BT@PANI核壳粒子的绿色制备及PVDF基复合材料的介电性能

doi:10.11896/cldb.22120173

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (16883KB)
Export: BibTeX | EndNote (RIS)

Abstract Dielectric capacitors composed of polymer-matrix composite films with high dielectric constants have a practical application and prospect in the fields of new energy vehicles, solar and wind power grid-connected power generation and energy storage and so on. Barium titanate/polymer composites, which present low dielectric loss and high breakdown field strength, are the prospective materials used as the core part of the capacitors. Now, it is urgent to solve the problem of the balanced improvement on high polarizability and low loss. In this work, barium titanate@polyaniline (BT@PANI) core-shell particles were prepared by the in-situ polymerization using malic acid as a surface modification agent for BT particles and a doping agent of PANI. Then polyvinylidene fluoride (PVDF)-based composites were prepared. The results show that barium titanate-aniline cationic particles (BT-An⁺) was obtained by two-step surface modification of malic acid and hydrochloric acid, and so the core-shell structure character of all products prepared under various mass rations of An and BT is clear. When the mass ratio of An to BT is 0.5∶1, the average particle size is 450 nm and the distribution is the narrowest. and its conductivity value is 1.45×10^-3 S/cm. The PVDF-based composite with 30wt% BT@PANI loading has high dielectric constants which vary from 31 to 15 in range of 10³—10⁶ Hz. Meanwhile, the dielectric loss remained less than 0.3 within the wide frequency range. The BT@PANI/PVDF composite presents not only good frequency stability but also effective suppression of dielectric loss under the condition of obtaining high dielectric constant. In addition, this work greatly reduces the utilization rate of inorganic oxidizing acids and organic agents and so provides an experimental guidance for green preparation of high performance dielectric composites.

Key words： composite dielectric polymer-base dielectric property core-shell structure green preparation

Published: 10 July 2024 Online: 2024-08-01

CLC number:

TB33

Fund:National Natural Science Foundation of China (51767016).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Haiyan
	XIAN Longdi
	SHANG Tianrong
	YAO Jiaqi
	YAN Xiaobin
	LI Lan

Cite this article:

WANG Haiyan,XIAN Longdi,SHANG Tianrong, et al. Green Preparation of Core-shell BT@PANI Particles and Dielectric Properties of Poly(vinylidene fluoride)-based Composites[J]. Materials Reports, 2024, 38(13): 22120173-6.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22120173 OR http://www.mater-rep.com/EN/Y2024/V38/I13/22120173

1 Zhang Q, Jiang P K, Huang X Y. Insulating Materials, 2019, 52(4), 1(in Chinese).
张强, 江平开, 黄兴溢. 绝缘材料, 2019, 52(4), 1.
2 Zhang H, Heng T T, Fang Z G, et al. Acta Materiae Compositae Sinica, 2021, 38(7), 2107(in Chinese).
张慧, 衡婷婷, 房正刚, 等. 复合材料学报, 2021, 38(7), 2107.
3 Wu Z Q, Peng Y W, Guo Q, et al. Materials Today Communications, 2022, 32, 103857.
4 Wei J J, Zhu L. Progress in Polymer Science, 2020, 106, 101254.
5 Wang J, Liu S H, Chen C Q, et al. Acta Physica Sinica, 2020, 69(21), 59 (in Chinese).
王娇, 刘少辉, 陈长青, 等. 物理学报, 2020, 69(21), 59.
6 Zhou W Y, Kou Y J, Yuan M X, et al. Composites Science and Technology, 2019, 181, 107686.
7 Wang Y Z, Qu S N, Yin X X. Materials Reports, 2022, 36(4), 209(in Chinese).
汪叶舟, 曲绍宁, 尹训茜. 材料导报, 2022, 36(4), 209.
8 Shang S Y, Tang C Y, Jiang B B. Composites Communications, 2021, 25, 100745.
9 Guan S S, Tang Y K, Song S C, et al. Materials Science and Enginee-ring: B, 2021, 271, 115280.
10 Zhang X H, Ye H J, Xu L X, et al. Applied Surface Science, 2022, 600, 154113.
11 Wang M, Pan X R, Qi X D, et al. Composites Communications, 2020, 21, 100411.
12 Li T, Zhou W Y, Cao D, et al. Modern Plastics Processing and Applications, 2021, 33(1), 60(in Chinese).
李婷, 周文英, 曹丹, 等. 现代塑料加工应用, 2021, 33(1), 60.
13 Phromviyo N, Thongbai P, Maensiri S. Applied Surface Science, 2018, 446, 236.
14 Wang H Y, You Y B, Zha J W, et al. Composites Science and Technology, 2020, 200, 108405.
15 Jiang Y C, Wang J B, Zhang Q L, et al. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2019, 576, 55.
16 Zhang Q L, Jiang Y C, Yu E J, et al. Surface and Coatings Technology, 2019, 358, 293.
17 Liu Y J, Zhao X M, Liang T L. Materials Reports, 2016, 30(S2), 304(in Chinese).
刘元军, 赵晓明, 梁腾隆. 材料导报, 2016, 30(S2), 304.
18 Meher D, Suman, Karna N, et al. Polymer, 2019, 181, 121759.
19 Yang R, Wang B, Li M D, et al. Industrial Crops and Products, 2019, 136, 121.
20 Kövilein A, Kubisch C, Cai L Y, et al. Journal of Chemical Technology and Biotechnology, 2020, 95(3), 513.
21 You Y B, Wang H Y, Li L, et al. Journal of Materials Science: Materials in Electronics, 2022, 33, 4268.
22 Zhang Y, Li X L, Lyu L Y, et al. Electronic Components and Materials, 2014, 33(3), 31(in Chinese).
张园, 李小丽, 吕丽云, 等. 电子元件与材料, 2014, 33(3), 31.
23 Zhang R R, Li L L, Long S J, et al. Ceramics International, 2021, 47(15), 22155.
24 Ji W J, Deng H, Guo C, et al. Composites Part A: Applied Science and Manufacturing, 2019, 118, 336.
25 Wang H Y, Zhang X T, Zha J W, et al. Journal of Materials Science: Materials in Electronics, 2019, 30(4), 3325.
26 Sun D D, Huang S J, Gao Y, et al. Journal of Alloys and Compounds, 2019, 783, 256.