Materials Reports 2019, Vol. 33 Issue (Z2): 568-572 |
POLYMERS AND POLYMER MATRIX COMPOSITES |
|
|
|
|
|
Preparation of Super-hydrophobic Ni/CNTs@pDA Composite Coating with Micro/Nano Binary Structures by Dopamine Modification |
CHEN Jianfeng1,2, WANG Fangming1, ZHONG Shifang1, HU Mingjin1, ZHANG Jiangtao1, WANG Kaidong1, LI Xiaobing1,2
|
1 College of Mechanical Engineering, Nanchang University, Nanchang 330031; 2 Key Laboratory of Tribology, Nanchang University, Nanchang 330031 |
|
|
Abstract In order to enhance the corrosion resistance, rub resistance and wear resistance of Ni/CNTs composite coating, surface modification of carbon nanotubes (CNTs) was carried out by dopamine (DA), and the hydrophilicity of CNTs and the bonding between CNTs and the substrate was improved obviously. The high resolution transmission electronic microscope (HRTEM) and energy dispersive spectrometer (XPS) confirmed that the CNTs were coated with poly-dopamine (pDA) up to 3.6 nm. Then the tribological properties and corrosion behavior of the composite coating were measured by ball-on-disk wear tester and electrochemical workstation. The results showed that the performance of Ni/CNTs@pDA compo-site coating is better than the pure nickel coating. Finally,tridecafluorooctyl trimethoxysilane (FAS) was selected to modify the composite coating surface to improve their hydrophobicity. The maximum contact angle measuring up to 152.7°.
|
Published: 25 November 2019
|
|
About author:: Jianfeng Chen, is a lecturer at Nanchang University.From September 2012 to June 2017, he obtained the doctor’s degree in instrument science and technology engineering from University of Science and Technology of China. As the first author, he has published more than 10 papers in academic journals at home and abroad. He is a reviewer of several academic journals.The research work mainly focuses on micro-nano engineering to carry out research on advanced micro-nano processing technology and the interface interaction mechanism of bionic table. Xiaobing Li, male, born in 1979, associate professor/doctor, visiting scholar of Georgia Institute of Technology, USA, deputy director of department of mechanical engineering, school of mechanical and electrical engineering, Nanchang University.He is also the member of youth committee of surface engineering branch of Chinese mechanical engineering society, deputy secretary general of tribology branch of Jiangxi mechanical engineering society, director of surface engineering branch, director of Jiangxi engineering graphics society. Mainly engaged in research on mechanical product innovation, surface engineering and tribology, etc. He has presided over and participated in 10 scientific research projects at or above provincial and ministerial level, including the national natural science foundation of China and the provincial natural science foundation, published more than 60 academic papers, including more than 10 papers included in SCI and EI, and applied for more than 60 invention patents. |
|
|
1 陈小华,张刚,陈传盛,等.无机材料学报,2003(6),1320. 2 Qiu C, Liu D, Jin K, et al. Diamond and Related Materials,2017,76,150. 3 Jian F C, Jiang T Z, Ming J H, et al. Surface and Coatings Technology,2018,353,1. 4 Hovestad A, Janssen L J J. Journal of Applied Electrochemistry,1995,25(6),519. 5 Musiani M. Electrochimica Acta,2000,45(20),3397. 6 徐滨士.上海金属,2008(1),1. 7 杨防祖,姚士冰,周绍民.厦门大学学报:自然科学版,2001,40(2),418. 8 王健雄.腐蚀与防护,2002(1),6. 9 Ciubotariu A C, Benea L, Lakatos-Varsanyi M, et al. Electrochimica Acta,2008,53(13),4557. 10 Tsubota T, Tanii S, Ishida T, et al. Diamond and Related Materials,2005,14(3-7),608. 11 Benea L, Başa S B, Dnil E, et al. Materials & Design,2015,65,550. 12 Tong L, Bajpai V, Tao J, et al. Chemical Reviews,2006,106(3),1105. 13 Salvetat J P, Bonard J M, Bacsa R, et al. American Journal of Orthodontics & Dentofacial Orthopedics,2010,138(5),623. 14 Pierard N, Fonseca A, Colomer J F, et al. Carbon,2004,42(8-9),1691. 15 Huang W, Lin Y, Taylor S, et al. Nano Letters,2002,2(3),231. 16 Goh P S, Ismail A F, Aziz M. In: Conference Proceedings of the Nanoscience and Nanotechnology, International Conference on Nanoscience and Nanotechnology. Malaysia,2008,pp.224. 17 Dayani Y, Malmstadt N. Langmuir,2012,28(21),8174. 18 Xu Y, Wang X, Tian R, et al. Applied Surface Science,2008,254(8),2431. 19 Waite J H, Tanzer M L. Science,1981,212(4498),1038. 20 Lee H, Dellatore S M, Miller W M, et al. Science,2007,318(5849),426. 21 Sever M J, Weisser J T, Monahan J, et al. Angewandte Chemie International Edition,2010,116(23),3046. 22 Chao C, Liu J, Wang J, et al. ACS Applied Materials & Interfaces,2013,5(21),10559. 23 朱丽君.多巴胺对炭黑/CNTs的表面功能化修饰的研究.硕士学位论文,北京化工大学,2012. 24 Sureshkumar M, Siswanto D Y, Chen Y C, et al. Journal of Polymer Science Part B: Polymer Physics,2013,51(4),303. |
|
|
|