INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
Investigation on Resistance of Chloride Penetration of Alkali Activated Slag Concrete and Related Electrical Test Methods |
YU Qi1,2, WAN Xiaomei1,3, ZHAO Tiejun1,3, WANG Teng1, HAN Xiao1, SUN Zhongtao1
|
1 School of Civil Engineering, Qingdao University of Technology, Qingdao 266033, Shandong,China 2 Qingdao Qingjian New Material Group Co., Ltd, Qingdao 266108, Shandong, China 3 Cooperative Innovation Center of Engineering Construction and Safety in Shandong Blue Economic Zone, Qingdao University ofTechnology, Qingdao 266033,Shandong, China |
|
|
Abstract Alternating current resistivity method, electric flux method and rapid chloride migration method (RCM) were applied to evaluatethe resistance of chloride penetration in alkali-activated slag concrete and the evolution mechanism was analyzed. At the same time, combined with the long-term exposure test of chloride environment, the applicability of the above three electrical parameters test methods to the alkali slag concrete was discussed. The results show that the slag concrete activated by sodium hydroxide behaves higher resistance to chloride penetration than the slag concrete activated by water glass. The addition of fly ash increases the porosity of alkali-activated slag concrete and weakens the ability to resist chloride penetration. There are good correlations among the evaluation results of resistivity method, electric flux method and RCM method, and all of them behave sound applicability to alkali-activated slag concrete.
|
Published: 10 March 2022
Online: 2022-03-08
|
|
Fund:National Natural Science Foundation of China (51878365) |
|
|
1 Zhao T J. Concrete Permeability, Science Press, China, 2006,pp.52(in Chinese). 赵铁军. 混凝土渗透性, 科学出版社, 2006,pp.52. 2 Loche J M, Ammar A, Dumargue P. Cement and Concrete Research, 2004, 35(9),1797. 3 Monfore G E. Journal of the PCA Research Development Laboratories, 1968,5, 35. 4 Hansen M R, Leming M L, Zia P, et al. Special Publication, 1993, 140, 121. 5 Feldman R F, Chan G W, Brousseau R J, et al. Materials Journal, 1994, 91(3), 246. 6 Lu X Y,Li C L,Chen M X, et al. China Concrete and Cement Products, 1999(5), 12(in Chinese). 路新瀛, 李翠玲, 陈美霞, 等. 混凝土与水泥制品, 1999(5), 12. 7 Han J G, Li K F. Journal of Building Materials, 2015,18(4),704(in Chinese). 韩建国, 李克非. 建筑材料学报, 2015,18(4),704. 8 Maes M, Gruyaert E, De Belie N. Materials and Structures, 2013, 46(1), 89. 9 He Z X, Shi C J, Hu X, et al. Journal of the Chinese Ceramic Society,2015, 43(8),1111(in Chinese). 何宗旭, 史才军, 胡翔, 等. 硅酸盐学报,2015,43(8),1111. 10 Hu X, Shi C J, Shi Z, et al. Cement and Concrete Composites, 2019,104,103336. 11 Kumar S, Kumar R, Mehrotra S P. Journal of Materials Science, 2010,45(3),607. 12 Bai Y Z. Investigation of mechanical performance and relationship between mechanical and microstructure characterization of alkali-activated slag. Master's Thesis, Qingdao University of Technology, China, 2016(in Chinese). 白云志. 碱激发矿渣的力学性能以及与微观表征的相关性研究. 硕士学位论文, 青岛理工大学, 2016. 13 Liu G Q. Study on mechanism of binding chloride ion in alkali-activated slag. Master's Thesis, Qingdao University of Technology, China,2018(in Chinese). 刘国强. 碱激发矿渣对氯离子的固化机制研究. 硕士学位论文,青岛理工大学, 2018. 14 Cincotto M A, Melo A A, Repette W L.In:Proceedings of the 11th International Congress on the Chemistry of Cement. Durban, South Africa,2003,pp.18781888. 15 Sun J Y, Zhu P N, Wu C H. Bulletin of the Chinese Ceramic Society, 1988(6),16(in Chinese). 孙家瑛, 诸培南, 吴初航. 硅酸盐通报,1988(6),16. 16 Zhang Y. The mechanical properties and transport properties under loa-ding of alkali-activated slag concrete. Master's Thesis, Qingdao University of Technology, China,2017(in Chinese). 张宇. 碱激发矿渣混凝土的力学性能和荷载下的传输性能. 硕士学位论文,青岛理工大学, 2017. 17 Neto A A M, Cincotto M A, Repette W. Cement & Concrete Research, 2008, 38(4), 565. 18 Shi C J. Alkali-activated cements and concretes, Chemical Industry Press, China, 2008,pp.121(in Chinese). 史才军. 碱激发水泥和混凝土, 化学工业出版社, 2008,pp.121. 19 Tuutti K. Corrosion of steel in concrete, CBE Forskning fo 4.82 (Swedish Cement and Concrete Research Institute Stockholm), Sweden, 1982. 20 Jaegermann C. ACI Materials Journal, 1990, 87(4), 333. 21 Costa A, Appleton J. Materials and Structures, 1999, 32, 252. 22 Conciatori D, Sadouki H, Brühwiler E. Cement and Concrete Research, 2008, 38,1401. 23 Polder R B, Peelen W H A. Cement and Concrete Composites, 2002, 24, 427. |
|
|
|