晶粒组织对Al-Zn-Mg合金力学性能和腐蚀性能的影响

doi:10.11896/cldb.22050211

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (30974KB)
Export: BibTeX | EndNote (RIS)

Abstract Taking Al-Zn-Mg alloys with two different grain structures, recrystallized and fibrous as the research object, through room temperature tensile, exfoliation corrosion, slow strain rate tensile, four-point bending tests, the effects of grain structure on the mechanical properties and corrosion properties of the alloy were investigated by OM, TEM, SEM and EBSD. The results showed that:compared with the recrystallized structure alloy, the yield strength of the fiber-structured alloy was increased by 24.7 MPa and the tensile strength was increased by 56 MPa, the tensile strength and elongation loss rate in the slow strain rate tensile test were 65.2% and 80.3% lower than those of the recrystallized alloy, and the stress corrosion index was reduced by 75.5%, the time to fracture during the four-point bending test was 57 times longer than that of recrystallized alloys, compared with the recrystallized structure alloy, the maximum corrosion depth of exfoliation corrosion of the fiber structure alloy was increased by 160.4%. The improvement of the mechanical properties of the alloy with fibrous structure was mainly due to the grain refinement strengthening effect, and the improvement of the stress corrosion resistance was mainly due to its lower recrystallization fraction and lower proportion of high-angle grain boundaries.

Key words： Al-Zn-Mg grain structure mechanical property corrosion property

Published: 10 October 2023 Online: 2023-09-28

CLC number:

TG146.2

Fund:Henan Key Laboratory of Fastening Connection Technology (JGLJ2103) and the National Key Research and Deve-lopment Program of China(2016YFB0300901).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Pengyu
	YE Lingying
	KE Bin
	HU Tianjiao
	DONG Yu
	LIU Shengdan

Cite this article:

WANG Pengyu,YE Lingying,KE Bin, et al. Effect of Grain Structure on Mechanical and Corrosion Properties of Al-Zn-Mg Alloy[J]. Materials Reports, 2023, 37(19): 22050211-7.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22050211 OR http://www.mater-rep.com/EN/Y2023/V37/I19/22050211

1 Li H, Cao F, Guo S, et al, Journal of Alloys and Compounds, 2017, 719, 89.
2 Zander D, Schnatterer C, Altenbach C, et al. Material & Design, 2015, 83, 49.
3 Schnatterer C, Bulinager A, Zander D. Materials and Corrosion, 2016, 67(12), 1308.
4 Geertruyden W H V, Browne H M, Misiolek W Z, et al. Metallurgical & Materials Transactions A, 2005, 36(4), 1049.
5 Liu C M. Processing of nonferrous metals, Central South University Press, China, 2010, pp. 66(in Chinese).
刘楚明. 有色金属材料加工, 中南大学出版社, 2010, pp. 66.
6 Chen S Y, Chen K H, Dong P X, et al. Transactions of Nonferrous Metals Society of China, 2013(2), 329 (in Chinese).
陈送义, 陈康华, 董朋轩, 等. 中国有色金属学报, 2013(2), 329.
7 GB/T 22639-2008. Test method for exfoliation corrosion for wrought aluminum and aluminum alloys, Standards Press of China, China, 2008(in Chinese).
GB/T 22639-2008. 铝合金加工产品的剥落腐蚀实验方法, 中国标准出版社, 2008.
8 Sun Z X, Peng G S, Chen K H, et al. Powder Metallurgy Materials Science and Engineering, 2012(3), 297(in Chinese).
孙兆霞, 彭国胜, 陈康华, 等. 粉末冶金材料科学与工程, 2012(3), 297.
9 Chen K H, Chen S Y, Peng G. Special Casting and Nonferrous Alloys, 2010(2), 103(in Chinese).
陈康华, 陈送义, 彭国胜, 等. 特种铸造及有色合金, 2010(2), 103.
10 Liu W J, Zhang X M, Liu S D, et al. Transactions of Nonferrous Metals Society of China, 2010(6), 1102 (in Chinese).
刘文军, 张新明, 刘胜胆, 等. 中国有色金属学报, 2010(6), 1102.
11 Ye L Y, Yao X B, Tang J G, et al. Journal of Central South University (Science and Technology), 2019, 50(5), 1049(in Chinese).
叶凌英, 姚学彬, 唐建国, 等. 中南大学学报, 2019, 50(5), 1049.
12 Chai W R, Chen J C, Liu S D, et al. Journal of Materials Research, 2019, 33(7), 489(in Chinese).
柴文茹, 陈景超, 刘胜胆, 等. 材料研究学报, 2019, 33(7), 489.
13 Ding Q W, Zhang D, Yan Y, et al. Corrosion Science, 2020, 169, 108622.
14 Li Z M, Jiang H C, Wang Y L, et al. Journal of Materials Science and Technology, 2018, 34(7), 1172.
15 Wu P P, Tian A Q, Duan H W, et al. Failture Analysis and Prevention, 2016(1), 6(in Chinese).
吴沛沛, 田爱琴, 段浩伟, 等. 失效分析与预防, 2016(1), 6.
16 Shen P Y, Tang J G, Ye L Y, et al. Chinese Journal of Materials Reserch, 2018, 32(10), 751(in Chinese).
申澎洋, 唐建国, 叶凌英, 等. 材料研究学报, 2018, 32(10), 751.
17 Qu M, Tang J G, Ye L Y, et al. Marerials Repeots, 2020, 34(1), 2083(in Chinese).
瞿猛, 唐建国, 叶凌英, 等. 材料导报, 2020, 34(1), 2083.
18 Sinyavskii V S, Ulanova V V, Kalinin V D. Protection of Metals, 2004, 40(5), 481.
19 Yu X W. Relationship between three-dimensional microstructure and properties of deformation-aging Al-Zn-Mg-Cu aluminum alloy. Ph. D. Thesis, Hunan University, China, 2020 (in Chinese).
余雄伟. 形变时效Al-Zn-Mg-Cu铝合金三维微观结构与性能关系研究. 博士学位论文, 湖南大学, 2020.
20 Senkov O N, Shagiev M R, Senkova S V, et al. Acta Materialia, 2008, 56, 3723.
21 Bailey J E, Hirsch P B. Philosophical Magazine, 1960, 5(53), 485.
22 Liao W B, Liu X Y, Liu S D, et al. Journal of Central South University (Natural Science Edition), 2012, 46(6), 2137(in Chinese).
廖文博, 刘心宇, 刘胜胆, 等. 中南大学学报(自然科学版), 2012, 46(6), 2137.
23 He C H, Li H P, Ye L Y, et al. Marerials Repeots, 2021, 35(22), 22109(in Chinese).
贺春花, 李红萍, 叶凌英, 等. 材料导报, 2021, 35(22), 22109.
24 Fang H, Chao H, Chen K. Journal of Alloys and Compounds, 2015, 622, 166.
25 Sinyavskii V. Protection of Metals, 2004, 40(5), 481.
26 Chen M, Deng Y, et al. Materials Characterization, 2019, 148, 259.