镁铝尖晶石固溶体成分对TiN析出行为的影响<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.08.024

Abstract
Figure/Table
References (24)
Related Citation (15)

Download:

Full Text ( PDF ) (2876KB)
Export: BibTeX | EndNote (RIS)

Abstract Through the experiment of slag/steel reaction equilibrium on 2205 duplex stainless steel, inclusions in MgO-Al₂O₃ binary solid solution were obtained with different slag compositions. When the reaction reached the equilibrium, the new complex inclusion of MgO-Al₂O₃ solid solution combined with TiN would further form if adding 0.05% Ti to the steel. After water quenching, the inclusions were analyzed by SEM, and samples were electrolyzed by oxalic acid with content of 10%. And then grain morphology and size of δ ferrite was compared to that of as-cast microstructure without Ti. The experiment results showed that the precipitation quantity increased with the increase of Al₂O₃ proportion in MgO-Al₂O₃ solid solution while the grain of as-cast δ ferrite was obviously refined. It was found that TiN precipitated rarely out of MgO-rich MgO-Al₂O₃ solid solution and MgO-Al₂O₃, and the grain refining effect of δ ferrite was not obvious. By thermodynamic calculation, heterogeneous nucleation theory and experimental result analysis, it was concluded that inclusion composition of MgO-Al₂O₃ binary solid solution was jointly determined by slag composition and activity of Mg and Al. The increase of Al₂O₃ content in MgO-Al₂O₃ solid solution contributed to the lattice distortion of MgO-Al₂O₃, which is closely associated with vacancy in the lattice. Because of the enrichment of vacancies, lattice constant e was uneven. And vacancies had changed the crystal field and caused the movement or transfer of O^2-, which led to omission solid solution of spinel. It was the energy state changes of lattice that promoted the precipitation of Ti and N atoms on the surface of MgO-Al₂O₃ inclusion.

Key words： duplex stainless steel Mg-Al spinel solid solution TiN

Published: 02 May 2018

CLC number:

TF764+.1

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	PANG Zongxu
	ZHU Rong
	CHEN Peidun
	WANG Junhai

Cite this article:

PANG Zongxu,ZHU Rong,CHEN Peidun, et al. Effect of Mg-Al Spinel Solid Solution Composition on Precipitation Behavior of TiN[J]. Materials Reports, 2017, 31(8): 118-124.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.08.024 OR http://www.mater-rep.com/EN/Y2017/V31/I8/118

1 Niagaj J,Mazur L. Ferrite content measurements in S32101 lean duplex stainless steel and its welded joints[J]. Arc Metall Mater,2012,57(3):779.
2 Ruiz A, Ortiz N, Rubio C, et al. Utilization of ultrasonic measurements for determining the variations in microstructure of thermally degraded 2205 duplex stainless steel[J]. Nondestruct Evaluation,2009,28(3):131.
3 Lv J L, Liang T X, Wang C, et al. Effect of ultrafine grain on tensile behaviour and corrosion resistance of the duplex stainless steel[J]. Mater Sci Eng,2016,62(5):558.
4 Poole W J, Mitchell A, Weinberg F. Inoculating stainless steel with titanium nitride[J]. High Temp Mater Process,2011,16(3):173.
5 Villaret V, Deschaux F, Bordreuil C. A solidification model for the columnar to equiaxed transition in welding of a Cr-Mo ferritic stainless steel with Ti as inoculant[J]. Mater Process Technol,2016,233:115.
6 Mu W, Jönsson P G, Nakajima K. Potent nucleation site and its size for the formation of intragranular ferrite in steels with Ti₂O₃ additions[C]//日本鉄鋼協会講演論文集,2015:9.
7 Shi X F, Cheng G G. Study on mechanism of TiN formation and precipitation in 430 stainless steel[J]. Steelmaking,2008,24(4):36(in Chinese).
施晓芳, 成国光. 430不锈钢中TiN的形成和析出机理研究[J]. 炼钢,2008,24(4):36.
8 Shi C X, Cheng G G, Shi C M, et al. Research on TiN nucleation solidification structure refinement of 430 ferritic stainless steel[J]. J Chinese Rare Earth Soc,2006,24(S):423(in Chinese).
史彩霞, 成国光, 石超民, 等. 430铁素体不锈钢TiN形核细化凝固组织的研究[J]. 中国稀土学报,2006,24(S):423.
9 Shi X F, Cheng G G, Zhao P. Thermodynamic study of Ti₂O₃+TiN complex nucleus formation in 430 ferritic stainless steel [J].J University of Science and Technology Beijing,2010,32(10):1277(in Chinese).
施晓芳, 成国光, 赵沛. 430铁素体不锈钢中Ti₂O₃+TiN复合核心形成的热力学研究[J]. 北京科技大学学报,2010,32(10):1277.
10 史彩霞, 施晓芳, 成国光, 等. TiN对430铁素体不锈钢凝固组织的影响[C]//特钢连铸技术研讨会. 北京:冶金工业出版社,2007:37.
11 施晓芳, 成国光, 赵沛.含Ti复合核心对细化430铁素体不锈钢凝固组织的影响[C]//不锈钢连铸技术交流会. 北京:冶金工业出版社,2008:72.
12 施晓芳, 成国光, 史彩霞, 等. 含Ti复合核心细化430铁素体不锈钢凝固组织的研究[C]//中国钢铁年会. 北京:冶金工业出版社,2007:6.
13 Wang M L, Cheng G G, Yang X E, et al. Precipitation and growth of titanium oxide during solidification of low carbon steel with tita-nium[J].Iron Steel Res,2004,15(5):47(in Chinese).
王明林, 成国光, 杨新娥, 等. 含钛低碳钢凝固过程中氧化钛的析出和长大[J]. 钢铁研究学报,2004,15(5):47.
14 Wang M L, Cheng G G, Zhao P, et al. Formation thermodynamics of titanium oxide during solidification of low carbon steel containing titanium[J]. Iron Steel Res,2004,16(3):40(in Chinese).
王明林, 成国光, 赵沛, 等. 含钛低碳钢凝固过程中氧化钛形成的热力学[J]. 钢铁研究学报,2004,16(3):40.
15 王明林, 成国光, 仇圣桃, 等. 含钛低碳洁净钢凝固过程氧化物的析出和长大[C]//第二届钢结构进展国际会议. 北京:冶金工业出版社,2007:6.
16 Königsberger E, Schuster E, Gamsjäger H, et al. Thermochemical data and software for the optimization of processes and materials[J]. Jpn Soc Calorimetry Thermal Analysis,2009,19(3):135.
17 Park J H, Lee S B, Dong S K. Inclusion control of ferritic stainless steel by aluminum deoxidation and calcium treatment[J]. Metall Mater Trans B,2005,36(1):67.
18 Ohta H, Suito H. Thermodynamics of aluminum and manganese deoxidation equilibria in Fe-Ni and Fe-Cr alloys[J]. Iron Steel Institute Jpn,2003,43(9):1301.
19 Umemoto M, Owen W S. Effects of austenitizing temperature and austenite grain size on the formation of athermal martensite in an iron-nickel and an iron-nickel-carbon alloy[J]. Metall Mater Trans B,1974,5(9):2041.
20 Ohta H, Suito H. Activities in CaO-SiO₂-Al₂O₃ slags and deoxidation equilibria of Si and Al[J]. Metall Mater Trans B,1996,27(6):943.
21 Kozeschnik E. A Scheil-Gulliver model with back-diffusion applied to the microsegregation of chromium in Fe-Cr-C alloys[J]. Metall Mater Trans A,2000,31(6):1682.
22 Kozeschnik E, Rindler W, Buchmayr B. Scheil-Gulliver simulation with partial redistribution of fast diffusers and simultaneous solid-solid phase transformations[J]. Int J Mater Res,2007,98(9):826.
23 Hillert M, Höglund L, Schalin M. Computer simulation of cooling curves for solidification[J]. Mater Trans Jim,2000,41(8):1098.
24 Yet-Ming Chiang. Grain-boundary migration in nonstoichiometric solid solutions of magnesium aluminate spinel: Ⅰ, grain growth stu-dies[J].J Am Ceram Soc,2005,72(2):271.