石灰石粉和含铝相辅助性胶凝材料的协同作用对混凝土抗碳化性能的影响

doi:10.11896/j.issn.1005-023X.2018.17.012

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2030KB)
Export: BibTeX | EndNote (RIS)

Abstract To investigate the impact of synergistic effect between limestone powder and supplementary cementitious materials containing aluminate phase on carbonation resistance of concrete, two kinds of supplementary cementitious materials containing aluminate phase and limestone powder were selected to replace cement in different proportion, and the hydration products and microstructure were measured by thermogravimetric analysis, XRD and mercury intrusion porosimetry. The results showed that incorporation of limestone powder reduce the carbonation resistance of concrete. The carbonation depth of concrete was minimal when the content of limestone powder was approximately 10%. However, when limestone powder and supplementary cementitious materials containing aluminate phase were mixed, they reacted to form calcium carboaluminate, which increase the volume of solid phase, optimize the pore structure, and their synergistic effect improved the carbonation resistance of concrete. When the limestone powder amount was 5%—15%, and the fly ash amount was less than 10% or the slag amount was 10%—30%, the carbonation depth of concrete was lowest.

Key words： limestone powder fly ash slag synergistic effect carbonation resistance

Published: 19 September 2018

CLC number:

TU528

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Dehui
	SHI Caijun
	JIA Huangfei

Cite this article:

WANG Dehui,SHI Caijun,JIA Huangfei. Impact of Synergistic Effect Between Limestone Powder and Supplementary Cementitious Materials Containing Aluminate Phase on Carbonation Resistance of Concrete[J]. Materials Reports, 2018, 32(17): 2986-2991.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.17.012 OR http://www.mater-rep.com/EN/Y2018/V32/I17/2986

1 Wang D H, Shi C J, Farzadnia N, et al. A review on use of limestone powder in cement-based materials: Mechanism, hydration and microstructures[J].Construction and Building Materials,2018,181:659.
2 Soroka I, Setter N. The effect of fillers on strength of cement mortars[J].Cement and Concrete Research,1977,7(4):449.
3 Soroka I, Setter N. Calcareous fillers and the compressive strength of Portland cement[J].Cement and Concrete Research,1976,6(3):367.
4 Schmidt M. Cement with interground additives-capabilities and environmental relief, Part 2[J].Zement-kalk-Gips,1992,45(6):296.
5 European Committee for Standardization. EN 197-1 (2000). “Cement-part 1”, composition, specifications and uniformity criteria for common cements[S].Brussels, Belgium,2000.
6 Canadian Standards Association. CSA A3001. Cementitious materials for use in concrete[S].Toronto, Ontario,2008.
7 Canadian Standards Association. CSA A3001. Cementitious materials for use in concrete[S].Toronto, Ontario,2010.
8 ASTM International. ASTM Standard C595. Standard specification for blended hydraulic cements[S].West Conshohocken,2012.
9 Celik K, Meral C, Gursel A P, et al. Mechanical properties, durability, and life-cycle assessment of self-consolidating concrete mixtures made with blended Portland cements containing fly ash and limestone powder[J].Cement and Concrete Composites,2015,56(77):59.
10 Vance K, Aguayo M, Oey T, et al. Hydration and strength development in ternary portland cement blends containing limestone and fly ash or metakaolin[J].Cement and Concrete Composites,2013,39(5):93.
11 Das S,Aguayo M, Dey V, et al. The fracture response of blended formulations containing limestone powder: Evaluations using two-parameter fracture model and digital image correlation[J].Cement and Concrete Composites,2014,53(10):316.
12 De W K, Ben H M, Le S G, et al. Hydration mechanisms of ternary Portland cements containing limestone powder and fly ash[J].Cement and Concrete Research,2011,41(3):279.
13 Arora A, Sant G, Neithalath N. Ternary blends containing slag and interground/blended limestone: Hydration, strength, and pore structure[J].Construction and Building Materials,2016,102:113.
14 Taylor H F W. Cement chemistry. 2nd Ed[M].London: Academic Press,1990.
15 Moesgaard M, Herfort D, Steenberg M, et al. Physical perfor-mances of blended cements containing calcium aluminosilicate glass powder and limestone[J].Cement and Concrete Research,2011,41(3):359.
16 Aqel M, Panesar D K. Hydration kinetics and compressive strength of steam-cured cement pastes and mortars containing limestone filler[J].Construction and Building Materials,2016,113:359.
17 Martin C, Philippe, Erick R. Efficiency of mineral admixtures in mortars quantification of the physical and chemical effects of fine admixtures in relation with compressive strength[J].Cement and Concrete Research,2006,36(2):264.
18 Deschner F, Winnefeld F, Lothenbach B, et al. Hydration of Portland cement with high replacement by siliceous fly ash[J].Cement and Concrete Research,2012,42(10):1389.
19 Lothenbach B, Matschei T, Moschner G, et al. Thermodynamic modeling of the effect of temperature on the hydration and porosity of Portland cement[J].Cement and Concrete Research,2008,38:1.