镍基单晶高温合金小角度晶界的形成机制、影响因素与控制措施

doi:10.11896/j.issn.1005-023X.2018.19.014

Abstract
Figure/Table
References
Related Citation (3)

Download:

Full Text ( PDF ) (3562KB)
Export: BibTeX | EndNote (RIS)

Abstract Ni-based single crystal superalloys are widely used to prepare the key hot end components of advanced aero-engines and industrial gas turbines. With the more complicated structure and larger size of the castings, and the increase of refractory elements, the tendency of solidification defects will increase. The low angle boundaries (LABs) are common defects in the casting process of single crystal superalloys by directional solidification. They can destroy the integrity of the single crystal and decrease the mechanical properties of castings once the deviation angle exceeds the tolerance. With the improvement of the service temperature of the single crystal superalloy, the damage of the LABs to the mechanical properties will be more serious. Therefore, the LABs have become an important issue to be solved in the development and application of Ni-based single crystal superalloys, and have been widely concerned by researchers at home and abroad.
The LABs in the single crystal are orientation deviations between the adjacent dendrites, different from that of the traditional. The effect of the LABs on rupture lives, creep properties and fatigue properties under different grain boundary misorientations and temperatures have been studied. The results showed that, the effects of LABs on the mechanical properties were not obvious when misorientations were small. However, with the increase of misorientations and the temperature, all the properties deteriorated rapidly. In order to explore the effective prevention and control measures, the formation mechanism and the influencing factors of LABs have been studied. The widely accepted formation mechanism is as follows: the plastic deformations of dendrites occur during the branching growth, resulting in their orientation deviations, when the dendrites converge again, the LABs form. However, there is no consensus on the causes of dendrite deformation. In addition, the research on the influence factors of LABs is not very systematic. It mainly focused on alloy composition and grain boundary strengthening elements, solidification parameters and orientations, and cas-tings size.
The LABs in Ni-based single crystal superalloys are caused by the orientation deviation of dendrites, whereas their influencing factors are complex, thus the LABs are almost inevitable. At present, it is mainly through the orientation control to decrease the formation of LABs, and by the grain boundary strengthening to increase the tolerance of the alloys to the LABs.
In this paper, the concept of LABs in single crystal superalloys are clarified, the effects of LABs on the mechanical properties are summarized, the formation mechanisms of LABs are reviewed and the influences of different factors are analyzed, such as alloy element, microelement, solidification conditions and casting structure, etc. On this basis, some possible measures to reduce the LABs and the way to strengthen the grain boundaries are proposed, and the future research aspects are stated.

Key words： Ni-based single crystal superalloy low angle boundaries (LABs) direction solidification

Published: 18 October 2018

CLC number:

TG132.3

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	HUO Miao
	LIU Lin
	HUANG Taiwen
	YANG Wenchao
	LI Yafeng
	WANG Xiaojuan
	ZHANG Jun
	FU Hengzhi

Cite this article:

HUO Miao,LIU Lin,HUANG Taiwen, et al. Formation Mechanism, Influencing Factors and Control Measures of Low Angle Boundaries in Ni-based Single Crystal Superalloys[J]. Materials Reports, 2018, 32(19): 3394-3404.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.19.014 OR http://www.mater-rep.com/EN/Y2018/V32/I19/3394

1 Reed R C. The superalloys: Fundamentals and applications[M].Cambridge: Cambridge University Press,2006.
2 Pollock T M, Tin S. Nickel-based superalloys for advanced turbine engines: Chemistry, microstructure and properties[J].Journal of Propulsion & Power,2006,22(2):361.
3 Rahimian M, Milenkovic S, Sabirov I. Microstructure and hardness evolution in MAR-M247 Ni-based superalloy processed by controlled cooling and double heat treatment[J].Journal of Alloys & Compounds,2013,550(2):339.
4 Graverend J B L, et al. Creep of a nickel-based single-crystal superalloy during very high-temperature jumps followed by synchrotron X-ray diffraction[J].Acta Materialia,2015,84:65.
5 Yeh A C, Tin S. Effects of Ru and Re additions on the high temperature flow stresses of Ni-base single crystal superalloys[J].Scripta Materialia,2005,52(6):519.
6 Tin S, Pollock T M, Murphy W. Stabilization of thermosolutal convective instabilities in Ni-based single-crystal superalloys: Carbon additions and freckle formation[J].Metallurgical & Materials Tran-sactions A,2001,32(7):1743.
7 Li Q, Shen J, Qin L, et al. Investigation on freckles in directionally solidified CMSX-4 superalloy specimens with abrupt cross section variation[J].Journal of Alloys & Compounds,2017,691:997.
8 Ter Vehn M M, et al. Undercooling related casting defects in single crystal turbine blades[C]∥Superalloys 1996. Los Angeles,1996:471.
9 Yang X L, Dong H B, Wang W, et al. Microscale simulation of stray grain formation in investment cast turbine blades[J].Materials Science & Engineering A,2004,386(1):129.
10 Aveson J W, et al. On the origin of sliver defects in single crystal investment castings[J].Acta Materialia,2013,61:5162.
11 Newell M, D’Souza N, Green N R. Formation of low angle boundaries in Ni-based superalloys[J].Materials Science & Engineering A,2005,413(1-4):567.
12 Bogdanowicz W, Albrecht R, Sieniawski J, et al. The subgrain structure in turbine blade roots of CMSX-4 superalloy[J].Journal of Crystal Growth,2014,401(9):418.
13 邓安华.金属材料简明辞典[M].北京:冶金工业出版社,1992:345.
14 Pollock T M, Murphy W H, Goldman E H, et al. Grain defect formation during directional solidification of nickel base single crystals[C]∥Superalloys 1992.Pennsylvania,1992:125.
15 Shi Z X, Li J R, Liu S Z, et al. Formation mechanism of low angle boundary of DD6 single crystal superalloy blades[J].Advanced Materials Research,2012,535-537:1019.
16 Shah D M, Cetel A. Evaluation of PWA1483 for large single crystal IGT blade applications[C]∥Superalloys 2000.Boston,2000:29.
17 Shi Zhenxue, Li Jiarong, Liu Shizhong, et al. Microstructures of low angle boundaries of DD6 single crystal superalloy blades[J].Rare Metal Materials and Engineering,2011,40(12):2117(in Chinese).
史振学,李嘉荣,刘世忠,等.DD6单晶高温合金叶片小角度晶界组织[J].稀有金属材料与工程,2011,40(12):2117.
18 Ross E W, O’Hara K S. Rene N4: A first generation single crystal turbine airfoil alloy with improved oxidation resistance, low angle boundary strength and superior long time rupture strength[J].Superalloys 1996,1996:19.
19 Cao Liang, Zhou Yizhou, Jin Tao, et al. Effect of grain boundary angle on stress rupture properties of a Ni-based bicrystal superalloy[J].Acta Metallurgica Sinica,2014,50(1):11(in Chinese).
曹亮,周亦胄,金涛,等.晶界角度对一种镍基双晶高温合金持久性能的影响[J].金属学报,2014,50(1):11.
20 Shi Z, Li J, Liu S, et al. Effect of LAB on the stress rupture properties and fracture characteristic of DD6 single crystal superalloy[J].Rare Metal Materials and Engineering,2012,41(6):962.
21 Patel Y, Browning P F, Fitzpatrick M D, et al. The effect of primary axis and low angle boundary misorientation on CMSX-10K mechanical properties[C]∥ASME Turbo Expo 2000: Power for Land, Sea and Air.Munich,2000.
22 Shi Zhenxue, Li Jiarong, Liu Shizhong, et al. Tensile properties of twist low angle boundary of DD6 single crystal superalloy[J].Journal of Aeronautical Materials,2009,29(3):88(in Chinese).
史振学,李嘉荣,刘世忠,等.DD6单晶高温合金扭转小角度晶界的拉伸性能[J].航空材料学报,2009,29(3):88.
23 Li J R, Zhao J Q, Liu S Z, et al. Effects of low angle boundaries on the mechanical properties of single crystal superalloy DD6[C]∥Superalloys 2008.Pennsylvania,2008:443.
24 Tamaki H, Yoshinari A, Okayama A, et al. Development of a low angle grain boundary resistant single crystal superalloy YH61[C]∥Superalloys 2000.Boston,2000:757.
25 Shi Zhenxue, et al. Effect of low angle boundary on high cycle fatigue properties of single crystal superalloy[J].Transactions of Materials and Heat Treatment,2015,36(s1):52(in Chinese).
史振学,等.小角度晶界对单晶高温合金高周疲劳性能的影响[J].材料热处理学报,2015,36(s1):52.
26 Napolitano R E, Schaefer R J. The convergence-fault mechanism for low-angle boundary formation in single-crystal castings[J].Journal of Materials Science,2000,35(7):1641.
27 Newell M, et al. Role of dendrite branching and growth kinetics in the formation of low angle boundaries in Ni-base superalloys[J].Materials Science & Engineering A,2005,412:307.
28 Newell M, D’Souza N, Green N R. Formation of low angle boundaries in Ni-based superalloys[J].International Journal of Cast Metals Research,2009,22(1-4):66.
29 Siredey N, et al. Dendritic growth and crystalline quality of nickel-base single grains[J].Journal of Crystal Growth,1993,130:132.
30 Dragnevski K, Mullis A M, Walker D J, et al. Mechanical deformation of dendrites by fluid flow during the solidification of undercooled melts[J].Acta Materialia,2002,50(14):3743.
31 Dahle A K, John D H S, Thevik H J, et al. Modeling the fluid-flow-induced stress and collapse in a dendritic network[J].Metallurgical and Materials Transactions B,1999,30(2):287.
32 Zhang X, Zhou Y, Han Y, et al. Dendritic growth pattern and dendritic network distortion in the platform of a Ni-based superalloy[J].Journal of Materials Science & Technology,2014,30(3):223.
33 Zhang Xiaoli. Fundamental research on production of single crystal superalloys by directional solidification[D].Graduate University of Chinese Academy of Sciences,2013(in Chinese).
张小丽.单晶高温合金定向凝固制备的基础研究[D].中国科学院大学,2013.
34 Zhang Jun, et al. Advances in solidification characteristics and typical casting defects in nickel-based single crystal superalloys[J].Acta metallurgica sinica,2015(10):1163(in Chinese).
张军,等.单晶高温合金凝固特性与典型凝固缺陷研究[J].金属学报,2015(10):1163.
35 Al-Jarba K A, Fuchs G E. Carbon-containing single-crystal nickel-based superalloys: Segregation behavior and carbide formation[J].JOM,2004,56(9):50.
36 Li Y F, Liu L, et al. The formation mechanism, influencing factor and processing control of stray grains in Nickle-based single crustal superalloys[C]∥Superalloys 2016. Pennsylvania,2016:293.
37 Chen Xianzhou. Low angle boundaries in homebred third generation Ni-based single crystal superalloy[D].Xi’an: Northwestern Polytechnical University,2014(in Chinese).
陈先洲.国产第三代镍基单晶高温合金中小角度晶界的研究[D].西安:西北工业大学,2014.
38 Jiao Juanjuan. The effects of dendritic orientation and alloy composition on solidification defects of single crystal superalloys[D].Xi’an: Northwestern Polytechnical University,2015(in Chinese).
焦娟娟.单晶高温合金晶体取向及合金成分对凝固缺陷影响研究[D].西安:西北工业大学,2015.
39 Guo Hailong. Effect of hafnium and boron on low angle boundary of nickel-based single crystal superalloys[D].Xi’an: Northwestern Polytechnical University,2016(in Chinese).
郭海龙.铪和硼对镍基单晶高温合金中小角度晶界的影响[D].西安:西北工业大学,2016.
40 Mihalisin J R, Corrigan J, Launsbach M, et al. Some effects of carbon in the production of single crystal superalloy castings[C]∥Superalloys 2004. Pennsylvania,2004:795.
41 Yan B C, Zhang J, Lou L H. Effect of boron additions on the microstructure and transverse properties of a directionally solidified superalloy[J].Materials Science & Engineering A,2008,474(1-2): 39.
42 Kotval P S, Venables J D, Calder R W. The role of hafnium in modifying the microstructure of cast nickel-base superalloys[J].Metallurgical Transactions,1972,3(2):457.
43 Shah D M, Cetel A. Evaluation of PWA1483 for large single crystal IGT blade applications[C]∥Superalloys 2000.Boston,2000:2954.
44 Chen Q Z, Jones C N, Knowles D M. The grain boundary microstructures of the base and modified RR 2072 bicrystal superalloys and their effects on the creep properties[J].Materials Science & Engineering A,2004,385(1):402.
45 Durandcharre M. The microstructure of superalloys[M].CRC Press,Washington,1997.
46 D’Souza N, et al. Directional and single-crystal solidification of Ni-base superalloys: Part Ⅰ. The role of curved isotherms on grain selection[J].Metallurgical and Materials Transactions A,2000,31:2877.
47 Elliott A J, et al. Directional solidification of large superalloy cas-tings with radiation and liquid-metal cooling: A comparative assessment[J].Metallurgical & Materials Transactions A,2004,35:3221.
48 Chen Xianzhou, et al. Effect of solidification rate and rhenium on low angle boundaries of nickel base single crystal superalloy blades[J].Hot Working Technology,2014(11):1(in Chinese).
陈先州,等.凝固速率及铼对镍基单晶高温合金叶片小角度晶界的影响[J].热加工工艺,2014(11):1.
49 D’Souza N, Jennings P A, Yang X L, et al. Seeding of single-crystal superalloys-role of constitutional undercooling and primary dendrite orientation on stray-grain nucleation and growth[J].Metallurgical & Materials Transactions B,2005,36(5):657.
50 Clements M L,Price A R, Bellows R S. Advanced solidification processing of an industrial gas turbine engine component[J].Journal of the Minerals, Metals and Materials Society,2003,55(3):27.
51 Kurz W, Fisher D J. Fundamentals of solidification[M].Switzerland: Trans Tech Publications LTD,1998.
52 Li Y, Liu L, Huang T, et al. The process analysis of seeding-grain selection and its effect on stray grain and orientation control[J].Journal of Alloys & Compounds,2016,657:341.
53 冯小辉,李应举,杨院生.外加电场对单晶高温合金生长取向偏离的影响[C]∥中国高温合金年会.北京,2015.
54 傅恒志,郭景杰,刘林,等.先进材料定向凝固[M].北京:科学出版社,2008.