SURFACE ENGINEERING MATERIALS AND TECHNOLOGY |
|
|
|
|
|
Heat Treatment Process of Induction Braze Coating of Rotary Blades |
LONG Weimin1,2, QIN Jian2, LU Quanbin2, LIU Dashuang3, WU Aiping1
|
1 Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China 2 Zhengzhou Research Institute of Mechanical Engineering Co., Ltd., Zhengzhou 450001, China 3 School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China |
|
|
Abstract The process of diamond induction brazing has a great influence on the microstructure and property of the steel substrate.Post brazing heat treatment is an important method to improve the performance of the substrate, but it also has great impact on the coating. The influence of post heat treatment on the hardness and microstructure evolution of induction brazing nickel base alloy coating was investigated by means of high temperature microscope, SEM, XRD, hardness testing and other analytical methods. The results show that the NiCrSiB brazing coating structure was mainly composed of Ni solid solution, CrB, Ni3Si, Ni3B, and Ni-Ni3Si eutectic phases. After quenching treatment, the content and dimension of Ni3Si-Ni solid solution eutectic crystals decreased, the CrB phase grew to a certain extent, and the total content of Ni3Si phase reduced. After tempering treatment, the content of the eutectic structure near the grain boundary of the NiCrSiB brazing coating increased, and CrB phase grew further to promote the formation of little Ni3Si phase. The hardness of the brazed state coating was higher, then it decreased integrally after quenching and rose again after tempering. A novel technology of brazing and coating combined with heat treatment to improve the comprehensive performance of the rotary cultivator was developed, based on the rotary blade for agricultural machinery equipment as the specific object.
|
Published:
Online: 2022-04-07
|
|
Fund:National Natural Science Foundation of China (U2004186), Key Technology Requirements in Henan Province (191110111000), and Ningbo “3315” Talent Plan 2020 Innovative Team Class C. |
|
|
1 Kılıçay K, Buytoz S, Ulutan M.Surface and Coatings Technology, 2020, 397, 125974. 2 Zhang Z Z, Niu J J, Fu Y W. Transactions of Materials and Heat Treatment, 2004, 25(2), 31(in Chinese). 张增志, 牛俊杰, 付跃文.材料热处理学报, 2004, 25(2), 31. 3 Pan C G, Gong M C, Feng S Q, et al. Surface and Coatings Technology, 2021, 419, 127278. 4 Zhang Z Z, Han G Q, Fu Y W,et al. Journal of Materials Engineering, 2003(4), 3(in Chinese). 张增志, 韩桂泉, 付跃文, 等. 材料工程, 2003(4), 3. 5 Du S E, Li C, Yao Y Q, et al. Materials for Mechanical Engineering, 2019, 43(7), 38(in Chinese). 杜圣恩, 林晨, 姚永强, 等. 机械工程材料, 2019, 43(7), 38. 6 Meng L, Zhu B B, Rui Y, et al. Journal of Materials Research and Technology, 2021, 13, 1431. 7 Wang X X, Wu S J, Li S, et al. The Chinese Journal of Nonferrous Metals, 2021, 31(1), 72(in Chinese). 王星星, 武胜金, 李帅, 等. 中国有色金属学报, 2021, 31(1), 72. 8 Hou L N. Surface Technology, 2012, 41(4), 49(in Chinese). 侯立宁. 表面技术, 2012, 41(4), 49. 9 Ma Q, Li Y, Wang J, et al. Journal of Alloys and Compounds, 2015, 645, 151. 10 Sun W, Bhowmik A, Tan A W Y,et al. Surface and Coatings Technology, 2019, 358, 1006. 11 Yu J, Song B. Results in Physics, 2018, 11, 212. 12 Pei X J, Zhang J G, Huang J H, et al. Powder Metallurgy Technology, 2006(1), 8(in Chinese). 裴新军, 张建纲, 黄继华, 等. 粉末冶金技术, 2006(1), 8. 13 Xiao Q, Sun W L, Liu J D, et al. Materials Reports, 2021, 35(8), 08146(in Chinese). 肖奇, 孙文磊, 刘金朵, 等. 材料导报, 2021, 35(8), 08146. 14 Gisario A, Puopolo M, Venettacci S, et al. International Journal of Refractory Metals and Hard Materials, 2015, 52, 123. 15 Ma B J, Pu F N, Yang G L, et al. Welding & Joining, 2017(8), 10(in Chinese). 马伯江, 卜凡宁, 杨广蕾, 等. 焊接, 2017(8), 10. 16 Qin J, Long W M, Lu Q B, et al. Materials Reports, 2020, 34(Z2), 457(in Chinese). 秦建, 龙伟民, 路全彬, 等. 材料导报, 2020, 34(Z2), 457. 17 Liu T, Joo H G, Gao L X, et al. International Journal of Refractory Metals and Hard Materials, 2012, 35, 246. 18 Wang Z H, Yang A D, Zhang T, et al. Journal of Materials Engineering, 2008(9), 56(in Chinese). 王智慧, 杨爱弟, 张田, 等. 材料工程, 2008(9), 56. 19 Long W M, Liu D S, Dong X,et al. Surface Engineering, 2020, 36(12), 1315. |
|
|
|