N-异丙基丙烯酰胺-丙烯酸钠共聚包覆四氧化三铁温敏磁性吸水树脂的制备与表征<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.020.007

Abstract
Figure/Table
References
Related Citation (1)

Download:

Full Text ( PDF ) (1371KB)
Export: BibTeX | EndNote (RIS)

Abstract A temperature-sensitive, magnetic, and water-absorbent resin was prepared in this work by copolymerizing N-isopropyl acrylamide and sodium acrylate to envelop the pre-synthesized Fe₃O₄ nanoparticles, in which the Fe₃O₄ magnetic nanoparticles were prepared by coprecipitation method, and the envelopment was conducted by free-radical copolymerization in aqueous system. The obtained sample was characterized by X-ray diffraction(XRD), Fourier transform infrared spectrometer(FTIR)and thermal gravimetry(TG). Based on temperature sensitivity, swelling property, and deswelling property, it can be found that the resin possesses good water absorption and temperature sensitivity, as the low critical solution temperature (LCST) and swelling ratio were 50 ℃ and 116.74 g/g, respectively, and water loss in the fine coal was 77.90% at 70 ℃ within 30 min. When the sample was fully swelled by water and treated by ultrasonication for 30 min, only a small amount of Fe₃O₄ was removed, illuminating a relatively stable magnetic property.

Key words： sodium acrylate N-isopropylacrylamide Fe₃O₄ nanoparticles temperature-sensitive magnetic and water-absor-bent resin

Published: 05 May 2018

CLC number:

TD94

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CHEN Hangchao
	ZHANG Suhong
	LIU Shengyu
	ZHANG Zhiqiang
	GUO Jianying

Cite this article:

CHEN Hangchao,ZHANG Suhong,LIU Shengyu, et al. Preparation and Characterization of a Temperature-sensitive, Magnetic, Water-absorbent Resin Comprising Fe₃O₄ Nanoparticles and Poly(N-isopropylacrylamide-co-sodium acrylate) Envelope[J]. Materials Reports, 2017, 31(20): 30-34.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.020.007 OR http://www.mater-rep.com/EN/Y2017/V31/I20/30

1 Schild H G, Tirrell D A. Interaction of poly(N-isopropylacrylamide) with sodium n-alkyl sulfates in aqueous solution[J]. Langmiur, 1991,7(4):665.
2 Wu C, Zhou S Q. Laser light-scattering study of the phase transition of poly(N-isopropylacrylamide) in water.I.single chain[J]. Macromolecules, 1995,28(24):8381.
3 Hu Y Q, Quan C M, Liu H N, et al. Review on thermo-responsive adsorbent material[J].Mater Rev: Rev, 2016,30(6):126(in Chinese).
胡耀强,权朝明,刘海宁,等. 温敏材料吸附研究进展[J]. 材料导报:综述篇, 2016,30(6):126.
4 Wei W, Hu X Y, Qi X L, et al. A novel thermo-responsive hydrogel based on salecan and poly(N-isopropylacrylamide):Synthesis and characterization[J]. Colloids Surf B:Biointerfaces, 2015,125(9):1.
5 Manek E, Domján A, Madarász J, et al. Interactions in aromatic probe molecule loaded poly(N-isopropylacrylamide) hydrogels and implications for drug delivery[J]. Eur Polym J, 2015,68:657.
6 Bai H H, Zhang Q S, He T, et al. Adsorption dynamics,diffusion and isotherm models of poly(NIPAm/LMSH) nanocomposite hydrogels for the removal of anionic dye amaranth from an aqueous solution[J]. Appl Clay Sci, 2016,124-125:157.
7 Mahida V P, Patel M P. Removal of some most hazardous cationic dyes using novel poly(NIPAAm/AA/N-allylisatin) nanohydrogel[J]. Arabian J Chem, 2016,9(3):430.
8 Nakayama M, Okano T. Polymer terminal group effects on properties of thermoresponsive polymeric micelles with controlled outer-shell chain lengths[J]. Biomacromolecules, 2005,6(4):2320.
9 Kim S, Healy K E. Synthesis and characterization of injectable poly(N-isopropyl acrylamide-co-acrylic acid) hydrogels with proteolytically degradable cross-links[J]. Biomacromolecules, 2003,4(5):1214.
10Pu H T, Ding Z L, Ma R D. Effect of hydrophilic monomers on the thermosensitivity of eva preirradiated NIPAAm[J]. Polym Mater Sci Eng, 1997,13(9):79(in Chinese).
浦鸿汀, 丁中立, 马瑞德. EVA-g-NIPAAm中接枝链亲水性对热敏性的影响[J]. 高分子材料科学与工程, 1997,13(9):79.
11Chen H T, Fan Y, Fang Y. Dual pH- and thermo-responsive self-assembly of the P(NIPAM-co-AA) hydrophilic random copolymer in pure aqueous solution[J]. Acta Phys-Chim Sin, 2014,30(7):1290(in Chinese).
陈韩婷, 樊晔, 方云. 全亲水无规共聚物P(NIPAM-co-AA)的pH和温度双重刺激响应性水相自组装[J]. 物理化学学报, 2014,30(7):1290.
12Zhan Y, He P X, Sun Z G, et al. Synthesis and drug loading pro-perties of dual thermo and redox sensitive P(NIPAM-AA) nanogels[J]. Chem J Chin Universities, 2015,36(12):2563(in Chinese).
詹园, 何培新, 孙争光, 等. 还原和温度双重敏感 P(NIPAM-AA)纳米凝胶的合成及载药性能[J]. 高等学校化学学报, 2015,36(12):2563.
13Klemetsrud T, Hiorth M, Smistad G, et al. Characterization of temperature induced changes in liposomes coated with poly(N-isopropylacrylamide-co-methacrylic acid)[J]. J Colloid Interface Sci, 2015,450:7.
14Liu R Q, Liang S, Jing C, et al. Synthesis and proporties of tempe-rature and pH-sensitive and Gadolinium contained polymeric magne-tic resonance imaging contrast agent[J]. Chem J Chin Universities, 2016,37(1):155(in Chinese).
刘瑞清, 梁爽, 江存, 等. 温度和 pH 敏感高分子含钆核磁共振成像造影剂的合成及性能[J]. 高等学校化学学报, 2016,37(1):155.
15Tang X B, Sun A H, Chu C Y, et al. Highly sensitive multiresponsive photonic hydrogels based on a crosslinked acrylamide-N-isopropylacrylamide (AM-NIPAM) co-polymer containing Fe₃O₄@C crystalline colloidal arrays[J]. Sensors Actuators B:Chem, 2016,236:399.
16Li Z X, Lv M G, Zhang Y F, et al. Sythesis and characterization of thermo-responsive hydrogels based on poly(N-isopropylacrylamide)/acrylamide interpenetrate networks[J]. Polym Mater Sci Eng, 2014,30(10):1(in Chinese).
李朝霞, 吕满庚, 张云飞, 等. 聚(N-异丙基丙烯酰胺)/聚丙烯酰胺互穿网络水凝胶的合成和性能[J]. 高分子材料科学与工程, 2014,30(10):1.
17Gong Y, Liu Q L, Zhu A M, et al. One-pot synthesis of poly(N-isopropylacrylamide)/chitosan composite microspheres via microemulsion[J]. Carbohydr Polym, 2012,90(1):690.
18Wang J S, Peng F, Yan F F, et al. Preparation and drug releasing property of poly(N-isopropylacrylaimde-co-N-hydroxymethyl acry-lamide)/chitosan hydrogel[J]. J Chem Eng Chin Universities, 2014,28(5):1119(in Chinese).
王进爽, 彭飞, 严芳芳, 等. 聚(异丙基丙烯酰胺-羟甲基丙烯酰胺)/壳聚糖水凝胶的制备及其释药性能[J]. 高校化学工程学报, 2014,28(5):1119.
19Li X M, Wang G H, Cheng Y. Preparation and characteristics of Fe₃O₄/BaTiO₃ heterostructural nanocomposite as photocatalyst[J]. Res Chem Intermediates, 2013,41(5):3031.
20Lu Z Y, Zhao X X, Zhu Z, et al. Enhanced recyclability,stability and selectivity of CdS/C@Fe₃O₄ nanoreactor for orientation photodegradation of ciprofloxacin[J]. Chem—A Eur J, 2015,21(51):18528.
21Sun X T, Yang L R, Li Q, et al. Polyethylenimine-functionalized poly(vinyl alcohol) magneticmicrospheres as a novel adsorbent for rapid removal of Cr(Ⅵ) from aqueous solution[J]. Chem Eng J, 2015,262:101.
22Fan H, Wang C Z, Wei Y M, Synthesis and application of boronic acid functionalized magnetic adsorben for sensitive analysis of salbutamol residues in pig tissues[J]. Biomed Chromatography, 2015,29(12):1834.
23Wu J, Liu Y, Li W, et al. Magnetically guided survivin-siRNA deliveryand simultaneous dual-modal imaging visualization based on Fe₃O₄@mTiO₂ nanospheres for breast cancer[J]. J Mater Chem B, 2014,2(44):7756.
24Chen L, Li L F, Zhang H, et al. Magnetic thermosensitive core/shell microspheres:Synthesis, characterization and performance in hyperthermia and drug delivery[J]. RSC Adv, 2014,87(4):46806.
25Zhan F, Fan J W, Li C K, et al. Hydrothermal fabrication of Fe₃O₄ nano-sized magneric particles[J]. Metall Funct Mater, 2012,19(1):20(in Chinese).
詹凤, 范君伟, 李成魁, 等. 水热法制备纳米Fe₃O₄磁性颗粒[J]. 金属功能材料, 2012,19(1):20.