Materials Reports 2019, Vol. 33 Issue (z1): 457-461 |
POLYMERS AND POLYMER MATRIX COMPOSITES |
|
|
|
|
|
Study on Polyacrylonitrile Gel Polymer Electrolyte Films Reinforced by Crosslinking Agent and Non-woven Fabrics |
MA Panlong1,2, ZHANG Zhonghou1, HAN Lin1, CHEN Rongyuan1
|
1 Department of Materials and Chemical Engineering, Zhengzhou University of Light Industry, Zhengzhou 450001 2 Institution of Chemistry, Henan Academy of Sciences, Zhengzhou 450002 |
|
|
Abstract The polyacrylonitrile based gel polymer electrolyte (PAN-EGDMA-GPE) cross-linked by ethylene glycol dimethacrylate (EGDMA), and the PAN-EGDMA-GPE composited with the non-woven fabrics (NWF-PAN-EGDMA-GPE) were successfully prepared by in-situ polymerization. The molecular structure, thermal properties, tensile strength and ionic conductivity of GPE films were detected with the infrared spectrometer, integrated thermal analyzer, universal testing machine and electrochemical workstation. The results showed that the tensile strength of GPE films were significantly improved by EGDMA cross-linker and PP non-woven fabrics. When the amount of EGDMA used was 2.5%( weight) of the monomer, the concentration of LiClO4 was 1 mol/L, and the electrolyte mass content was 87.5% of PAN-EGDMA-GPE, the NWF-PAN-EGDMA-GPE film had the comprehensive performance, the tensile strength of that was 8.47 MPa, which was increased by 31.6 times, comparing to the 0.26 MPa of the unreinforced polyacrylonitrile GPE, the ionic conductivity of that was 1.24×10-3 S/cm.
|
Published: 05 July 2019
|
|
About author:: Panlong Ma graduated from Zhengzhou University of Light Industry in June 2015 with a master's degree in engineering. He is currently an intern researcher at the Institute of Chemistry, Henan Academy of Sciences, and is mainly engaged in the research of polymer composite materials and electronic chemicals.Zhonghou Zhang is a professor and tutor of master,s degree in Department of Materials and Chemical Engineering, Zhengzhou University of Light Technology. He graduated from the Department of Chemistry, Zhengzhou University in 1986 and received his Ph.D. in Material Science, Donghua University in 2009. Since June 2002, he has taught at Zhengzhou University of Light Industry. He is mainly engaged in the research of functional polymer materials, composite materials and flame retardant materials. More than 20 professional papers have been published, and more than 10 scientific and technological projects (including one national project and five provincial projects) have been completed. He has won one second-class prize and two third-class prizes for scientific and technological progress in Henan Province. |
|
|
1 Li W L, Wu Y H, Wang J W, et al. European Polymer Journal,2015,67,365. 2 Kang W M, Ma X M, Zhao H H, et al. Journal of Solid State Electrochem,2016,20,2791. 3 Peng X X, Zhou L, Jing B, et al. Journal of Solid State Electrochem,2016,20,255. 4 Song S H, Wang J W, Tang J W, et al. Ionics,2017,23,3365. 5 Peng S S, Cao Q, Jing Yang, et al. Solid State Ionics,2015,282,49. 6 Tong Y F, Que M M, Su S, et al. Ionics,2016,22,1311. 7 Li W L, Xing Y J, Wu Y H, et al. Electrochimica Acta,2015,151,289. 8 Kang W M, Deng N P, Ma X M, et al. Electrochimica Acta,2016,216,276. 9 黄兆阁, 张宁. 青岛科技大学学报(自然科学版),2017,38(4),59. 10 He C F, Liu J Q, Cui J Q. et al. Solid State Ionics,2018,315,102. 11 张帆,管兴华,马晓燕,等. 高分子学报,2015(7),852. 12 Huang Y, Liu B, Cao H J, et al. Journal of Solid State Electrochem,2017,21,2291. 13 Liu B, Huang Y, Cao H J, et al. Journal of Membrane Science,2018,545,140. 14 邓纯,肖琴,漆志刚,等. 高分子材料科学与工程,2017,33(8),151. 15 Wang Q F, Zhang B, Zhang J J, et al. Electrochimica Acta,2015,157,191. 16 Yang K Q, Ma X Y, Sun K, et al. Journal of Solid State Electrochem,2018,22,441. 17 Liu Y, Ma X Y, Sun K, et al. Journal of Solid State Electrochem,2018,22,581. 18 Chen T T, Liao Y H, Wang X S, et al.Electrochimica Acta,2016,191,923. 19 周锦涛,焦晓宁,于宾,等. 高等学校化学学报,2017,38(6),1018. 20 Luo X Y, Liao Y H, Xie H L, et al. Ionics,2016,22,1035. 21 Luo X Y, Liao Y H, Xie H L, et al. Electrochimica Acta,2016,220,47. 22 Li Z H, Chen T T, Liao Y H.Ionics,2015,21,2763. 23 Hang T T Le, Duc Tung Ngo, Ramchandra S Kalubarme, et al.ACS Applied Materials & Interfaces,2016,8,20710. 24 Wu D Z, He J L, Zhang M Z, et al. Journal of Power Sources,2015,290,53. 25 Zhao M K, Zuo X X, Wang C Y, et al. Ionics,2016,22,2123. 26 Huang W Y, Liao Y H, Li G J, et al. Electrochimica Acta,2017,251,145. |
|
|
|