钼及钼合金表面硅化物涂层的制备、改性及抗氧化性能研究进展

doi:10.11896/cldb.18060028

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2913KB)
Export: BibTeX | EndNote (RIS)

Abstract Molybdenum has been widely used in electronic devices, heater elements, glass fiber processing, thermometry protective tubes and aerospace crafts, by virtue of its excellent high-temperature mechanical properties, corrosion resistance, and a cheaper price compared to tungsten, niobium and tantalum. However, poor antioxidant ability has limited the further application of molybdenum under high temperature circumstances. This exaggerates the importance of research and improvement for antioxidant ability of molybdenum and its alloys.
The silicide coating, with high-temperature self-healing ability, has been regarded as a promising protection for Mo and Mo alloys substrates against oxidation. Thus extensive research has been done to improve silicide coatings, which includes: (i) single element modification by nitriding, boronizing, aluminizing, etc., (ii) multi-element modification and the formation of composition-graded coating, and (iii) introducing reinforcement phases. Nitriding can change the microstructure of silicide coating, and consequently reduce the difference in thermal expansion coefficient (CTE) between coating and substrate. Boronizing can improve the coating’s self-healing ability and result in the formation of T2 (Mo₅SiB₂) alloy layer which suppresses the internal diffusion of Si. Aluminizing makes the coating to generate Al₂O₃-SiO₂ thin film under low-temperature oxidative condition, and thus is conducive to the prevention of “pesting” failure of MoSi₂ coating. In respect of multi-element modification, carburizing can lead to the reaction between coating elements and substrate to form graded coating. The enrichment of Cr on coating surface by chromizing reduces the internal diffusion of Si and the volatilization of MoO₃. The high-temperature ductility and anti-oxidation properties of the silicide coating can be improved by titanizing. The former is the consequence of C11b/C40 dual-phase structure caused by the alloying effect of titanium, while the latter comes from the formation of dense Si-Ti-O compound glass. In addition, Zr-containing reinforcements (e.g. ZrB₂ and ZrSi₂) can also be used to modify silicide coatings. And high-melting-point phase ZrO₂ generated at high temperatures in modified coatings play a “skeleton” role in the oxide scale improving anti-oxidation properties of coating. On the other hand, by adding whiskers as reinforcing particles, coating is promoted in strength and toughness and crack propagation is restrained, owing to pull out, bridging and crack deflection effects of the whiskers. It can be concluded, based on the domestic and foreign studies upon element modification of silicide coating, that the key factors influencing oxidation resis-tance of silicide coating are “pesting” oxidation, inter-diffusion between coating and substrate, and difference of CTE between coating and substrate.
This review provides a comprehensive description over the global research works on silicide coating modification, by adding single element in isolation or using multiple elements in combination or introducing reinforcement. It also gives an analysis for the key factors related to oxidation resistance of silicide coating, and an outlook on the future research.

Key words： molybdenum molybdenum alloys silicide anti-oxidation coating “pesting” oxidation graded coating reinforcement nitriding boronizing aluminizing titanizing carburizing chromizing

Published: 15 August 2019

CLC number:

TG146.4

About author:: Haoran He, an engineer, received his B.S. degree in materials science and engineering from Chongqing University in 2014. He is a material technologist in Chongqing Materials Research Institute and currently pushing his directed education Master’s degree in Chongqing University of Technology under the supervision of Prof. Junqiang Xu, instructors for master and doctor students, who is working at the Chongqing University of Technology as professor.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HE Haoran
	XU Junqiang
	MIAO Xin
	LIU Qi
	BO Xinwei

Cite this article:

HE Haoran,XU Junqiang,MIAO Xin, et al. Preparation, Modification and Oxidation Resistance of Silicide Coatings on Moand Mo Alloys Substrates: a Review[J]. Materials Reports, 2019, 33(19): 3227-3235.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.18060028 OR http://www.mater-rep.com/EN/Y2019/V33/I19/3227

Zheng X, Bai R, Wang D H, et al. Rare Metal Materials and Enginee-ring,2011,40(10),1871(in Chinese).郑欣,白润,王东辉,等.稀有金属材料与工程,2011,40(10),1871.2 Lang D, Pöhl C, Holec D, et al. Journal of Alloys & Compounds,2016,654,445.3 Li B R, Cheng S. Aerospace Manufacturing Technology,1995(4),43(in Chinese).李宝蓉,程升. 航天制造技术,1995(4),43.4 Han Q. China Molybdenum Industry,2002,26(4),32(in Chinese).韩强.中国钼业,2002,26(4),32.5 Li M S. High temperature corrosion of metal, Metallurgical Industry Press, China,2001(in Chinese).李美栓.金属的高温腐蚀,冶金工业出版社,2001.6 Chakraborty S P, Banerjee S, Sharma I G, et al. Journal of Nuclear Materials,2010,403(1),152.7 Wang Y, Wang D Z, Shun A K, et al. Materials Review A: Review Papers,2012,26(1),137(in Chinese).汪异,王德志,孙翱魁,等.材料导报:综述篇,2012,26(1),137.8 Song R, Wang K S, Hu P, et al. Materials Review A: Review Papers,2016,30(3),69(in Chinese).宋瑞,王快社,胡平,等.材料导报:综述篇,2016,30(3),69.9 Lee E W, Khan A, Cook J, et al. JOM,1991,43(3),54.10 Zhu Y T, Stan M, Conzone S D, et al. Journal of the American Ceramic Society,1999,82(10),2785.11 Opeka M M, Talmy I G, Zaykoski J A. Journal of Materials Science,2004,39(19),5887.12 Tatemoto K, Ono Y, Suzuki R O. Journal of Physics & Chemistry of Solids,2005,66(2),526.13 Alam M Z, Venkataraman B, Sarma B, et al. Journal of Alloys and Compounds,2009,487(1-2),335.14 Yoon J K, Kim G H, Byun J Y, et al. Surface & Coatings Technology,2003,172(2),176.15 Nyutu E K, Kmetz M A, Suib S L. Surface & Coatings Technology,2006,200(12),3980.16 Xie N P. Study on preparation and properties of silicides coating on the molybdenum surface by in-situ synthesizing. Master’s Thesis, Hunan University of Science and Technology, China,2011(in Chinese).谢能平.钼表面原位合成硅化物涂层的制备工艺与性能研究.硕士学位论文,湖南科技大学,2011.17 Cai Z, Liu S, Xiao L, et al. Surface & Coatings Technology,2017,324,182.18 Wang Y. Preparation and properties of Mo-based alloys oxidation resis-tance coatings at elevated temperature. Ph.D. Thesis, Central South University, China,2014(in Chinese).汪异.钼基合金高温抗氧化涂层的制备及其性能研究.博士学位论文,中南大学,2014.19 Chatilyan H A, Kharatyan S L, Harutyunyan A B. Materials Science & Engineering A,2007,459(1),227.20 Yoon J K, Kim G H, Byun J Y, et al. Surface & Coatings Technology,2001,148(2),129.21 Knittel S, Mathieu S, Vilasi M. Intermetallics,2011,19(8),1207.22 Li J G, Zhou S Y, Hu Y F. Modern surface engineering and its application, Chemical Industry Press, China,2014(in Chinese).李金桂,周师岳,胡业峰.现代表面工程技术与应用,化学工业出版社,2014.23 Glass D. In: Conference Record of the 2008 AIAA 15th Conference on Ceramic Matrix Composite (CMC) Thermal Protection Systems (TPS) and Hot Structures for Hypersonic Vehicles. Dayton,2008,pp.2682.24 Hirvonen J P, Suni I, Kattelus H, et al. Surface & Coatings Technology,1995,s74-75(1-3),981.25 Hsieh T, Choe H, Lavernia E J, et al. Materials Letters,1997,30(30),407.26 Yoon J K, Lee J K, Byun J Y, et al. Surface & Coatings Technology,2002,160(1),29.27 Yoon J K, Kim G H, Byun J Y, et al. Surface & Coatings Technology,2003,165(1),81.28 Yoon J K, Kim G H, Han J H, et al. Surface & Coatings Technology,2005,200(7),2537.29 Gu S Y, Zhang H A, Xie N P. Journal of Xiamen University of Technology,2011,19(2),18(in Chinese).古思勇,张厚安,谢能平.厦门理工学院学报,2011,19(2),18.30 Huang Y, Lin J, Zhang H. Ceramics International,2015,41(10),13903.31 Xie N P, Zhang H A, Gu S Y. Materials for Mechanical Engineering,2012,36(1),23(in Chinese).谢能平,张厚安,古思勇.机械工程材料,2012,36(1),23.32 Meyer M K, Thom A J, Akinc M. Intermetallics,1999,7(2),153.33 Meyer M, Kramer M, Akinc M. Advanced Materials,1996,8(1),85.34 Akinc M, Meyer M K, Kramer M J, et al. Materials Science & Enginee-ring A (Structural Materials: Properties, Microstructure and Processing),1999,261(1-2),16.35 Tang Z, Thom A J, Kramer M J, et al. Intermetallics,2008,16(9),1125.36 Tian X, Guo X, Sun Z, et al. International Journal of Refractory Metals & Hard Materials,2014,45,8.37 Wang Y, Yan J, Wang D. International Journal of Refractory Metals & Hard Materials,2017,68,60.38 Meschter P J. Metallurgical Transactions A (Physical Metallurgy and Materials, Science),1992,23(6),1763.39 Chou T C, Nieh T G. JOM,1993,45(12),15.40 Mitra R, Rao V V R. Materials Science & Engineering A,1999,260(1),146.41 Majumdar S. Surface & Coatings Technology,2012,206(15),3393.42 Chen H, Ma Q, Shao X, et al. Materials Science & Engineering A,2014,592(2),12.43 Majumdar S, Sharma I G. Intermetallics,2011,19(4),541.44 Tang D Z. Research on the preparation and properties of coating on molybdenum. Master’s Thesis, Central South University, China,2014(in Chinese).汤德志.钼合金表面涂层的制备及性能研究.硕士学位论文,中南大学,2014.45 Gu S Y, Zhang H A, Xie N P. Mining and Metallurgical Engineering,2012,32(5),116(in Chinese).古思勇,张厚安,谢能平.矿冶工程,2012,32(5),116.46 Gu S Y, Zhang H A, Wu Y H, et al. Rare Metal Materials and Enginee-ring,2014,43(5),1219(in Chinese).古思勇,张厚安,吴艺辉,等.稀有金属材料与工程,2014,43(5),1219.47 Liu J, Gong Q, Shao Y, et al. Applied Surface Science,2014,308(308),261.48 Zhang H, Gu S. International Journal of Refractory Metals & Hard Mate-rials,2013,41(11),128.49 Zhang Ping, Guo Xiping, Ren Xuanru, et al. Intermetallics,2018,93(2),134.50 Tao Q, Guo X P. Journal of Inorganic Materials,2009,24(6),1219.51 Heron A J, Schaffer G B. Materials Science & Engineering A,2003,352(1),105.52 Umakoshi Y, Sakagami T, Hirano T, et al. Acta Metallurgica Et Materialia,1990,38(6),909.53 Boettinger W J, Perepezko J H, Frankwicz P S. Materials Science & Engineering A,1992,155(1-2),33.54 Li W, Fan J L, Fan Y, et al. Journal of Alloys and Compounds,2018,740(5),711.55 Zhang Y, Li Y, Bai C. Ceramics International,2017,43(8),6250.56 Zhang Y, Ni W, Li Y. Ceramics International,2018,44(10),11166.57 Wang L, Fu Q, Zhao F, et al. Surface & Coatings Technology,2018,347,257.58 Kobayashi A, El-Sheikhy R. Transactions of Jwri,2007,36,87.59 Vinci A, Zoli L, Sciti D. Journal of the European Ceramic Society,2018,38,3767.60 Guo S, Mizuguchi T, Ikegami M, et al. Ceramics International,2011,37(2),585.61 Jiang Y, Feng D, Ru H, et al. Surface & Coatings Technology,2018,339,91.62 Xiao Lairong, Rao Bo, Cai Zhenyang, et al. Ordnance Material Science and Engineering,2015(6),27(in Chinese).肖来荣,饶博,蔡圳阳,等.兵器材料科学与工程,2015(6),27.63 Cai Z, Wu Y, Liu H, et al. Materials & Design,2018,155,463.64 David H C, Hurley G F. Cheminform,1987,70(4),C-79.65 Fu Q G, Li H J, Li K Z, et al. Surface Review & Letters,2006,44(9),1866.66 Jia L, Zhang X, Zhi W, et al. Materials & Design,2012,34,853.67 Ren J, Zhang Y, Zhang P, et al. Journal of the European Ceramic Society, 2017, 37(8), 2759.68 Fu Qiangang. Study on the SiC whisker-toughed silicides and SiC/Glass oxidation protective coatings. Ph.D. Thesis, Northwestern Polytechnical University, China,2007 (in Chinese).付前刚.SiC晶须增韧硅化物及SiC/玻璃高温防氧化涂层的研究.博士学位论文,西北工业大学,2007.69 Wang L, Fu Q, Zhao F. Intermetallics,2018,94,106.70 Feng P Z, Qu X H, Humail I S, et al. Journal of University of Science & Technology Beijing,2007,14(6),558.71 Wang G, Zhao S K, Jiang G. Journal of Inorganic Materials,2001,16(6),1041(in Chinese).王刚,赵世柯,江莞.无机材料学报,2001,16(6),1041.72 Tortorici P C, Dayananda M A. Metallurgical & Materials Transactions A,1999,30(3),545.73 Yoon J K, Lee J K, Lee K H, et al. Intermetallics,2003,11(7),687.