弱碱环境下硅灰复合硅酸盐胶凝材料体系硫酸盐侵蚀产物

doi:10.11896/j.issn.1005-023X.2017.024.006

Abstract
Figure/Table
References
Related Citation (4)

Download:

Full Text ( PDF ) (546KB)
Export: BibTeX | EndNote (RIS)

Abstract The composite silicate cementing systems with 0%, 5% and 10% (mass fraction) cement replacement ratio by silica fume were immersed in 10% (mass fraction) sodium sulfate and weak alkaline solution for 210 d, the attack products and contents were studied. The attack products were characterized by XRD, SEM and EDS. The contents of gypsum in composite silicate cementing system with silica fume were calculated by using K value, the contents of free and total sulfate ion in composite silicate cementing system with silica fume were determined by spectrophotometry. The results show that the main attack products of composite silicate cementing system with silica fume are gypsum and ettringite in 10% sodium sulfate and weak alkaline solution, and the formation of attack products causes the specimen to expand and crack. The contents of free and total sulfate ion and the attack product in composite silicate cementing system with silica fume obviously decrease, and the expansion rates decrease with the increase of silica fume. Silica fume has a certain improvement effect on the expansion of composite silicate cementing system with silica fume.

Key words： weak alkaline sodium sulfate Portland cement silica fume attack product

Published: 08 May 2018

CLC number:

TB321

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LI Yan
	YANG Xuguang
	SUN Daosheng
	WANG Aiguo
	LIU Kaiwei

Cite this article:

LI Yan,YANG Xuguang,SUN Daosheng, et al. Sulfate Attack Product of Composite Silicate Cementing System with Silica Fume in Weak Alkaline[J]. Materials Reports, 2017, 31(24): 26-29.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.024.006 OR http://www.mater-rep.com/EN/Y2017/V31/I24/26

1 吴中伟, 廉慧珍. 高性能混凝土[M]. 北京:中国铁道出版社,1999.
2 Qiao Hongxia, He Zhongmao, Liu Cuilan. Dynamic elastic modulus and microstructure study of concrete in sulfate environment[J]. J Harbin Institute of Technology, 2008,34(4):452(in Chinese).
乔宏霞, 何忠茂, 刘翠兰. 硫酸盐环境混凝土动弹性模量及微观研究[J]. 哈尔滨工业大学学报, 2008,34(4):452.
3 Jin Yannan, Zhou Shuangxi. Types and mechanism of concrete sulfate attack[J]. J East China Jiaotong University, 2006,23(5):4(in Chinese).
金雁南, 周双喜. 混凝土硫酸盐侵蚀的类型及作用机理[J]. 华东交通大学学报, 2006,23(5):4.
4 Tian B, Cohen M D. Does gypsum formation during sulfate attack on concrete lead to expansion?[J]. Cem Concr Res, 2000,30(1):117.
5 Wu Meng, Ji Yongsheng, Zhan Guangmei, et al. Mechanism study on red mud geopolymer to sulfate attack at low temperature[J]. Mater Rev: Res, 2016,30(9):112(in Chinese).
吴萌, 姬永生, 展光美,等. 低温环境下赤泥地聚合物抗硫酸盐侵蚀机理研究[J]. 材料导报:研究篇, 2016,30(9):122.
6 Neville A. The confused world of sulfate attack on concrete[J]. Cem Concr Res, 2004,34(8):1275.
7 Omar S. Baghab ra Al-Amoudi. Attack on plain and blended cements exposed to aggressive sulfate environments[J]. Cem Concr Compos, 2002,24:305.
8 Raphaёl Tixier. Modeling of damage in cement-based materials subjected to external sulphate attackⅡ: Comparision with experiments[J]. J Mater Civil Eng, 2003,15(4):314.
9 Xi Yaozhong. Recent progress in cement chemistry—Notes on the 9^th international congress on the chemistry of cement[J]. J Chin Ceram Soc, 1993,21(6):577(in Chinese).
席耀中. 近年来水泥化学新进展——第九届国际水泥化学会议[J]. 硅酸盐学报, 1993,21(6):577.
10Liang Yongning, Yuan Yingshu. The effect of sulfate as an environmental factor on the concrete deterioration: Remarked on the present research[J]. Concrete, 2005(3):27(in Chinese).
梁咏宁, 袁迎曙. 硫酸盐侵蚀环境因素对混凝土性能的影响——研究现状综述[J]. 混凝土,2005(3):27.
11Zhang Shuyuan. Corrosion mechanism of concrete subjected to sulfate salt in complex environment[D]. Qingdao: Qingdao Technological University, 2014(in Chinese).
张淑媛. 复杂环境下混凝土硫酸盐侵蚀机理[D]. 青岛:青岛理工大学, 2014.
12Feng Lingyun. Influence of silica fume and water reducer on resistance to sulfate attack of cement[J]. J Southwest Jiaotong University, 1988,69(3):1(in Chinese).
凤凌云. 硅灰和减水剂对水泥耐硫酸盐腐蚀的影响[J].西南交通大学学报, 1988,69(3):1.
13Xiao Jia, Deng Dehua, Yuan Qiang, et al. Improvement effect of silica fume on the cement paste in sulfate attack[J]. J Southwest Petroleum Institute, 2006,28(3):103(in Chinese).
肖佳,邓德华,元强,等.硅灰对水泥净浆抗硫酸盐侵蚀性能的改善作用[J]. 西南石油学院学报, 2006,28(3):103.
14Li Yuhua. Using K value method with X-ray in quantitative analysis of cement physical phases[J]. Cem Eng, 2001(3):34(in Chinese).
李玉华. 用X射线K值法定量分析水泥物相[J]. 水泥工程, 2001(3):34.
15Yuan Ke, Liao Libing, Wan Hongbo, et al. Quantitative analysis of cristobalite and α-quartz in bentonite by X-ray powder diffraction-comparison between external standard and K-value method[J]. J Chin Ceram Soc, 2011,39(2):377(in Chinese).
袁珂, 廖立兵, 万红波,等. 膨润土中方石英和α-石英的定量相分析-X射线衍射外标法和K值法的对比[J]. 硅酸盐学报, 2011, 39(2):377.