蒸养温度效应及其对水泥基材料热伤损的影响<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.023.025

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2001KB)
Export: BibTeX | EndNote (RIS)

Abstract The temperature change of cement-based material in moist-curing and steam-curing were measured by temperature sensors. The evolutions of hydration products and microstructure were investigated by means of XRD, SEM, TGA and MIP. Results show that in the steam-curing process, temperature of specimen surface increases first. At the end of temperature increasing, surface temperature is about 30 ℃ higher than the internal temperature. Afterwards, the internal temperature increasing exceeds the surface. Internal temperature is about 25 ℃ higher than surface after constant temperature(60 ℃) curing for 3 hours. The change of temperature and time exerts limited effects on the formation of hydration products, but it brings about remarkable influence on pore structure and microtopography on surface layer. At the end of steam-curing, the total porosity and harmful pore ratio with diameter larger than 200 nm in surface layer are 1.22 and 10.3 times of that of internal structure. The total porosity is reduced effectively in moist-curing at 28 d. However, the pore ratio with diameter greater than 200 nm is still 1.6 times of moist-curing specimens.

Key words： steam-curing concrete temperature microstructure porosity heat damage

Published: 08 May 2018

CLC number:

TU528

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	MA Kunlin
	HE Jionghuang
	LONG Guangcheng
	DANG Hanfei
	XIE Youjun

Cite this article:

MA Kunlin,HE Jionghuang,LONG Guangcheng, et al. Steam-curing Temperature Effect and Its Influence on Heat Damage of Cement-based Material[J]. Materials Reports, 2017, 31(23): 171-176.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.023.025 OR http://www.mater-rep.com/EN/Y2017/V31/I23/171

1 Kjellsen K O, Detwiler R J, Gj rv O E. Pore structure of plain cement pastes hydration at different temperatures[J]. Cem Concr Res, 1990, 20(6):927.
2 Kjellsen K O, Detwiler R J, Gjr v O E. Development of microstructures in plain cement pastes hydrated at different temperatures[J]. Cem Concr Res, 1991, 21(1):179.
3 Escalante-Garc a J I, Sharp J H. Effect of temperature on the hydration of the main clinker phases in portland cements: Part I, neat cements[J]. Cem Concr Res,1998, 28(9):1245.
4 Paul M, Glasser F. Impact of prolonged warm (85 ℃) moist cure on portland cement paste[J]. Cem Concr Res, 2000, 30(12):1869.
5 Gallucci E, Zhang X, Scrivener K L. Effect of temperature on the microstructure of calcium silicate hydrate (C-S-H)[J]. Cem Concr Res, 2013, 53(2):185.
6 Zhang Ziming, Zhou Hongjun, Zhao Jikun. Influences of temperature on strength of concrete[J]. J Hohai University( Natural Sciences), 2004(6):674(in Chinese).
张子明,周红军,赵吉坤. 温度对混凝土强度的影响[J].河海大学学报(自然科学版),2004(6):674.
7 Tang Kefeng, Liu Tao. Effect of high temperature curing on compressive strength of concrete[J]. J Build Mater, 2006(4):473(in Chinese).
谭克锋,刘涛. 早期高温养护对混凝土抗压强度的影响[J]. 建筑材料学报, 2006(4):473.
8 Bazant Z P, Najjar L J. Nonlinear water diffusion in nonsaturated concrete[J]. Materi Struct, 1972, 5(1):3.
9 Ayano T, Wittmann F H. Drying, moisture distribution, and shrinkage of cement-based materials[J]. Mater Struct, 2002, 35(247):134.
10 Zhang Zhibo, Zhang Jun. Experimental study on relationship between shrinkage strain and environmental humidity of concrete[J]. J Build Mater, 2006(6):720(in Chinese).
张智博,张君. 混凝土收缩与环境湿度的关系研究[J]. 建筑材料学报,2006(6):720.
11 Huang Yu, Qi Kun, Zhang Jun. Development of internal humidity in concrete at early ages[J]. J Tsinghua University (Sci Technol), 2007(3):309(in Chinese).
黄瑜,祁锟,张君. 早龄期混凝土内部湿度发展特征[J].清华大学学报(自然科学版),2007(3):309.
12 Gao Yuan, Zhang Jun, Hou Dongwei. Calculation of moisture induced stresses and evaluation of cracking risk in early-age concrete[J]. Eng Mech, 2012,29(2):121(in Chinese).
高原,张君,侯东伟. 早龄期混凝土湿度应力计算与开裂风险评估[J]. 工程力学, 2012,29(2):121.
13 He Zhimin, Long Guangcheng, Xie Youjun, et al. Water sorptivity of steam curing concrete[J]. J Build Mater, 2012(2):190(in Chinese).
贺智敏,龙广成,谢友均,等. 蒸养混凝土的毛细吸水特性研究[J]. 建筑材料学报,2012(2):190.
14 He Zhimin, Long Guangcheng, Xie Youjun, et al. Surface layer degradation effect of steam-cured concrete[J]. J Build Mater, 2014(6):994(in Chinese).
贺智敏,龙广成,谢友均,等. 蒸养混凝土的表层伤损效应[J]. 建筑材料学报, 2014(6):994.
15 Ma Kunlin, Long Guangcheng, Xie Youjun. A real case of steam-sured concrete track slab premature deterioration due to ASR and DEF[J]. Case Studies Constr Mater, 2017, 6:63.
16 Xiong Rongrong, Long Guangcheng, Xie Youjun, et al. Influence of mineral admixtures on compressive strength and pore structure of steam-cured high-strength cement paste[J]. J Chin Ceram Soc, 2017,45(2):175(in Chinese).
熊蓉蓉,龙广成,谢友均,等. 矿物掺合料对蒸养高强浆体抗压强度及孔结构的影响[J].硅酸盐学报,2017,45(2):175.