硅含量对Al-Si-Cu相变储能材料腐蚀性的影响

doi:10.11896/cldb.201904003

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (1469KB)

Suppl. Info.
Export: BibTeX | EndNote (RIS)

Abstract High liquid corrosivity has long became the obstacle to the application of Al alloys as phase-change energy-storage materials. It has been common knowledge that the composition of energy storage material is one of the important factors that affect its liquid corrosivity. Thereby, in this work, a corrosion test scheme of 304 stainless steel in liquid Al-xSi-10Cu (6≤x≤15) alloys was conducted, so as to investigate the effect of Si element content on liquid corrosivity. We characterized the morphology, element distribution and phase composition of the corrosion products by means of electron probe and XRD, and also carried out kinetic and thermodynamic analyses for the corrosion reaction. The results showed that with the increase of Si content, both the corrosion layer thickness and the growth coefficient of corrosion products exhibit biphasic (decrease→increase) change, while the diffusion activation energy of corrosion products displays an opposite variation, and all of them reach the minimum or maximum value at the Si content of 9%. When the Si content is in the range of 6%~9%, a short-duration corrosion leads to a corrosion layer mainly composed of Al₉₅Fe₄Cr phase and Fe₂Al₅ phase, the vacancies of the latter of which can be filled by Si atoms so that the corrosive elements diffusion can be attenuated. But a long-duration corrosion leads to a corrosion layer mainly composed of Al₉₅Fe₄Cr phase, Fe_xSi_yAl_z phase and FeAl phase. The Fe_xSi_yAl_z phase grows quite slowly and can prevent element diffusion. Moreover, the formation enthalpy of FeAl phase is larger than that of Fe₂Al₅ phase, so the corrosion thickness can be reduced. When the Si content ranges in 9% to 15%, the specific reason for the corrosion thickness increment with the addition Si element remains unclear and further study is needed.

Key words： Si Al-Si-Cu phase-change energy-storage material liquid corrosion intermetallic compound

Published: 11 March 2019

CLC number:

TG178

Fund:This work was financially supported by the Fundamental Research Funds for the Central Universities (11CX05003A) and the General Program of Shengli College, China University of Petroleum (KY2015021).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Xiaohua
	YU Sirong
	GUO Lijuan
	ZHOU Yangli

Cite this article:

ZHANG Xiaohua,YU Sirong,GUO Lijuan, et al. Effect of Si Content on Liquid Corrosivity of Al-Si-Cu Energy Storage Materials[J]. Materials Reports, 2019, 33(4): 582-585.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.201904003 OR http://www.mater-rep.com/EN/Y2019/V33/I4/582

Huang X. Research on thermal storage properties of phase-change mate-rials based on Mg-Cu-Zn-Al-Si alloy. Master’s Thesis, Wuhan University of Technology,China,2014(in Chinese).黄昕.Mg-Cu-Zn-Al-Si多元合金相变材料储热性能的研究.硕士学位论文,武汉理工大学,2014.2 Su Z, Cheng X M, Zhu J Q, et al. Journal of Functional Materials,2017,48(2),2236(in Chinese).孙正,程晓敏,朱教群,等.功能材料,2017,48(2),2236.3 Xu J, Yu S. Materials Review A:Review Papers,2013,27(10),93(in Chinese).许骏,于思荣.材料导报:综述篇,2013,27(10),93.4 Cheng X M, He G, Wu X W, et al. Materials Review A:Review Papers,2010,24(9),139(in Chinese).程晓敏,何高,吴兴文,等.材料导报:综述篇,2010,24(9),139.5 Dong J. Research on the optimization design and thermal storage properties of high-temperature phase change thermal storage Al-Si-Cu-Mg-Zn alloy. Master’s Thesis, Wuhan University of Technology, China,2009(in Chinese).董静.基于Al-Si-Cu-Mg-Zn合金的高温储热材料优化设计与储热性能研究.硕士学位论文,武汉理工大学,2009.6 Li X H, Li G X, Wu Y, et al. Hot dip plating and seepage plating of steel parts. Chemical Industry Press, China,2009(in Chinese).李新华,李国喜,吴勇,等.钢铁制件热浸镀与渗镀. 化学工业出版社,2009.7 Akdeni M V, Mekhrabov A O, Yilmaz T. Scripta Metallurgica Et Mate-rialia,1994,31(12),1723.8 Qian W J, Gu W G. Acta Metallurgica Sinica,1994,30(9),403(in Chinese).钱卫江,顾文桂.金属学报,1994,30(9),403.9 Han W. Influence of Si on the growth kinetics of Fe2Al5 during reactive diffusion between Fe and Al. Master’s Thesis, Xiangtan University,China,2009(in Chinese).韩炜.Si对Fe-Al反应过程中Fe2Al5相生长动力学的影响.硕士学位论文,湘潭大学,2009.10 Denner S, Jones R, Thomas R. Journal of Iron and Steel Reseach International,1975,48,241.11 Eggeler G, Auer W, Kaesche H. Journal of Materials Science,1986,21(9),3348.12 Chinese Society for Corrosion and Protection. Metal corrosion manual, Shanghai Science and Technology Press, China,1987(in Chinese).中国腐蚀与防护学会.金属腐蚀手册.上海科学出版社,1987.13 Akdeniz M V, Mekhrabov A O. Acta Materialia,1998,46(4),1185.14 Mekhrabov A O, Akdeniz M V. Acta Materialia,1999,47(7),2067.15 Hou Xiaoxia, Yang Hua, Zhao Yan, et al. Materials Letters,2002.58(27-28),3424.16 Zhao G D, Guo P M, Zhao P. Journal of Central South University,2011,42(6),1578(in Chinese).赵定国,郭培民,赵沛.中南大学学报,2011,42(6),1578.