聚丙烯酸铵和柠檬酸铵分散剂对钇铝石榴石陶瓷透光率的影响

doi:10.11896/j.issn.1005-023X.2018.08.001

Abstract
Figure/Table
References
Related Citation (3)

Download:

Full Text ( PDF ) (1769KB)
Export: BibTeX | EndNote (RIS)

Abstract Yttrium aluminum garnet (Y₃Al₅O₁₂, YAG) transparent ceramics were prepared by vacuum sintering with the addition of sintering aids and dispersants into YAG precursor. The precursor of YAG was prepared via ultrasound-microwave-assisted alkoxide hydrolysis precipitation method. The crystal structures, morphology and optical properties of transparent YAG ceramics with the addition of different dispersant were investigated. The results showed that pure-phase transparent YAG ceramics could be obtained with the addition of all kinds of dispersants. By adding the ammonium polyacrylic acid (NH₄PAA), no obvious boundaries were formed between crystalline grains and large pores emerged. With the addition of ammonium citrate (AC), well-dispersed crystalline grains could be formed with the average size of about 3 μm. The transmittance in the near-infrared waveband of the transparent YAG ceramic was 76% without the addition of dispersants. However, with the addition of NH₄PAA, the transmittance of the transparent YAG ceramics was reduced to only 51%, and when adding AC it rose back to 78%. The result indicates that AC can refine the grain size of the transparent YAG ceramics and promote the removal of residual pores, thus contribute to the formation of transpa-rent YAG ceramics with higher transmittance.

Key words： dispersants yttrium aluminum garnet alkoxide hydrolysis precipitation method transmittance

Published: 11 May 2018

CLC number:

TG174.75

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SI Wei
	DING Chao
	PAN Wei

Cite this article:

SI Wei,DING Chao,PAN Wei. Influence of Ammonium Polyacrylic Acid and Ammonium Citrate Dispersants on Transmittance of Yttrium Aluminum Garnet Ceramics[J]. Materials Reports, 2018, 32(8): 1209-1212.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.08.001 OR http://www.mater-rep.com/EN/Y2018/V32/I8/1209

1 Tobi E O, Chaim R. Effect of green density and electric field direction on densification of YAG nano-powders by spark plasma sintering[J].Journal of Materials Science,2009,44:2063.
2 Sharma P K, Dutta R K, Pandey A C. Performance of YAG∶Eu³⁺, YAG∶Tb³⁺ and BAM∶Eu²⁺plasma display nanophosphors[J].Journal of Nanoparticle Research,2012,14:731.
3 Lu Z W, Lu T C, Wei N, et al. Novel phenomenon on valence unvariation of doping ion in Yb∶YAG transparent ceramics using MgO additives[J].Journal of Wuhan University of Technology-Materials Science Edition,2013,28(2):320.
4 Zhang L, Lu Z, Zhu J Z, et al. Citrate sol-gel combustion preparation and photoluminescence properties of YAG∶Ce phosphors[J].Journal of Rare Earths,2012,30(4):289.
5 Caponetti E, Saladino M L, Serra F, et al. Co-precipitation synthesis of Nd∶YAG nano-powders: The effect of Nd dopant addition with thermal treatment[J].Journal of Materials Science,2007,42:4418.
6 Potdevin A, Lechevallier S, Chadeyron G, et al. Waveguiding ter-bium-doped yttrium aluminum garnet coatings based on the sol-gel process[J].Thin Solid Films,2009,517:4610.
7 Guo K, Huang M L, Chen H H, Yang X X, et al. Comparative study on photoluminescence of amorphous and nano-crystalline YAG∶Tb phosphors prepared by a combustion method[J].Journal of Non-Crystalline Solids,2012,358(1):88.
8 Jiao H, Ma Q, He L L, et al. Low temperature synthesis of YAG∶Ce phosphors by LiF assisted sol-gel combustion method[J].Powder Technology,2010,198(2):229.
9 You Y L , Qi L H, Li X L, et al. Preparation of YAG nano-powders via an ultrasonic spray co-precipitation method[J].Ceramics International,2013,39(4):3987.
10 Malekfar R, Arabgari S. Temperature effects on the structure and morphology of Nd∶YAG nanocrystallites[J].Current Applied Phy-sics,2011,11(4):1077.
11 Bagayev S N, Kaminskii A A, Kopylov Yu L, et al. Problems of YAG nanopowders compaction for laser ceramics[J].Optical Mate-rials,2011,33(5):702.
12 Liu J, Cheng X N, Li J, et al. Influence of non-stoichiometry on so-lid-state reactive sintering of YAG transparent ceramics[J].Journal of the European Ceramic Society,2015,35(11):3127.
13 Li Y K, Zhou S M, Lin H, et al. Fabrication of Nd∶YAG transpa-rent ceramics with TEOS, MgO and compound additives as sintering aids[J].Journal of Alloys and Compounds,2010,502(1):225.
14 Yang H, Qin X P, Zhang J, et al. Fabrication of Nd∶YAG transpa-rent ceramics with both TEOS and MgO additives[J].Journal of Alloys and Compounds,2011,509(17):5274.
15 Zhang X R, Wang X C, Fu P, et al. Microwave dielectric properties of YAG ceramics prepared by sintering pyrolysised nano-sized powders[J].Ceramics International,2015,41(6):7783.
16 L Y, Zhang W, Tan J, et al. Dispersion of concentrated aqueous neodymia-yttria-alumina mixture with ammonium poly(acrylic acid) as dispersant[J].Journal of Alloys and Compounds,2011,509(6):3122.
17 Kwadwo A A, Gary L M, John Q D. Aqueous slip casting of transparent yttrium aluminum garnet (YAG) ceramics[J].Ceramics International,2008,34:1309.18 Si W, Ding C, Ding S Q. Synthesis and characterization of YAG na-noparticles by ultrasound-assisted and ultrasound-microwave-assisted alkoxide hydrolysis precipitation methods[J].Journal of Nanomate-rials,2014,2014:1.
19 Zhang L, Pan W, Feng J. Dependence of spectroscopic and thermal properties on concentration and temperature for Yb∶Y₂O₃ transpa-rent ceramics[J].Journal of the European Ceramic Society,2015,35:2547.
20 Lee S H, Kupp E R, Stevenson A J, et al. Hot isostatic pressing of transparent Nd∶YAG ceramics[J].Journal of the American Ceramic Society,2009,92(7):1456.
21 Zhou Jun, Pan Yubai, Li Jiang, et al. Fabrication of YAG transpa-rent ceramics using slip casting with ethanol[J].Journal of Inorganic Materials,2011,26(3):254(in Chinese).
周军,潘裕柏,李江,等.无水乙醇注浆成型制备YAG透明陶瓷[J].无机材料学报,2011,26(3):254.