喷射成形工艺参数对沉积坯质量的影响

doi:10.11896/cldb.201903003

Abstract
Figure/Table
References
Related Citation (11)

Download:

Full Text ( PDF ) (2516KB)
Export: BibTeX | EndNote (RIS)

Abstract There are many parameters that affect the quality of spray forming billet. Apart from the own characteristics of the material, the process para-meters play a crucial role in determining the quality of the billet. The effects of spray forming processing parameters on properties of as-deposited billet were studied in this paper. Emphases were placed on the effects of melt superheat and gas pressure on the shape, porosity and solidification microstructures of as-deposited billet of M3 high speed steel. The results showed that there was a remarkable impact of melt superheat and gas pressure on the properties of as-deposited billet. The obviously refined solidification microstructure could be achieved whether by decreasing the melt superheat or increasing of the gas pressure. The porosity of the bottom dropped with increasing melt superheat, while the porosity in the edge, surface and center region decreased first and then increased with increasing melt superheat. On the other hand, the value of P (porosity) increased monotonically with the rise of gas pressure in the bottom, surface, and periphery zones, whereas the porosity of the central zone decreased firstly and then grew with the increase of gas pressure. A high quality as-deposited billet with the desired shape, low porosity and fine microstructure could be obtained by spray forming under the melt superheat of 160—180 ℃ and gas pressure of 0.45—0.5 MPa, respectively.

Key words： spray forming as-deposited billet high speed steel melt superheat porosity

Published: 13 February 2019

CLC number:

TB31

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LU Lin
	WU Wenheng
	LONG Qianlei
	ZHANG Liang
	ZHANG Jishan

Cite this article:

LU Lin,WU Wenheng,LONG Qianlei, et al. Effects of Spray Forming Parameters on Properties of As-deposited Billet[J]. Materials Reports, 2019, 33(3): 390-394.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.201903003 OR http://www.mater-rep.com/EN/Y2019/V33/I3/390

1 Singer A R E. Metals Materials,1970,4(6),246.
2 Singer A R E. Powder Metallurgy,1982,25(4),195.
3 Zhang J S, Xiong B Q, Cui H. Spray Forming Rapid Solidification Technology:Principles and Applications, Science Press, China,2008(in Chinese).
张济山,熊柏青,崔华.喷射成形快速凝固技术-原理与应用,科学出版社,2008.
4 Peng C Q. Spray forming technology, Central South Univesity Press, China,2004(in Chinese).
彭超群.喷射成形技术,中南大学出版社,2004.
5 Schruff I, Schüler V, Spiegelhauer C. The Use of Tool Steels: Experience and Research,2002(2),10.
6 Grant P S,Cantor B,Katgerman L. Acta Metallurgica,1993,41(11),3109.
7 Cai W D, Lavernia E J. Metallurgical and Materials Transactions B,1998,29(5),1085.
8 Cai W D, Lavernia E J. Materials Science and Engineering A,1997,226,8.
9 Mesquita R A, Barbosa C A. Materials Science and Engineering A,2004,383(1),87.
10 Annavarapu S, Apelian D, Lawley A. Metallurgical Transactions A,1990,21(12),3237.
11 Mathur P, Annavarapu S, Apelian D, et al. Materials Science and Engineering A,1991,142(2),261.
12 Lee E S, Ahn S. Acta Metallurgica,1994,42(9),3231.
13 Grant P S, Kim W T, Bewlay B P, et al. Scripta Metallurgica,1989,23(10),1651.
14 Hu H, Lavernia E J, Lee Z H, et al. Metallurgical and Materials Tran-sactions A,2000,31(3),725.
15 Zhang J X, Lu L, Wang H B, et al. Materials Review A: Review Papers,2014,28(7),17(in Chinese).
张金祥,卢林,王和斌,等.材料导报:综述篇,2014,28(7),17.
16 Lu L, Huang J F, Hou L G, et al. Journal of University of Science and Technology Beijing,2014,36(10),1292(in Chinese).
卢林,黄进峰,侯陇刚,等.北京科技大学学报,2014,36(10),1292.
17 Apelian D, Lawley A, Mathur P. Spray deposition: a fundamental study of droplet impingement, spreading and consolidation. Ph.D.Thesis, Drexel Univ Philadelphia Pa Dept of Materials Engineering, USA,1989.
18 Mathur P, Apelian D, Lawley A. Acta Metallurgica,1989,37(2),429.
19 Annavarapu S, Doherty R D. International Journal of Powder Metallurgy,1993,29(4),331.
20 Bewlay B P, Cantor B. Metallurgical Transactions B,1990,21(5),899.
21 Annavarapu S, Apelian D, Metallurgical Transactions A,1988,19(12),3077.
22 Lavernia E J, Baran J, Gutierrez E. Materials Science and Engineering A,1991,132,119.
23 Xu Q, Gupta V V, Lavernia E J. Metallurgical and Materials Transactions B,1999,30(3),527.
24 Smith J E, Jordan M L. Journal of Colloid Science,1964,19(6),549.
25 Lubanska H. Journal of Metals,1970,22(2),45.