Abstract The present work provides a comparative investigation on the creep rupture behavior of Super304H steel under simulated coal ash/gas environment and in static air condition, respectively, by using a synergistic corrosion-static loading apparatus. The results indicated that the corrosion medium shortened the rupture life of Super304H steel under varying stresses, and this shor-tening effect become more remarkable with the extension of exposure time. Based on the double logarithm method, the Super304H steel subjected to coal ash/gas corrosion was determined to be 80 MPa, with a decrement of about 43% compared to the specimen in static air condition (140 MPa). We observed a smooth oxide film formed on the steel surface in static air, and on the contrary, the loose and porous corrosion product and a large number of “tumor like” bulge product for the specimen surface under the simulated corrosion environment. XRD and EDS measurements showed that the corrosion products are rich in Fe, Cr, Ni, sulfides and complex sulfates. The decay of the high temperature durability of Super304H under loading can be ascribed to the corrosion-medium-induced increase of nucleation rate at the corrosion layer/metal interface.

Key words： Super304H coal ash/gas high temperature corrosion creep rupture internal sulfidation

Published: 18 September 2018

CLC number:

TG178

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LIU Wu
	LU Jintao
	HUANG Jinyang
	DANG Yingying
	ZHAO Xinbao
	ZHAO Maiqun
	YUAN Yong

Cite this article:

LIU Wu,LU Jintao,HUANG Jinyang, et al. The High Temperature Stress Rupture Behavior of Super304H Steel Subjected to Simulated Coal Ash/Gas Corrosion[J]. Materials Reports, 2018, 32(16): 2787-2792.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.16.016 OR http://www.mater-rep.com/EN/Y2018/V32/I16/2787

1 Zhao Qingquan.The research of domestic super304H steel pipes on mechanical properties, microstructure and creep rupture strength[D]. Lanzhou: Lanzhou University of Technology,2008(in Chinese).
赵庆权.国产化Super304H钢管组织性能及持久强度研究[D].兰州:兰州理工大学,2008.
2 Yang Yan, Cheng Shichang, Yang Gang. Present situation of exploiting and research of Super304H steel for boiler [J]. Special Steel,2002,23(1):27(in Chinese).
杨岩,程世长,杨钢.Super304H锅炉钢的开发和研究现状[J].特殊钢,2002,23(1):27.
3 Iseda A, Okada H, Semba H, et al. Long term creep properties and microstructure of SUPER304H, TP347HFG and HR3C for A-USC boilers[J]. Energy Materials Materials Science & Engineering for Energy Systems,2007,2(4):99.
4 Li X M, Zhang Z, Zou Z. Microstructure evolution of a novel Super304H steel aged at high temperatures[J]. Materials Transactions,2010,51(2):305.
5 Li Y, Lu J T, Yang Z, et al. Effect of sulfur content on corrosion behavior of candidate steels used for 700℃ Level A-USC boiler in simulated coal ash and flue gas environments[J]. Journal of Chinese Society for Corrosion and Protection,2016,36(5):505(in Chinese).
李琰,鲁金涛,杨珍,等.烟气S含量对700 ℃超超临界锅炉候选合金腐蚀行为影响[J].中国腐蚀与防护学报,2016,36(5):505.
6 Gao Y, Zhang C, Xiong X, et al. Intergranular corrosion susceptibility of a novel Super304H stainless steel[J]. Engineering Failure Analysis,2012,24(9):26.
7 Le Ming, Wang Hongzhe, Yu Zaisong, et al. Influence of surface modification on steam oxidation of Super304H at 650℃[J]. Thermal Power Generation,2016,45(11):42(in Chinese).
乐明,王弘喆,于在松,等.表面改性对Super304H钢在650℃饱和蒸汽中氧化行为的影响[J].热力发电,2016,45(11):42.
8 Huang Jinyang, Lu Jintao, Yang Zhen, et al. Corrosion behavior of Ni-Cr based coating prepared by plasma cladding in simulated coal combustion environment[J]. Thermal Power Generation,2017(4):70(in Chinese).
黄锦阳,鲁金涛,杨珍,等.等离子熔覆Ni-Cr涂层在模拟锅炉燃烧环境中的腐蚀行为[J].热力发电,2017(4):70.
9 Wright I G, Dooley R B. A review of the oxidation behaviour of structural steels in steam [J]. International Materials Reviews,2010,55(3):129.
10 Grabke H J. Metal dusting [J]. Materials and Corrosion,2003,54:736.
11 Zhao Q X. High temperature corrosion of water wall materials T23 and T24 in simulated furnace atmospheres [J].Chinese Journal Chemical Engineering,2012,20(4):814.
12 Li Min, Qiu Jihua, Xiang Jun, et al. An anti-corrosion simulation for the high temperature corrosion on boiler water-wall during diffe-rent operation[J]. Proceedings-Chinese Society of Electrical Engineering,2002,22(7):150(in Chinese).
李敏,丘纪华,向军,等.锅炉水冷壁高温腐蚀运行工况的防腐模拟[J].中国电机工程学报,2002,22(7):150.
13 He X Q, Wang J D, Zhu J H, et al. Fatigue life prediction and verification for HIC hermetical sealing under random vibration loading[J]. Applied Mechanics & Materials,2014,668:176.
14 Calvarin-Amiri G, Molins R, Huntz A M. Effect of the application of a mechanical load on the oxide-layer microstructure and on the oxidation mechanism of Ni-20Cr Foils[J]. Oxidation of Metals,2000,53(3):399.
15 Stroosnijder M F, Guttmann V, De Wit J H W. Corrosion and creep behaviour of steel 800H in sulphidizing/oxidizing/carburizing environments at 700 ℃-Part I: Corrosion behaviour in the stress free and the stressed state[J]. Materials & Corrosion,2015,41(9):503.
16 Homaeian A, Alizadeh M. Interaction of hot corrosion and creep in Steel 617[J]. Engineering Failure Analysis,2016,66:373.
17 Xiong W Z, He J J, Chen J, et al. Compressive creep behavior of 12Cr1MoV steel under hot corrosion environment[J]. Ordnance Material Science & Engineering,2016,39(4):16.
熊维舟,何建军,陈荐,等.12Cr1MoV合金在热腐蚀环境下的压缩蠕变行为研究[J].兵器材料科学与工程,2016,39(4):16.
18 Swaminathan J, Raghavan S. Vanadic hot corrosion-creep Inte-raction of Superni-C 276 in the temperature range 650—750 ℃[J]. High Temperature Materials & Processes,1994,13(4):277.
19 李美栓.金属的高温腐蚀[M].北京:冶金工业出版社,2001.
20 Hammer J E, Laney S J, Jackson R W, et al. The oxidation of ferritic stainless steels in simulated solid-oxide fuel-cell atmospheres[J]. Oxidation of Metals,2007,67(1-2):1.
21 李铁藩.金属的高温氧化和热腐蚀[M].北京:化学工业出版社,2003.
22 Ma Y H, Zheng K Y, Lin F S, et al. Effect of surface treatment on steam oxidation resistance of steel Super304H[J]. Journal of Chinese So-ciety of Power Engineering,2013,33(7):572(in Chinese).
马云海,郑开云,林富生,等.表面加工状态对Super304H钢抗蒸汽氧化性能的影响[J].动力工程学报,2013,33(7):572.
23 Ennis P J, Czyrska-Filemonowicz A. Recent advances in creep-resistant steels for power plant applications[J]. Sadhana,2003,28(3-4):709.
24 Lu J T, Gu Y F, Yang Z. Coal ash induced corrosion of three candidate materials for superheater boiler tubes of advanced ultrasupercritical power station[J]. Corrosion Science & Protection Technology,2014,26(3):205(in Chinese).
鲁金涛,谷月峰,杨珍.3种700 ℃级超超临界燃煤锅炉备选高温合金煤灰腐蚀行为[J].腐蚀科学与防护技术,2014,26(3):205.
25 张俊善.材料的高温变形与断裂[M].北京:科学出版社,2010.
26 Kassner M E. Fundamentals of creep in metals and steels (second edition)[M]. Netherlands: Elsevier Science,2004:243.
27 Crossman F W, Ashby M F. The non-uniform flow of polycrystals by grain-boundary sliding accommodated by power-law creep[J]. Acta Metallurgica,1975,23(4):425.