.
10 Wang Dongpo, Gong Baoming, Wu Shipin, et al. Research review on fatigue life improvement of welding joint and structure[J]. Journal of East China Jiaotong University,2016,33(6):1(in Chinese).
王东坡,龚宝明,吴世品,等.焊接接头与结构疲劳延寿技术研究进展综述[J].华东交通大学学报,2016,33(6):1.
11 Wang Guiyang, Wang Haidou, Zhang Yubo, et al. Development of research in improving fatigue properties of welded joints by ultraso-nic impact treatment[J]. Materials Review A: Review Papers,2016,30(5):87(in Chinese).
王桂阳,王海斗,张玉波,等.超声冲击法提高焊接接头疲劳特性研究进展[J].材料导报:综述篇,2016,30(5):87.
12 He Bolin, Yu Yingxia, Yu Huanghuang, et al. Grain refining mec-hanism and fatigue properties of bogie welded cruciform joints treated by ultraso-nic impact[J]. Current Nanoscience,2012,8(1):17.
13 He Bolin, Yu Yingxia, Liu Jing, et al. Research about the effect of ultrasonic impact on the fatigue property of cruciform joint of 16MnR steel[J]. Rare Metal Materials and Engineering,2012,41(S1):283.
14 He Bolin, Deng Haipeng, Jiang Mingming, et al. Effect of ultraso-nic impact treatment on the ultra high cycle fatigue properties of SMA490BW steel welded joints[J]. International Journal of Advanced Manufacturing Technology,2018,96:1571.