| POLYMERS AND POLYMER MATRIX COMPOSITES |
|
|
|
|
|
| Absorption, Desorption and Re-swelling Behavior of Superabsorbent Polymers in Cementitious Materials: a Review |
| YANG Haitao1,2, BIAN Hongjian1,2, LIU Juanhong3,*
|
1 Key Laboratory of Roads and Railway Engineering Safety Control, Ministry of Education, Shijiazhuang Tiedao University, Shijiazhuang 050043, China
2 School of Civil Engineering, Shijiazhuang Tiedao University, Shijiazhuang 050043, China
3 College of Civil and Resource Engineering, University of Science and Technology, Beijing 100083, China |
|
|
|
|
Abstract Cracks and the reduction of water tightness after cracking are the important factors leading to the decrease of durability of cementitious mate-rials. Superabsorbent polymers (SAP) can relieve the self-shrinkage and improve the freeze-thaw resistance, impermeability after cracking, and self-healing ability of cementitious materials. The above functions of SAP rely on its absorption, desorption and re-swelling behavior in cementitious materials. In this paper, the mechanism of the absorption and desorption of SAP and its key influencing factors were first summarized. Then, the evolution mechanism of the re-swelling behavior of SAP in cracks was reviewed. In solutions, the osmotic pressure between the gel and solutions is the driving force for SAP swelling. Ca2+, as the key ion, can complex with the carboxyl group on the polymer chains and increase the ionic crosslinking density of SAP. A high ionic crosslinking density will produce a reverse osmotic pressure and induce the desorption of SAP. In cementitious materials, the key factors influencing the desorption rate of SAP are osmotic pressure and capillary force. Reducing the desorption under osmotic pressure and improving the desorption under capillary force can enhance the internal curing efficiency of SAP. Compared with AA SAP, AA-co-AM SAP has a more excellent internal curing effect due to its stronger water restraint ability. The re-swelling capacity of SAP in cracks of cementitious materials is lower than that in solutions, because the restraint effect of cracks and the high ion concentration in cracks inhibit the re-swelling of SAP. Designing new SAP based on the crack characteristics, mix designs and hydration process of cementitious materials may help to enhance the application effect of SAP.
|
|
Published: 25 February 2023
Online: 2023-03-02
|
|
|
| Fund:Natural Science Foundation of Hebei Province (E2021210003) and National Natural Science Foundation of China (52208278). |
|
|
1 Cheng Y, Zhang Y, Jiao Y, et al. Construction and Building Materials, 2016,129, 106.
2 Berrocal C G, Lundgren K, Löfgren I. Cement and Concrete Research, 2016,80, 69.
3 Mignon A, De Belie N, Dubruel P, et al. European Polymer Journal, 2019, 117, 165.
4 Mignon A, Snoeck D, Dubruel P, et al. Materials, 2017, 10(3), 237.
5 Lee H X D, Wong H S, Buenfeld N R. Cement and Concrete Composites, 2018, 88, 150.
6 Snoeck D, Pel L, De Belie N. Scientific Reports, 2017, 7(1), 1.
7 Kang S, Hong S, Moon J. Cement and Concrete Research, 2018, 108, 20.
8 Mo J, Ou Z, Zhao X, et al. Construction and Building Materials, 2017, 146, 283.
9 Snoeck D, Jensen O M, De Belie N. Cement and Concrete Research, 2015, 74, 59.
10 Zhong P, Wyrzykowski M, Toropovs N, et al. Cement and Concrete Research, 2019, 123, 105789.
11 Van Tittelboom K, Wang J, Araújo M, et al. Construction and Building Materials, 2016, 107, 125.
12 Laustsen S, Hasholt M T, Jensen O M. Materials and Structures, 2015, 48(1-2), 357.
13 Mechtcherine V, Schröfl C, Wyrzykowski M, et al. Materials and Structures, 2017, 50(1), 14.
14 Snoeck D, Steuperaert S, Van Tittelboom K, et al. Cement and Concrete Research, 2012, 42(8), 1113.
15 Hong G, Choi S. Construction and Building Materials, 2017, 143, 366.
16 Lee H X D, Wong H S, Buenfeld N R. Cement and Concrete Research, 2016, 79, 194.
17 Rodríguez C R, Figueiredo S C, Deprez M, et al. Cement and Concrete Composites, 2019, 104, 103395.
18 Snoeck D, Van Tittelboom K, Steuperaert S, et al. Journal of Intelligent Material Systems and Structures, 2013, 25(1), 13.
19 Deng H, Liao G. Construction and Building Materials, 2018, 170, 455.
20 Snoeck D, Van den Heede P, Van Mullem T, et al. Cement and Concrete Research, 2018, 113, 86.
21 Mechtcherine V, Reinhardt H W. Application of superabsorbent polymers in concrete construction, Springer, Heidelberg, 2012, pp.58.
22 Mechtcherine V, Secrieru E, Schröfl C. Cement and Concrete Research, 2015, 67, 52.
23 Kang S, Hong S, Moon J. Cement and Concrete Composites, 2018, 88, 64.
24 Yun K, Kim K, Choi W, et al. Polymers, 2017, 9(11), 600.
25 Siriwatwechakul W, Siramanont J, Vichit-Vadakan W. Journal of Materials in Civil Engineering, 2012, 24(8), 976.
26 Ma X, Yuan Q, Liu J, et al. Construction and Building Materials, 2019, 195, 66.
27 Esteves L P. Cement and Concrete Composites, 2011, 33(7), 717.
28 Liu H, Bu Y, Sanjayan J G, et al. Construction and Building Materials, 2016, 112, 253.
29 Ashkani M, Bouhendi H, Kabiri K, et al. Construction and Building Materials, 2019, 206, 540.
30 Pourjavadi A, Fakoorpoor S M, Hosseini P, et al. Cement and Concrete Composites, 2013, 37, 196.
31 Schroefl C, Mechtcherine V, Vontobel P, et al. Cement and Concrete Research, 2015, 75, 1.
32 Yang J, Wang F, Liu Z, et al. Cement and Concrete Research, 2019, 118, 25.
33 Yang H, Liu J, Jia X, et al. Construction and Building Materials, 2020, 243, 118228.
34 Kang S, Hong S, Moon J. Cement and Concrete Research, 2017, 97, 73.
35 Riyazi S, Kevern J T, Mulheron M. Construction and Building Materials, 2017, 147, 669.
36 Wyrzykowski M, Lura P, Pesavento F, et al. Cement and Concrete Research, 2011, 41(12), 1349.
37 Farzanian K, Ghahremaninezhad A. Materials and Structures, 2017, 50(5), 216.
38 Farzanian K, Ghahremaninezhad A. Materials and Structures, 2018, 51(1), 3.
39 Wang F, Yang J, Cheng H, et al. ACI Materials Journal, 2015, 112(3), 463.
40 Yang H, Liu J, Zhou Q, et al. Materials and Structures, 2019, 52(5), 103.
41 Hong G, Choi S. Construction and Building Materials, 2018, 164, 570.
42 Hong G, Song C, Park J, et al. Construction and Building Materials, 2019, 195, 187. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2023, Vol. 37 